Ti6Al4V cellular structures were produced by selective laser melting(SLM)and then filled either with beta-tricalcium phosphate(β-TCP)or PEEK(poly-ether-ether-ketone)through powder metallurgy techniques,to improve ost...Ti6Al4V cellular structures were produced by selective laser melting(SLM)and then filled either with beta-tricalcium phosphate(β-TCP)or PEEK(poly-ether-ether-ketone)through powder metallurgy techniques,to improve osteoconductivity and wear resistance.The corrosion behavior of these structures was explored considering its importance for the long-term performance of implants.Results revealed that the incorporation of open cellular pores induced higher electrochemical kinetics when being compared with dense structures.The impregnation ofβ-TCP and PEEK led to the creation of voids or gaps between the metallic matrix and the impregnated material which also influenced the corrosion behavior of the cellular structures.展开更多
基金supported by FCT through the grants PD/BD/140202/2018,SFRH/BD/140191/2018 and SFRH/BD/128657/2017the projects PTDC/EMS-TEC/5422/2014 and NORTE-01-0145-FEDER-000018-HAMa BICo+1 种基金supported by FCT with the reference project UID/EEA/04436/2019the financial support through the M-ERA-NET/0001/2015 project(FCT)
文摘Ti6Al4V cellular structures were produced by selective laser melting(SLM)and then filled either with beta-tricalcium phosphate(β-TCP)or PEEK(poly-ether-ether-ketone)through powder metallurgy techniques,to improve osteoconductivity and wear resistance.The corrosion behavior of these structures was explored considering its importance for the long-term performance of implants.Results revealed that the incorporation of open cellular pores induced higher electrochemical kinetics when being compared with dense structures.The impregnation ofβ-TCP and PEEK led to the creation of voids or gaps between the metallic matrix and the impregnated material which also influenced the corrosion behavior of the cellular structures.