A good joint of Ti Bw/Ti6Al4V composites and Inconel 718 alloys was obtained by Gas Tungsten Arc Welding(GTAW) heat transmission. The interfacial reaction mechanism of joint was investigated and analyzed in details. O...A good joint of Ti Bw/Ti6Al4V composites and Inconel 718 alloys was obtained by Gas Tungsten Arc Welding(GTAW) heat transmission. The interfacial reaction mechanism of joint was investigated and analyzed in details. Owing to the heat input applied on the surface of Ti Bw/Ti6Al4V composites, a solid-state reaction layer appeared at the interface of Ti Bw/Ti6Al4 V composites to Inconel 718 alloys. The thickness of the reaction layer was obviously increased with increasing heat input.Developing of reaction layer mainly depended on the diffusion of elements of Ti and Ni through the interface during welding to form solid solutions and intermetallic compounds(IMCs). The reaction layer can be divided into Ti-rich zone(layer 2) and Nirich zone(layer 1). In Ni-rich zone, relatively coarse dendrites were the predominant, however, more brittle IMCs like Ti2Ni were found in the Ti-rich zone. Micro hardness of reaction layer was much higher than that of base metal. While a slight decrease of hardness was found between Ti-rich zone and Ni-rich zone due to the formation of TiNi.展开更多
基金China Postdoctoral Science Foundation(2018T110215)National Key R&D Program of China(2018YFB1107801)+1 种基金Science Fund for CreativeResearch Groups of NSFC(51621064)National Natural Science Foundation of China(51805070)。
基金supported by the National Key R&D Program of China(Grant No.2017YFB0703100)the National Natural Science Foundation of China(Grant Nos.51822103,51801206,and 51731009)the Fundamental Research Funds for the Central Universities(Grant No.HIT.BRETIV.201902)
文摘A good joint of Ti Bw/Ti6Al4V composites and Inconel 718 alloys was obtained by Gas Tungsten Arc Welding(GTAW) heat transmission. The interfacial reaction mechanism of joint was investigated and analyzed in details. Owing to the heat input applied on the surface of Ti Bw/Ti6Al4V composites, a solid-state reaction layer appeared at the interface of Ti Bw/Ti6Al4 V composites to Inconel 718 alloys. The thickness of the reaction layer was obviously increased with increasing heat input.Developing of reaction layer mainly depended on the diffusion of elements of Ti and Ni through the interface during welding to form solid solutions and intermetallic compounds(IMCs). The reaction layer can be divided into Ti-rich zone(layer 2) and Nirich zone(layer 1). In Ni-rich zone, relatively coarse dendrites were the predominant, however, more brittle IMCs like Ti2Ni were found in the Ti-rich zone. Micro hardness of reaction layer was much higher than that of base metal. While a slight decrease of hardness was found between Ti-rich zone and Ni-rich zone due to the formation of TiNi.