A TiA1N coating was deposited on a heat resistant steel X12CrMoWVNbN10-1-1 by vacuum arc ion plating. The tensile and fatigue properties of the coated steel were investigated at room temperature （RT） and 650 ℃. The...A TiA1N coating was deposited on a heat resistant steel X12CrMoWVNbN10-1-1 by vacuum arc ion plating. The tensile and fatigue properties of the coated steel were investigated at room temperature （RT） and 650 ℃. The results reveal that the TiA1N coating is compact, on which a small number of large particle and pits are present. The Ti/Al atomic ratio in the coating is about 0.94. The average hardness of the coating is 1 868 HV0.1 and the interface bonding force between TiAIN coating and the substrate is about 3 l N. The elastic modulus and the strength of the steel are improved by the deposition of TiAIN coating. The influence of the TiA1N coating on the tensile properties of the steel can be ignored at both RT and 650 ℃. Moreover, there is no obvious decrease of the fatigue limit of substrate when the steel is coated by the coating at the investigated temperature.展开更多
基金Funded by National Science Foundation of China(No.51172182)the Program for New Century Excellent Talents in University(No.NCET-08-0460)the 111 Project(No.B08040)
文摘A TiA1N coating was deposited on a heat resistant steel X12CrMoWVNbN10-1-1 by vacuum arc ion plating. The tensile and fatigue properties of the coated steel were investigated at room temperature （RT） and 650 ℃. The results reveal that the TiA1N coating is compact, on which a small number of large particle and pits are present. The Ti/Al atomic ratio in the coating is about 0.94. The average hardness of the coating is 1 868 HV0.1 and the interface bonding force between TiAIN coating and the substrate is about 3 l N. The elastic modulus and the strength of the steel are improved by the deposition of TiAIN coating. The influence of the TiA1N coating on the tensile properties of the steel can be ignored at both RT and 650 ℃. Moreover, there is no obvious decrease of the fatigue limit of substrate when the steel is coated by the coating at the investigated temperature.