In-situ TiB2 particles reinforced 2014 aluminum alloy composite was prepared using an exothermic reaction process with K2TiF6 and KBF4 salts. The effects of CeO2 additive on the microstructure and properties of in-sit...In-situ TiB2 particles reinforced 2014 aluminum alloy composite was prepared using an exothermic reaction process with K2TiF6 and KBF4 salts. The effects of CeO2 additive on the microstructure and properties of in-situ TiB2/2014 composite were investigated. The results showed that CeO2 at high temperature exhibits the same function as Ce. When 0.5% （mass fraction） CeO2 additive was added, the dispersion of TiB2 particles in the matrix is improved significantly, and particles have no obvious settlement. The dispersing mechanism of TiB2 particles in 2014 Al alloy matrix was explained. Compared with the composite without CeO2, the hardness, tensile strength, yield strength and elongation of the composite with CeO2 addition are greatly increased in as-cast condition.展开更多
（TiB2＋Al2O3）/NiAl composites were synthesized by self-propagation high-temperature synthesis, and their phase compositions, microstructures and evolution modes were studied. The microstructures and shapes vary with...（TiB2＋Al2O3）/NiAl composites were synthesized by self-propagation high-temperature synthesis, and their phase compositions, microstructures and evolution modes were studied. The microstructures and shapes vary with the TiB2＋Al2O3 content in the NiAl matrix. TiB2 particles take a great variety of elementary shapes such as white bars, plates, herringbones, regular cubes and cuboids. These results outline a strategy of self-assembly processes in real time to build diversified microstructures. Some TiB2 grains in sizes of 2-5μm are embeded in Al2O3 clusters, while a small number of TiB2 particles disperse in the NiAl matrix. It is believed that the higher the TiB2＋Al2O3 content is, the more the regular shapes and homogeneous distributions of TiB2 and Al2O3 will be present in the NiAl matrix.展开更多
A novel technique for fabricating TiB_2/Al composites in molten aluminum was introduced. The formation mechanism of brittleAl,Ti particulates up to 30 m in size produced in the composites was studied and a method of e...A novel technique for fabricating TiB_2/Al composites in molten aluminum was introduced. The formation mechanism of brittleAl,Ti particulates up to 30 m in size produced in the composites was studied and a method of eliminating them was proposed. The resultsshow that (l) the brittle Al,Ti particulates are always present in the composites when the molar ratio of Ti to B 'T,:nB is l:2; and (2) theformation of the brittle Al,Ti phase can be avoided entirely from the final product by using a proper 'T,:nB of l:4 in the Ti-B-Al preforms.In the former case, the tensile elongation of the composite is only 4%, much lower than the value of pure aluminum (20%). In the latercase, the tensile elongation of this composite is 10%, higher than the value of the composite with a lot ofAl,Ti (4%), whereas the ultimatetensile stfength of the former is nearly that of the later.展开更多
Ceramic tapes, containing Al2O3-25 wt pct TiB2(B) and Al2O3-25 wt pct nano-TiC (c), have been obtained by tape casting process. Numerous tapes (about 60～80 tapes) were prepared by stacking in turn the composition (B)...Ceramic tapes, containing Al2O3-25 wt pct TiB2(B) and Al2O3-25 wt pct nano-TiC (c), have been obtained by tape casting process. Numerous tapes (about 60～80 tapes) were prepared by stacking in turn the composition (B) and (C), laminating under 10 MPa pressure, eliminating the solvent and burning out the polymer additives. The final green bodies were hot pressed at 1750℃ and 30 MPa. The composite has a bending strength of 568 MPa and a fracture toughness of 5.8 M Pa·m1/2. SEM analysis exhibits that Al2O3 particle growth was inhibited by TiC particles in C. but TiB2 particles could not hinder Al2O3 growth in B. The curves of GTA indicates that all organic additives could be removed completely above 600℃展开更多
14% and 20% (volume fraction) TiB2p/6061Al composites were fabricated by pressure infiltration method, and then were extruded. The microstructure and properties of TiB2p/Al composites before and after extrusion were s...14% and 20% (volume fraction) TiB2p/6061Al composites were fabricated by pressure infiltration method, and then were extruded. The microstructure and properties of TiB2p/Al composites before and after extrusion were studied by TEM, SEM and tensile method. The results show that TiB2 particles employed are equiaxed polyhedrals and are well wetted with the aluminum alloy. Hot extruding is effective in eliminating defects such as pores, which are induced in the fabrication process. After T6 treatment and extrusion treatment, elastic modulus, tensile strength and elongation of 14%TiB2p/6061Al composites are 107 GPa, 364.1 MPa and 9.25%, respectively. While those of 20%TiB2p/6061Al composites are 120 GPa, 472.6 MPa and 9.79%, respectively, which show high strength and plasticity. A lot of dimples and a few cracked particles are observed on the fracture surfaces of the composites, which indicates good plasticity of the composites. The high strength and plasticity of TiB2p/6061Al composites are attributed to good bonding between TiB2 particles and aluminum alloy.展开更多
TiB2-Al2O3 composite powders were produced by self-propagating high-temperature synthesis（SHS） method with reductive process from B2O3-TiO2-AI system. X-ray diffraction（XRD） and scanning electron microscopy（SEM...TiB2-Al2O3 composite powders were produced by self-propagating high-temperature synthesis（SHS） method with reductive process from B2O3-TiO2-AI system. X-ray diffraction（XRD） and scanning electron microscopy（SEM） analyses show the presence of TiB2 and Al2O3 only in the composite powders produced by SHS. The powders are uniform and free-agglomerate. Transmission electron microscopy （TEM） and high resolution electron microscopy （HREM） observation of microstructure of the composite powders indicate that the interfaces of the TiB2-Al2O3 bond well, without any interfacial reaction products. It is proposed that the good interfacial bonding of the composite powders can be resulted from the TiB2 particles crystallizing and growing on the Al2O3 particles surface with surface defects acting as nucleation centers.展开更多
Mechanical properties were tested for in situ TiB2/A357 composite fabricated by LSM (mixed salts reaction) method. Micro structures of as cast and plastic deformed TiB2/A357 were investigated. The results show that th...Mechanical properties were tested for in situ TiB2/A357 composite fabricated by LSM (mixed salts reaction) method. Micro structures of as cast and plastic deformed TiB2/A357 were investigated. The results show that there is a low misfit between (200) Al and (101)TiB2 with [011]//Al [101]TiB2. There is a change from fully dendritic structure of the α-Al of A357 to a rosette-type structure of TiB2/A357. Significant increases in proof stress and Young's modulus can be obtained at low TiB2 additions. There exist dislocation loops around neighboring TiB2 particles with about 0.1μm in diameter and dislocation multiplication near TiB2 particles.展开更多
The thermodynamic analysis of the formation of in-situ reinforced phases in （TiB2＋Al3Ti）/Al-4.5Cu composites prepared by mixed salts reaction was conducted, and heat changes of mixed salts system were analyzed by d...The thermodynamic analysis of the formation of in-situ reinforced phases in （TiB2＋Al3Ti）/Al-4.5Cu composites prepared by mixed salts reaction was conducted, and heat changes of mixed salts system were analyzed by differential thermal analysis（DTA）.The results show that although TiB2 possesses the strongest formation ability in Al-Ti-B ternary system, [Ti] is relatively excessive in the in-situ reaction and it combines with Al to form AlaTi phase. The reinforced phases are TiB2 and AlaTi in the produced composites due to the reaction taking place to form reinforced phase with the addition of mixed salts into Al-4.5Cu melt between 900 ℃ and 1 032 ℃.展开更多
基金Project (2008AA03A239) supported by the High-tech Research and Development Program of China
文摘In-situ TiB2 particles reinforced 2014 aluminum alloy composite was prepared using an exothermic reaction process with K2TiF6 and KBF4 salts. The effects of CeO2 additive on the microstructure and properties of in-situ TiB2/2014 composite were investigated. The results showed that CeO2 at high temperature exhibits the same function as Ce. When 0.5% （mass fraction） CeO2 additive was added, the dispersion of TiB2 particles in the matrix is improved significantly, and particles have no obvious settlement. The dispersing mechanism of TiB2 particles in 2014 Al alloy matrix was explained. Compared with the composite without CeO2, the hardness, tensile strength, yield strength and elongation of the composite with CeO2 addition are greatly increased in as-cast condition.
基金Project(51272141)supported by the National Natural Science Foundation of ChinaProject(ts20110828)supported by the Taishan Scholars Project of Shandong Province,ChinaProject(2015AA034404)supported by the Ministry of Science and Technology of China
文摘（TiB2＋Al2O3）/NiAl composites were synthesized by self-propagation high-temperature synthesis, and their phase compositions, microstructures and evolution modes were studied. The microstructures and shapes vary with the TiB2＋Al2O3 content in the NiAl matrix. TiB2 particles take a great variety of elementary shapes such as white bars, plates, herringbones, regular cubes and cuboids. These results outline a strategy of self-assembly processes in real time to build diversified microstructures. Some TiB2 grains in sizes of 2-5μm are embeded in Al2O3 clusters, while a small number of TiB2 particles disperse in the NiAl matrix. It is believed that the higher the TiB2＋Al2O3 content is, the more the regular shapes and homogeneous distributions of TiB2 and Al2O3 will be present in the NiAl matrix.
文摘A novel technique for fabricating TiB_2/Al composites in molten aluminum was introduced. The formation mechanism of brittleAl,Ti particulates up to 30 m in size produced in the composites was studied and a method of eliminating them was proposed. The resultsshow that (l) the brittle Al,Ti particulates are always present in the composites when the molar ratio of Ti to B 'T,:nB is l:2; and (2) theformation of the brittle Al,Ti phase can be avoided entirely from the final product by using a proper 'T,:nB of l:4 in the Ti-B-Al preforms.In the former case, the tensile elongation of the composite is only 4%, much lower than the value of pure aluminum (20%). In the latercase, the tensile elongation of this composite is 10%, higher than the value of the composite with a lot ofAl,Ti (4%), whereas the ultimatetensile stfength of the former is nearly that of the later.
文摘Ceramic tapes, containing Al2O3-25 wt pct TiB2(B) and Al2O3-25 wt pct nano-TiC (c), have been obtained by tape casting process. Numerous tapes (about 60～80 tapes) were prepared by stacking in turn the composition (B) and (C), laminating under 10 MPa pressure, eliminating the solvent and burning out the polymer additives. The final green bodies were hot pressed at 1750℃ and 30 MPa. The composite has a bending strength of 568 MPa and a fracture toughness of 5.8 M Pa·m1/2. SEM analysis exhibits that Al2O3 particle growth was inhibited by TiC particles in C. but TiB2 particles could not hinder Al2O3 growth in B. The curves of GTA indicates that all organic additives could be removed completely above 600℃
基金Project(NCET-07-0234) supported by Program for New Century Excellent Talents in UniversityProject(20060400813) supported by China Postdoctoral Science Foundation
文摘14% and 20% (volume fraction) TiB2p/6061Al composites were fabricated by pressure infiltration method, and then were extruded. The microstructure and properties of TiB2p/Al composites before and after extrusion were studied by TEM, SEM and tensile method. The results show that TiB2 particles employed are equiaxed polyhedrals and are well wetted with the aluminum alloy. Hot extruding is effective in eliminating defects such as pores, which are induced in the fabrication process. After T6 treatment and extrusion treatment, elastic modulus, tensile strength and elongation of 14%TiB2p/6061Al composites are 107 GPa, 364.1 MPa and 9.25%, respectively. While those of 20%TiB2p/6061Al composites are 120 GPa, 472.6 MPa and 9.79%, respectively, which show high strength and plasticity. A lot of dimples and a few cracked particles are observed on the fracture surfaces of the composites, which indicates good plasticity of the composites. The high strength and plasticity of TiB2p/6061Al composites are attributed to good bonding between TiB2 particles and aluminum alloy.
文摘TiB2-Al2O3 composite powders were produced by self-propagating high-temperature synthesis（SHS） method with reductive process from B2O3-TiO2-AI system. X-ray diffraction（XRD） and scanning electron microscopy（SEM） analyses show the presence of TiB2 and Al2O3 only in the composite powders produced by SHS. The powders are uniform and free-agglomerate. Transmission electron microscopy （TEM） and high resolution electron microscopy （HREM） observation of microstructure of the composite powders indicate that the interfaces of the TiB2-Al2O3 bond well, without any interfacial reaction products. It is proposed that the good interfacial bonding of the composite powders can be resulted from the TiB2 particles crystallizing and growing on the Al2O3 particles surface with surface defects acting as nucleation centers.
文摘Mechanical properties were tested for in situ TiB2/A357 composite fabricated by LSM (mixed salts reaction) method. Micro structures of as cast and plastic deformed TiB2/A357 were investigated. The results show that there is a low misfit between (200) Al and (101)TiB2 with [011]//Al [101]TiB2. There is a change from fully dendritic structure of the α-Al of A357 to a rosette-type structure of TiB2/A357. Significant increases in proof stress and Young's modulus can be obtained at low TiB2 additions. There exist dislocation loops around neighboring TiB2 particles with about 0.1μm in diameter and dislocation multiplication near TiB2 particles.
文摘The thermodynamic analysis of the formation of in-situ reinforced phases in （TiB2＋Al3Ti）/Al-4.5Cu composites prepared by mixed salts reaction was conducted, and heat changes of mixed salts system were analyzed by differential thermal analysis（DTA）.The results show that although TiB2 possesses the strongest formation ability in Al-Ti-B ternary system, [Ti] is relatively excessive in the in-situ reaction and it combines with Al to form AlaTi phase. The reinforced phases are TiB2 and AlaTi in the produced composites due to the reaction taking place to form reinforced phase with the addition of mixed salts into Al-4.5Cu melt between 900 ℃ and 1 032 ℃.