原位合成TiB_2-TiC陶瓷基复合材料

分析了 Ti B2 - Ti C陶瓷基复合材料的原位生成机理 ,利用普通的热压烧结设备 ,以 Ti H2 - B4C为原料原位合成了高性能的 Ti B2 - Ti C陶瓷基复合材料。 TEM和 X射线衍射的研究结果表明 :原位合成的复合材料中 Ti B2 为长柱状的显微形貌 。

原位Al_2O_3和TiB_2粒子增强Al-Cu合金基复合材料的制备和性能

由ＴｉＯ２ＡｌＢＣｕＯ体系制备了原位Ａｌ２Ｏ３和ＴｉＢ２粒子增强Ａｌ３．２％Ｃｕ和Ａｌ６．０％Ｃｕ合金基复合材料。Ｘ射线衍射分析表明，在两种复合材料中均有Ａｌ２Ｏ３和ＴｉＢ２生成，没有发现Ａｌ３Ｔｉ相产生。原位生成的Ａｌ２Ｏ３和ＴｉＢ２粒子为尺寸小于２μｍ的等轴状粒子，在Ａｌ基体中均匀分布。室温拉伸试验表明两种ＡｌＣｕ合金基原位复合材料具有很高的强度，并且随着基体合金中Ｃｕ含量的增加复合材料的强度增加。动态压缩试验表明，这种ＡｌＣｕ合金基原位复合材料的强度对应变速率是不敏感的，这可由不同应变速率变形后的复合材料基体中位错密度大致相同来解释。高温压缩蠕变试验表明，两种复合材料均表现出高的显态应力指数。随基体合金中Ｃｕ含量的增加复合材料的蠕变抗力明显提高。

ZrB2加入量对BN-AlN-TiB2复相陶瓷性能的影响

以h-BN、TiB2、AlN、Y2O3粉为主要原料,研究了ZrB 2的加入量(添加质量分数分别为1%、2%、3%、4%和5%)对BN-AlN-TiB 2复相陶瓷显气孔率、抗弯强度和电阻率的影响,并用XRD和SEM分别表征了试样的物相组成和显微结构。结果表明:随着ZrB2添加量(w)从1%增加到5%,BN-AlN-TiB2复相陶瓷的显气孔率显著降低,抗弯强度显著提高,而电阻率明显降低。当ZrB2加入量(w)为5%时,BN-AlN-TiB2复相陶瓷的各项性能较佳。

原材料特性对 SiC-TiB_2 复合陶瓷性能的影响

以微米级α－ＳｉＣ粉为原料，用常压烧结法制备ＳｉＣ－１５％ＴｉＢ２（体积分数）复合陶瓷．研究了原材料特性如烧结助剂种类、增韧相类型和原料ＳｉＣ粉粒度对材料性能和显微组织的影响．结果表明，Ａｌ－Ｂ－Ｃ是ＳｉＣ－ＴｉＢ２复合陶瓷的有效烧结助剂．用它为助剂制备的陶瓷其相对密度和抗弯强度高于以Ｂ－Ｃ，Ａｌ－Ｃ和Ｓｉ－Ｃ为助剂的ＳｉＣ陶瓷．与纯ＴｉＢ２粉末相比，以ＴｉＢ２－ＳｉＣ复合粉为增韧相的复合陶瓷性能改善，且抗氧化性较好．ＳｉＣ原料粉末的粒度是影响ＳｉＣ可烧结性最重要的因素．粒度愈细，ＳｉＣ陶瓷的相对密度和抗弯强度愈高．

钢水连续测温用BN-AlN-TiB_2复合陶瓷热电偶保护管

首次采用BN -AlN -TiB2 复合陶瓷材料制作的热电偶保护管 ,在中间包钢水中连续使用了 4 .5h ,连续测温与点测值的误差仅为± 2℃ 保护管侵蚀最严重的部分是与钢渣的接触面 ,厚度仅减薄了 2 .5mm 造成保护管侵蚀较少的原因是TiB2 被氧化成TiO2 后阻止了氧化层向内部进一步扩散以及TiB2 ,TiO2

添加剂镍对原位合成TiB_2-TiC复相陶瓷材料性能的影响

用TiH2 ,Ni和B4 C作为原料 ,采用热等静压法制备了TiB2 TiC复相陶瓷材料 ,此方法工艺简单 ,成本较低。XRD研究表明在样品中只存在TiB2 和TiC两相 ;TEM研究结果表明TiB2 晶粒为规则的多边形和板条状 ,添加剂Ni位于TiB2 TiC交界处 ;显微硬度、断裂韧性和SEM断口形貌的研究结果表明添加剂Ni显著提高了TiB2 TiC复相陶瓷材料的综合性能。

Effect of nano-graphite on mechanical properties and oxidation resistance of ZrB_(2)-SiC-graphite electrode ceramics

ZrB_(2)-based ceramic composites were prepared by spark plasma sintering using ZrB_(2) powder prepared by molten salt method as raw material and SiC and nano-graphite as additives.The effects of nano-graphite addition on the physical properties and oxidation resistance of ZrB_(2)-based ceramic samples were investigated.The results show that the addition of an appropriate amount of nano-graphite can effectively improve the density of ZrB_(2)-based ceramic composites and improve the physical properties of the materials.The flexural strength of the ceramic sample with 8 vol.%nano-graphite reached 418.54 MPa,which was 53.14% higher than that of ZrB_(2)-SiC ceramic material(273.31 MPa),and its oxidation resistance was also significantly improved.It demonstrats that the addition of an appropriate amount of nano-graphite can effectively improve the physical properties and oxidation resistance of ZrB_(2)-SiC ceramic composites.Via prolonging its service life in application and promoting the development of ZrB_(2)-based ceramic composites,it is of great significance for clean steel smelting.

激光熔覆原位自生复合材料涂层的研究

利用激光熔覆技术,使用HL 1500型CO2 激光器在 45#钢表面制备出原位自生成的Ni基金属陶瓷TiB2 涂层。并采用现代化分析手段对涂层的宏观形貌,显微组织特征和元素分部进行了系统的观察和分析。研究结果表明,熔覆合金层显微组织由枝晶固溶体及其间细密的共晶组织组成,涂层中存在γ Fe,γ Ni,TiB2,TiB和少量的Ni4B3。

过渡塑性相工艺制造Ti-B-C复合陶瓷材料

给出了以ＴｉＨ２和Ｂ４Ｃ为原料通过过渡塑性相工艺（ｔｒａｎｓｉｅｎｔｐｌａｓｔｉｃｐｈａｓｅｐｒｏｃｅｓｓｉｎｇ）制备Ｔｉ－Ｂ－Ｃ复合陶瓷材料的方法。同时进行了ＴｉＨ２－Ｂ４Ｃ体系和Ｔｉ－Ｂ４Ｃ体系的对比实验，结果表明，ＴｉＨ２在８００℃以下分解获得高性能的Ｔｉ粉和Ｂ４Ｃ发生了如下反应：（３＋ｘ）Ｔｉ＋Ｂ４Ｃ→２ＴｉＢ２＋（１＋ｘ）ＴｉＣ１１＋ｘ（０≤ｘ≤１）。在相同条件下以ＴｉＨ２作为过渡塑性相的ＴｉＨ２－Ｂ４Ｃ体系比Ｔｉ－Ｂ４Ｃ体系具有优越的烧结性能，在１６００℃时热压烧结４ｈ可以获得高性能的ＴｉＢ２－ＴｉＣｘ复合陶瓷材料（断裂韧性为７．７ＧＰａｍ１／２，抗弯强度为７６５ＭＰａ）。还利用Ｘ衍射和扫描电镜对这种材料的显微结构进行了研究。