The hardness values and the wear resistance of Al2O3P/ Zn-Al composite, prepared by means of rheological casting technology,are investigated separately in this work. The results show that the addition of Al2O3P increa...The hardness values and the wear resistance of Al2O3P/ Zn-Al composite, prepared by means of rheological casting technology,are investigated separately in this work. The results show that the addition of Al2O3P increases the hardness values of the matrix at both room and high temperature and improves the wear resistance of the material.The hardness values and the wear resistance of the composite rise with the increase of the particle volume fraction or the decrease of the particle size.The raising of test temperature results in a rapid descending of its hardness values.However, the addition of Al2O3P improves the property of high temperature resistance of Zn-Al alloys significantly.Moreover,the effect of quenching, tempering or cycling heat treatment on the hardness values of the composite is also studied.展开更多
A γ-Al2O3 particles reinforced Al-Si alloy matrix composite was fabricated by adding NH4Al（SO4）2 to molten aluminum alloy. TEM observation shows that in-situ γ-Al2O3 particles are generally spherical and uniformly...A γ-Al2O3 particles reinforced Al-Si alloy matrix composite was fabricated by adding NH4Al（SO4）2 to molten aluminum alloy. TEM observation shows that in-situ γ-Al2O3 particles are generally spherical and uniformly distributed in the matrix. The results of dry sliding wear tests show that the wear resistance of the composites increases with increasing mass fraction, and the volume loss is considerably lesser than that of the matrix and is lesser than that of the composites by adding γ-Al2O3 particles directly.展开更多
文摘The hardness values and the wear resistance of Al2O3P/ Zn-Al composite, prepared by means of rheological casting technology,are investigated separately in this work. The results show that the addition of Al2O3P increases the hardness values of the matrix at both room and high temperature and improves the wear resistance of the material.The hardness values and the wear resistance of the composite rise with the increase of the particle volume fraction or the decrease of the particle size.The raising of test temperature results in a rapid descending of its hardness values.However, the addition of Al2O3P improves the property of high temperature resistance of Zn-Al alloys significantly.Moreover,the effect of quenching, tempering or cycling heat treatment on the hardness values of the composite is also studied.
基金the Key Project of Ministry of Education of China (No.105055).
文摘A γ-Al2O3 particles reinforced Al-Si alloy matrix composite was fabricated by adding NH4Al（SO4）2 to molten aluminum alloy. TEM observation shows that in-situ γ-Al2O3 particles are generally spherical and uniformly distributed in the matrix. The results of dry sliding wear tests show that the wear resistance of the composites increases with increasing mass fraction, and the volume loss is considerably lesser than that of the matrix and is lesser than that of the composites by adding γ-Al2O3 particles directly.