MoSi/Ti composite coatings (MoST?), have been deposited by a closed-field unbalanced magnetron sputter ion-plating system. The high ion-current densities at low substrate bias voltage of the system ensures that the Mo...MoSi/Ti composite coatings (MoST?), have been deposited by a closed-field unbalanced magnetron sputter ion-plating system. The high ion-current densities at low substrate bias voltage of the system ensures that the MoST? coatings are characteristic of dense coherent structures, with high adhesion (critical scratch load above 120 N), high load bearing capacity up to 5 GPa., low friction (0.02-0.1), high wear resistance (less than 4xlO"17 m3/N m) even at a relative humidity of 40%, and high temperature resistance up to 350 °C. The successful applications of MoST? coatings in large- scale productions for dry cutting and forming, with increasing lifetime and productivity are presented.展开更多
TiAl3-Al coating was deposited on orthorhombic Ti2AlNb alloy substrate by cold spraying with the mixture of pure Al and Ti as the feedstock powder at a fixed molar ratio of 3-1 when the spraying distance,gas temperatu...TiAl3-Al coating was deposited on orthorhombic Ti2AlNb alloy substrate by cold spraying with the mixture of pure Al and Ti as the feedstock powder at a fixed molar ratio of 3-1 when the spraying distance,gas temperature and gas pressure for the process were 10 mm,250 ℃ and 1.8 MPa,respectively.The as-sprayed coating was then subjected to heat treatment at 630 ℃ in argon atmosphere for 5 h at a heating rate of 3 ℃/min and an argon gas flow rate of 40 mL/min.The obtained TiAl3-Al composite coating is about 212 μm with a density of 3.16 g/cm3 and a porosity of 14.69% in general.The microhardness and bonding strength for the composite coating are HV525 and 27.12 MPa.展开更多
文摘MoSi/Ti composite coatings (MoST?), have been deposited by a closed-field unbalanced magnetron sputter ion-plating system. The high ion-current densities at low substrate bias voltage of the system ensures that the MoST? coatings are characteristic of dense coherent structures, with high adhesion (critical scratch load above 120 N), high load bearing capacity up to 5 GPa., low friction (0.02-0.1), high wear resistance (less than 4xlO"17 m3/N m) even at a relative humidity of 40%, and high temperature resistance up to 350 °C. The successful applications of MoST? coatings in large- scale productions for dry cutting and forming, with increasing lifetime and productivity are presented.
文摘TiAl3-Al coating was deposited on orthorhombic Ti2AlNb alloy substrate by cold spraying with the mixture of pure Al and Ti as the feedstock powder at a fixed molar ratio of 3-1 when the spraying distance,gas temperature and gas pressure for the process were 10 mm,250 ℃ and 1.8 MPa,respectively.The as-sprayed coating was then subjected to heat treatment at 630 ℃ in argon atmosphere for 5 h at a heating rate of 3 ℃/min and an argon gas flow rate of 40 mL/min.The obtained TiAl3-Al composite coating is about 212 μm with a density of 3.16 g/cm3 and a porosity of 14.69% in general.The microhardness and bonding strength for the composite coating are HV525 and 27.12 MPa.