TiO_2 films were coated on the surface of diamond particles using a sol-gel method. The effects of heat treatment temperature on the morphology, phase composition and chemical bond of diamond particles coated with TiO...TiO_2 films were coated on the surface of diamond particles using a sol-gel method. The effects of heat treatment temperature on the morphology, phase composition and chemical bond of diamond particles coated with TiO2 films were investigated through SEM, TEM, X-ray diffraction analysis, Raman spectroscopy, FTIR, and XPS. The results showed that when being heat-treated at 600 ℃, the amorphous TiO_2 film transfered to the anatase film which bonded well with diamond substrate. Meanwhile, the Ti-O-C bond formed between TiO2 film and diamond substrate. When being heat-treated at 800 ℃, TiO2 film was still anatase, and partial diamond began to graphitize. The graphitizated carbon could also form the Ti-O-C bond with TiO_2 film, although TiO_2 film would tend to crack in this case.展开更多
基金Funded by National Natural Science Foundation of China(No.51375157)Shanghai Aerospace Eighth Research Institute SAST Foundation(No.2015044)+1 种基金the Central University Basic Scientific Research Business Expenses,State Key Laboratory of Silicate Materials for Architectures Program(No.SYSJJ2015-09)the Hunan Province Key Laboratory of Environmental Photocatalysis Application Technology Program(No.CCSU-KF-1504)
文摘TiO_2 films were coated on the surface of diamond particles using a sol-gel method. The effects of heat treatment temperature on the morphology, phase composition and chemical bond of diamond particles coated with TiO2 films were investigated through SEM, TEM, X-ray diffraction analysis, Raman spectroscopy, FTIR, and XPS. The results showed that when being heat-treated at 600 ℃, the amorphous TiO_2 film transfered to the anatase film which bonded well with diamond substrate. Meanwhile, the Ti-O-C bond formed between TiO2 film and diamond substrate. When being heat-treated at 800 ℃, TiO2 film was still anatase, and partial diamond began to graphitize. The graphitizated carbon could also form the Ti-O-C bond with TiO_2 film, although TiO_2 film would tend to crack in this case.