According to the design principle of the central composite experimental,the method of response surface analysis with three factors and three levels was adopted based on one factor test.A second-order quadratic equatio...According to the design principle of the central composite experimental,the method of response surface analysis with three factors and three levels was adopted based on one factor test.A second-order quadratic equation for photocatalysis of Procion Red MX-5B was built.Response surface and contour were graphed with the decoloration rate of Procion Red MX-5B as the response value.Based on the analysis of the response surface plots and their corresponding contour plots,effects of pH value,irradiation time and catalyst loading were explored.By using this new method,the optimum decoloration condition was obtained as follows:pH value,1.3;irradiation time,49.9 min;catalyst loading,0.57 g/L.In the optimization,R-Squared and Adj R-Squared correlation coefficients for quadratic model were evaluated quite satisfactorily as 0.9310 and 0.8620,respectively.Under the optimum conditions established,the performance of 99.47% for color removal was experimentally reached.It was found that all factors considered have an important effect on the decolorization efficiency of Procion Red MX-5B.By the ANOVA analysis and model confirmation the optimal solution obtained using RSM was experimentally validated and credible with preferable instructional ability for experiments.展开更多
Nano TiO2/Fe3O4 composite particles with different molar ratios of TiO2 to Fe3O4 were prepared via sol-gel method. X-ray diffraction, transmission electron microscopy, and vibration sample magnetometry were used to ch...Nano TiO2/Fe3O4 composite particles with different molar ratios of TiO2 to Fe3O4 were prepared via sol-gel method. X-ray diffraction, transmission electron microscopy, and vibration sample magnetometry were used to characterize the TiO2/Fe3O4 particles. The photocatalytic activity of the particles was tested by degrading methyl blue solution under UV illumination （254 nm）. The results indicate that with the content of TiO2 increasing, the photocatalytic activity of the composite particles enhances, while the magnetism of the particles decreases. When the molar ratio of TiO2 to Fe3O4 is about 8, both the photocatalytic activity and magnetism of the TiO2/Fe3O4 particles are relatively high, and their photocatalytic activity remains well after repeated use.展开更多
基金Sponsored by the National Natural Science Foundation of China (Grant No. 51078100)the National Creative Research Groups granted by NSFC(Grant No. 50821002)+1 种基金Excellent Youth Foundation of Heilongjiang Scientific Committee(Grant No. JC2010-03)State Key Laboratory of Urban Water Resource and Environment(Grant No. 2010DX11)
文摘According to the design principle of the central composite experimental,the method of response surface analysis with three factors and three levels was adopted based on one factor test.A second-order quadratic equation for photocatalysis of Procion Red MX-5B was built.Response surface and contour were graphed with the decoloration rate of Procion Red MX-5B as the response value.Based on the analysis of the response surface plots and their corresponding contour plots,effects of pH value,irradiation time and catalyst loading were explored.By using this new method,the optimum decoloration condition was obtained as follows:pH value,1.3;irradiation time,49.9 min;catalyst loading,0.57 g/L.In the optimization,R-Squared and Adj R-Squared correlation coefficients for quadratic model were evaluated quite satisfactorily as 0.9310 and 0.8620,respectively.Under the optimum conditions established,the performance of 99.47% for color removal was experimentally reached.It was found that all factors considered have an important effect on the decolorization efficiency of Procion Red MX-5B.By the ANOVA analysis and model confirmation the optimal solution obtained using RSM was experimentally validated and credible with preferable instructional ability for experiments.
基金supported by the National Natural Science Foundation of China (Nos. 50872011, 50402022, and 50672006)the National Basic Research Program of China (No. 2007CB613608)
文摘Nano TiO2/Fe3O4 composite particles with different molar ratios of TiO2 to Fe3O4 were prepared via sol-gel method. X-ray diffraction, transmission electron microscopy, and vibration sample magnetometry were used to characterize the TiO2/Fe3O4 particles. The photocatalytic activity of the particles was tested by degrading methyl blue solution under UV illumination （254 nm）. The results indicate that with the content of TiO2 increasing, the photocatalytic activity of the composite particles enhances, while the magnetism of the particles decreases. When the molar ratio of TiO2 to Fe3O4 is about 8, both the photocatalytic activity and magnetism of the TiO2/Fe3O4 particles are relatively high, and their photocatalytic activity remains well after repeated use.