锐钛矿型TiO_2水溶胶的低温制备及其表征

Anatase titanium dioxide hydrosol was prepared at low temperature by a simple method. The title material was characterized by TEM, XRD, FTIR and BET, respectively. The photocatalytic activity of the as-prepared TiO2 was evaluated by the degradation of methyl orange solution under sunlight and the photocatalytic oxidation of acetone in air. The results showed that the titanium dioxide hydrosol was composed of anatase phase with average grain size of about 7 nm, and the crystallinity became more perfect with the increase of temperature. The BET surface areas were more than 220 m2·g-1 for these samples. It is found that the photocatalytic activity was much better for the higher heat processing temperature. Especially, the photocatalytic activity of the sample with a heat treatment of 110 ℃ was better than that of P25. In addition, TiO2 hydrosol also possessed good photocatalytic activity under the sunlight illumination.

具有混晶结构纳米TiO_2水溶胶的低温制备及光催化性能研究

以工业级四氯化钛为原料,利用过氧化法于低温下制得了同时具有金红石相和锐钛矿相的纳米二氧化钛水溶胶。该溶胶为透明稳定的中性水溶液。并用FT-IR、XRD、紫外-可见光吸收光谱、TEM等多种手段对混晶型纳米二氧化钛水溶胶进行测试和表征。结果表明,利用过氧化法在低温下就能制得稳定的具有混晶结构的纳米二氧化钛水溶胶。对纳米二氧化钛水溶胶的光催化性能研究表明,在可见光下甲醛消解率在8 h内就达到93%,杀菌率达到99%。

稳定TiO_2水溶胶的制备及其在棉织物上的紫外线屏蔽整理

研究用钛酸丁酯作前驱物 ,水作溶剂 ,冰乙酸为稳定剂 ,制备稳定的TiO2 水溶胶 ,测定了不同温度、pH值下TiO2 水溶胶的凝胶时间。并将TiO2 水溶胶用于纯棉织物后整理上 ,结果表明 :用含 0 9%的TiO2 水溶胶整理的纯棉织物 ,在波长 2 97nm处紫外线屏蔽率达到 93% ,同时还有一定的疏水作用 ,经过整理的纯棉织物的水滴润湿时间远大于 1h。

纳米TiO_2水溶胶整理涤纶织物的自清洁性能的定量化研究

为了研究纳米TiO_2整理织物的自清洁性能,首先使用自制的宽光谱响应型纳米TiO_2水溶胶通过浸染工艺整理涤纶织物,然后采用染料罗丹明B作为特定模拟污垢,定量化考察了纳米TiO_2水溶胶添加量和染料浓度对整理织物自清洁性能的影响,并与浸轧整理工艺进行了比较.研究结果表明:使用纳米TiO_2水溶胶通过浸染工艺能够制备具有优良自清洁性能的整理涤纶织物,提高纳米TiO_2水溶胶添加量不仅能够增加纳米TiO_2粒子在涤纶织物表面负载量,而且能够对吸附于表面的染料、咖啡和酱油等实现自清洁效应,其对3种污渍最终的去除率分别达到95.24%、57.14%和70.06%.此外,浸染法制备的纳米TiO_2整理涤纶织物比浸轧法具有更好的自清洁性能.

稳定TiO_2水溶胶的紫外线屏蔽整理

简述了紫外线屏蔽整理原理及溶胶-凝胶原理;分析了稳定的TiO2水溶胶对不同纤维素纤维织物及M/T/C织物进行紫外线屏蔽整理的效果,讨论了纤维种类、形态结构、织物组织结构、厚度、染色用染料类别及染色色泽对织物紫外线屏蔽整理效果的影响,结果表明:稳定的TiO2水溶胶对织物进行紫外线屏蔽整理效果较好,是一种很有前途的整理方法。

溶胶-凝胶法低温制备TiO_2水溶胶工艺研究

采用正交试验法，以水溶胶对甲基橙的降解率为考察指标，对改进的溶胶-凝胶法低温制备高光催化活性TiO2水溶胶的工艺进行优化，并研究各因素对水溶胶光催化活性的影响。结果表明：pH值对水溶胶光催化活性的影响最显著，其次是回流温度、回流时间，TiCl4与加入的蒸馏水体积比的影响最小。推荐优选工艺条件是TiCl4与加入的蒸馏水体积比1：25、pH值8—9、回流温度80℃、回流时间6—8h。

稳定TiO_2水溶胶的制备及其对苎麻织物紫外线屏蔽整理的探讨

研究了用钛酸正丁酯为前驱物,水为溶剂,冰乙酸作稳定剂,采用溶胶-凝胶技术,制备稳定的TiO2水溶胶;简述了紫外线屏蔽整理原理及溶胶-凝胶原理;探讨了稳定的TiO2水溶胶对苎麻织物进行紫外线屏蔽整理的效果,结果表明:紫外线屏蔽整理效果较好,是一种很有前途的整理方法.

La/TiO_2-SiO_2水溶胶的制备及其稳定性研究

以钛酸正四丁脂和正硅酸乙酯为前驱物,水为溶剂,冰乙酸为稳定剂,醋酸镧为掺杂物,采用无醇、少酸工艺,制备La/TiO2-SiO2水溶胶,分析了TiO2与SiO2摩尔比、掺镧量、冰乙酸与钛酸丁脂摩尔比、水与钛酸丁脂摩尔比及搅拌时间对La/TiO2-SiO2水溶胶稳定性的影响.

TiO_2水溶胶在棉织物多功能免烫整理中的应用

利用二氧化钛水溶胶和KH-1超低甲醛树脂对棉织物进行免烫整理。探讨了制备二氧化钛水溶胶的转速、整理工艺条件及洗涤对整理织物性能的影响。结果表明,以(1 010±20)r/min的转速制备的TiO_2水溶胶的整理效果最好,最佳整理工艺为TiO_2水溶胶用量40g/L,KH-1树脂用量70g/L,pH值4.5,80℃预烘3min,150℃焙烘2min。

棉织物的TiO_2溶胶/BTCA免烫整理

研究了二氧化钛(TiO_2)水溶胶与丁烷四羧酸(BTCA)相结合,用于棉织物的免烫整理工艺。探讨了稳定剂用量、整理方式及工艺条件对织物性能的影响。试验结果表明,以乙酰丙酮为稳定剂的一浴法整理效果最好;最佳免烫整理工艺为:乙酰丙酮与TiO_2物质的量之比为1∶1,溶胶30 g/L,BTCA 70 g/L,pH值4.5,150℃焙烘2 min。

TiO_2薄膜的低温制备及其光催化活性研究

利用所制备的锐钛矿型TiO2水溶胶提拉法成膜,用Raman和TEM分析了TiO2薄膜的晶型和基团结构。可知TiO2颗粒为锐钛矿晶型,晶粒在10 nm左右,并以多个单晶的形式粘结成膜。气体光催化和甲基橙降解实验表明,所制得的TiO2薄膜具有良好的光催化活性。

纳米二氧化钛水溶胶对涤纶织物的抗静电整理

分析了纺织品产生静电的机理,并采用溶胶——凝胶法和微乳法制得的纳米TiO2水溶胶处理涤纶机织物,系统地分析了各种工艺因素对抗静电效果的影响并对整理后的织物性能进行了测试,通过正交实验得到最佳的整理工艺为:纳米TiO2水溶胶质量浓度为1.412g/L,处理温度为50℃,处理时间为30min,通过测试表明达到了较好的效果。

纳米TiO_2功能化纺织品的制备及性能研究

使用自制的纳米TiO_2水溶胶通过后整理工艺对棉织物进行处理得到纳米TiO_2水溶胶整理棉织物,对纳米TiO_2水溶胶整理织物进行了表征,并测试了其对染料的光催化降解性、甲醛降解性能、自清洁性能及抗菌性能。结果表明,纳米TiO_2水溶胶整理棉织物在光辐射条件下对水中的染料和室内空气中的甲醛具有显著的光催化降解作用。且该整理棉织物不仅具有显著的抗菌性,还能对吸附于其表面的老抽污渍进行光催化降解,实现自清洁效应,是一种集光催化、自清洁和抗菌的多功能织物。

复合溶胶-凝胶法改善PBO纤维的光稳定性

分别以钛酸正丁酯(C_(16)H_(36)O_4Ti)、醋酸(CH_3COOH)、盐酸(HCl)、丙基三甲氧基硅烷(KH560)、苯基三甲氧基硅烷(Ph-TMS)、甲醇(CH_3OH)和去离子水为原料,氨水(NH_3·H_2O)为催化剂,采用溶胶-凝胶法和复合溶胶-凝胶法分别涂覆制备防老化聚亚苯基苯并二噁唑(PBO)纤维。通过粒度分析验证了纳米溶胶的成功制备,通过EDS能谱、SEM扫描电镜、接触角测定等手段分析测试PBO纤维表面的化学组成与物理性能,验证防老化PBO纤维的制备。以拉伸强度测试、SEM扫描电镜和表面接触角表征PBO纤维的防老化性能。结果表明:在氙灯耐气候试验箱经历130 h的老化后,与未经过涂覆的PBO原纤相比,采用纳米TiO_2水溶胶-凝胶法涂覆的PBO纤维拉伸强度保持率只提高了5%,利用纳米有机硅溶胶-凝胶法涂覆的PBO纤维拉伸强度保持率可提高10%,而经过纳米TiO_2和有机硅复合溶胶-凝胶法涂覆的PBO纤维,拉伸强度保持率提高了27%,且老化后的纤维表面保持得非常完整。

溶胶-凝胶法对纯羊毛织物的抗菌整理工艺

采用溶胶-凝胶技术制备出稳定的TiO2/ZnO复合水溶胶,在溶胶阶段通过轧焙烘工艺对纯羊毛织物进行抗菌整理。研究了TiO2与ZnO的掺杂比例、复合溶胶用量及焙烘温度对毛织物抗菌功能的影响,并对整理后织物的抗菌功能耐久性进行了分析。研究结果表明,整理后的毛织物具有很好的抑菌功能,且织物的断裂强度、回潮率、硬挺性等物理机械性能都有所提高。经50次水洗之后,对金葡萄糖球菌和大肠杆菌的抑菌率分别为85.8%和77.5%。