改性溶胶包覆法制备聚苯胺/TiO_2-Fe_3O_4纳米复合物及吸波性能研究

通过改性溶胶法制备了Fe3O4纳米粒子均匀弥散于TiO2中的TiO2-Fe3O4二元纳米复合物,再在不同pH条件下原位聚合生长聚苯胺(PAn),获得了三元包覆纳米复合物PAn/TiO2-Fe3O4.采用透射电镜(TEM)、红外光谱(FT-IR)、粉末X-射线衍射(XRD)及电磁测量等手段对TiO2-Fe3O4和PAn/TiO2-Fe3O4的形貌、结构及性能进行了表征.实验结果表明,通过调节TiO2溶胶形成及包覆过程温度、介质pH值,能获得Fe3O4纳米粒子均匀弥散于TiO2中的二元纳米复合物,且其中TiO2为锐钛矿结构,Fe3O4为立方晶系,而形成的三元复合物PAn/TiO2-Fe3O4则呈现微米纤维结构.当三元复合物中Fe3O4和TiO2的的质量分数分别为6.4%和15.8%时,PAn/TiO2-Fe3O4在13.6 GHz处具有最大的反射损耗-36.4 dB,小于-10 dB的吸收带宽达到4.4 GHz,具有良好的吸波性能.

复合固体超强酸SO_4^(2-)/TiO_2-Fe_2O_3催化合成丁酸异丁酯

The composite solid superacid SO2-4/TiO2-Fe2O3(nTi∶nFe=2∶1)was prepared by the method of deveiopmental sol-gel and wet impregnation.First reported the composite solid superacid catalysis synthesized isobutyl butyrate for buthlacid and isobutyl alcohol.It was researched that the acid-alcohol rate,time,quantity and repeatly applicatiom of catalyzes had imflune upon yield of esterication reaction.The influent actors of reaction were investigated.The results showed that teh appropriate conditions should be:weight of cstalyst was 10g;molar ratio of isobutyl alcohol to buthlacid was 18∶1;reaction time was 30h;the taking water reagent (Benzene) was 15ml.The yield of isobutyl butyrate was about 985%.The acid value was:1602<Ho<1452.

Au与Fe_3O_4纳米微粒共嵌TiO_2纳米纤维的制备及可见光催化性能

通过静电纺丝法制备出含有Fe3O4纳米微粒的TiO2纳米纤维,再采用浸渍还原法将Au纳米微粒嵌入到TiO2纳米纤维上,制备出一种具有较强磁性和良好可见光响应能力的复合光催化材料.采用X射线衍射仪(XRD)、扫描电子显微镜(SEM)、透射电子显微镜(TEM)和紫外-可见固体漫反射光谱仪(UV-VisDRS)等对样品的结构和形貌进行表征,并以降解罗丹明B(RhB)为模型反应,考察了样品在可见光照射下的光催化性能.结果表明,嵌入Au纳米微粒可使复合纳米纤维在可见光下降解RhB时表现出非常好的降解速率和降解率;同时,将Fe3O4纳米微粒嵌入TiO2纳米纤维内部可以赋予材料较强的磁性,使材料便于分离和重复利用.

高盐度有机废水磁载催化剂降解工艺研究

以均匀沉淀法制备的Fe3O4磁粒为核心,以钛酸丁酯、正硅酸乙酯为原料,采用溶胶-凝胶法制备了磁载TiO2-SiO2-Fe3O4复合微粒,运用X射线衍射(XRD)、红外(IR)测试方法对所制得复合粒子进行表征,并以TiO2-SiO2-Fe3O4复合微粒为催化剂研究其高盐度有机废水催化降解的性能。结果表明,磁基体Fe3O4上包覆了一层SiO2和TiO2,制得磁载TiO2-SiO2-Fe3O4复合微粒。当有机废水pH=4.0,该催化剂的用量为3.0 g/L,空气体积流量为2 L/min,反应时间为1 h、温度为60℃时,COD的去除率为62.0%。