This article studies the role of electrochemical parameters in controlling the morphology of oxidized TiO_(2)nanotubes and the electrochemical performance of modified TiO_(2)nanotubes.Humidity is a key factor for fabr...This article studies the role of electrochemical parameters in controlling the morphology of oxidized TiO_(2)nanotubes and the electrochemical performance of modified TiO_(2)nanotubes.Humidity is a key factor for fabricating TiO_(2)nanotubes.When the relative humidity belows 70%,the TiO_(2)nanotubes can be successfully prepared.What's more,by changing the anodization voltage and time,the diameter and the length of TiO_(2)nanotubes can be adjusted.In addition,the TiO_(2)nanotubes are modified through electrochemical self-doping and loading Pt metal particles on the surface of the nanotubes,which promotes the performance of the supercapacitor.The sample anodized at 100 V for 3 h has a specific capacity of up to 2.576 mF/cm~2 at a scan rate of 100 mV/s after self-doping,and its capacity retention rate still remains at 89.55%after 5000 cycles,demonstrating excellent cycling stability.The Pt-modified sample has a specific capacity of up to 3.486 mF/cm~2 at the same scan rate,exhibiting more outstanding electrochemical performance.展开更多
A catalyst of ferroelectric-BaTiO_(3)@photoelectric-TiO_(2) nanohybrids(BaTiO_(3)@TiO_(2))with enhanced photocatalytic activity was synthesized via a hydrolysis precipitation combined with a hydrothermal approach.Comp...A catalyst of ferroelectric-BaTiO_(3)@photoelectric-TiO_(2) nanohybrids(BaTiO_(3)@TiO_(2))with enhanced photocatalytic activity was synthesized via a hydrolysis precipitation combined with a hydrothermal approach.Compared to pure TiO_(2),pure BaTiO_(3) and BaTiO_(3)/TiO_(2) physical mixture,the heterostructured BaTiO_(3)@TiO_(2) exhibits significantly improved photocatalytic activity and cycling stability in decomposing Rhodamine B(RhB)and the degradation efficiency is 1.7 times higher than pure TiO_(2) and 7.2 times higher than pure BaTiO_(3).These results are mainly attributed to the synergy effect of photoelectric TiO_(2),ferroelectric-BaTiO_(3) and the rationally designed interfacial structure.The mesoporous microstructure of TiO_(2) is of a high specific area and enables excellent photocatalytic activity.The ferroelectric polarization induced built-in electric field in BaTiO_(3) nanoparticles,and the intimate interfacial interactions at the interface of BaTiO_(3) and TiO_(2) are effective in driving the separation and transport of photogenerated charge carriers.This strategy will stimulate the design of heterostructured photocatalysts with outstanding photocatalytic performance via interface engineering.展开更多
基金National Natural Science Foundation of China(No.12004070)。
文摘This article studies the role of electrochemical parameters in controlling the morphology of oxidized TiO_(2)nanotubes and the electrochemical performance of modified TiO_(2)nanotubes.Humidity is a key factor for fabricating TiO_(2)nanotubes.When the relative humidity belows 70%,the TiO_(2)nanotubes can be successfully prepared.What's more,by changing the anodization voltage and time,the diameter and the length of TiO_(2)nanotubes can be adjusted.In addition,the TiO_(2)nanotubes are modified through electrochemical self-doping and loading Pt metal particles on the surface of the nanotubes,which promotes the performance of the supercapacitor.The sample anodized at 100 V for 3 h has a specific capacity of up to 2.576 mF/cm~2 at a scan rate of 100 mV/s after self-doping,and its capacity retention rate still remains at 89.55%after 5000 cycles,demonstrating excellent cycling stability.The Pt-modified sample has a specific capacity of up to 3.486 mF/cm~2 at the same scan rate,exhibiting more outstanding electrochemical performance.
基金Project(cstc2020jcyj-msxm X0930) supported by the Natural Science Foundation of Chongqing,ChinaProject(KJQN201901522) supported by Technological Research Program of Chongqing Municipal Education Commission,ChinaProject(cx2020068) supported by the Venture&Innovation Support Program for Chongqing Overseas Returnees,China。
文摘A catalyst of ferroelectric-BaTiO_(3)@photoelectric-TiO_(2) nanohybrids(BaTiO_(3)@TiO_(2))with enhanced photocatalytic activity was synthesized via a hydrolysis precipitation combined with a hydrothermal approach.Compared to pure TiO_(2),pure BaTiO_(3) and BaTiO_(3)/TiO_(2) physical mixture,the heterostructured BaTiO_(3)@TiO_(2) exhibits significantly improved photocatalytic activity and cycling stability in decomposing Rhodamine B(RhB)and the degradation efficiency is 1.7 times higher than pure TiO_(2) and 7.2 times higher than pure BaTiO_(3).These results are mainly attributed to the synergy effect of photoelectric TiO_(2),ferroelectric-BaTiO_(3) and the rationally designed interfacial structure.The mesoporous microstructure of TiO_(2) is of a high specific area and enables excellent photocatalytic activity.The ferroelectric polarization induced built-in electric field in BaTiO_(3) nanoparticles,and the intimate interfacial interactions at the interface of BaTiO_(3) and TiO_(2) are effective in driving the separation and transport of photogenerated charge carriers.This strategy will stimulate the design of heterostructured photocatalysts with outstanding photocatalytic performance via interface engineering.