The Nd:TiO_(2 )PEO coatings were formed in a phosphate-based electrolyte with the addition of Nd_(2)O_(3 )under the current density of 150,200,250 and 300 m A/cm^(2).SEM results showed that the micropores decreased on...The Nd:TiO_(2 )PEO coatings were formed in a phosphate-based electrolyte with the addition of Nd_(2)O_(3 )under the current density of 150,200,250 and 300 m A/cm^(2).SEM results showed that the micropores decreased on quantity and increased on scale with the increasing current density.AFM results revealed that the roughness of the coatings increased with the increasing current density.Phase and composition analysis showed that the Nd:TiO_(2) coatings were mainly composed of anatase and rutile phase.And the anatase phase content has reached the maximum value at the current density of 250 m A/cm^(2).XPS results indicated that Ti2p spin-orbit components of the Nd:TiO_(2) coatings are shifted towards higher binding energy,compared with the pure TiO_(2) coating,suggesting that some of the Nd^(3+)ions are combined with TiO_(2) lattice and led to dislocation.Photocatalytic test showed that the photocatalytic activity of Nd:TiO_(2) coatings varied in the same pattern with the anatase content variation in Nd:TiO_(2) coatings.The photocatalytic experiment results show that the photocatalytic activity of Nd:TiO_(2) coatings can be greatly enhanced with moderate amount of Nd^(3+).However,excessive amount of Nd^(3+)does not have an effective impact on the photoctalytic activity improvement.展开更多
化工、纺织印染与农药化肥等产业的蓬勃发展推动着人类社会的进步,但同时也给环境治理带来了巨大难题。目前,光催化降解局限于在特定波长下针对单一有机污染物进行降解,然而现实中的情况往往更复杂。因此,开发一种多功能光催化材料用于...化工、纺织印染与农药化肥等产业的蓬勃发展推动着人类社会的进步,但同时也给环境治理带来了巨大难题。目前,光催化降解局限于在特定波长下针对单一有机污染物进行降解,然而现实中的情况往往更复杂。因此,开发一种多功能光催化材料用于光催化降解不同有机污染物显得尤为重要。采用一步无模板溶剂热法合成了核壳结构的C-TiO_(2)复合材料前驱体,并在氩气气氛下煅烧得到高结晶度的C-TiO_(2)复合光催化材料。运用SEM、TEM、XRD和TG等表征手段对材料进行表征,结论如下:550℃煅烧时的样品为包含少量碳的高结晶度的锐钛矿相TiO 2,且550℃煅烧时的样品依然保持了完整的核壳结构。此外,C-TiO_(2)复合材料的比表面积高达85.69 m 2·g^(-1),平均孔径为16.4 nm以及孔体积为0.423 m 3·g^(-1)。在UV-Vis光照射下,C-TiO_(2)复合材料分别对罗丹明B(RhB)、亚甲基蓝(MB)和刚果红(CR)3种染料显示出增强的光催化降解活性。展开更多
基金Supported by the Open Project Foundation of Industrial Perception and Intelligent Manufacturing Equipment Engineering Research Center of Jiangsu Province (No. ZK220504)the Open Project Foundation of High-tech Key Laboratory of Agricultural Equipment and Intelligence of Jiangsu Province (No. MAET202104)+1 种基金the Open Project Foundation of Jiangsu Wind Power Engineering Technology Center (No. ZK220302)the Qing Lan Project of Jiangsu Province,China。
文摘The Nd:TiO_(2 )PEO coatings were formed in a phosphate-based electrolyte with the addition of Nd_(2)O_(3 )under the current density of 150,200,250 and 300 m A/cm^(2).SEM results showed that the micropores decreased on quantity and increased on scale with the increasing current density.AFM results revealed that the roughness of the coatings increased with the increasing current density.Phase and composition analysis showed that the Nd:TiO_(2) coatings were mainly composed of anatase and rutile phase.And the anatase phase content has reached the maximum value at the current density of 250 m A/cm^(2).XPS results indicated that Ti2p spin-orbit components of the Nd:TiO_(2) coatings are shifted towards higher binding energy,compared with the pure TiO_(2) coating,suggesting that some of the Nd^(3+)ions are combined with TiO_(2) lattice and led to dislocation.Photocatalytic test showed that the photocatalytic activity of Nd:TiO_(2) coatings varied in the same pattern with the anatase content variation in Nd:TiO_(2) coatings.The photocatalytic experiment results show that the photocatalytic activity of Nd:TiO_(2) coatings can be greatly enhanced with moderate amount of Nd^(3+).However,excessive amount of Nd^(3+)does not have an effective impact on the photoctalytic activity improvement.
文摘化工、纺织印染与农药化肥等产业的蓬勃发展推动着人类社会的进步,但同时也给环境治理带来了巨大难题。目前,光催化降解局限于在特定波长下针对单一有机污染物进行降解,然而现实中的情况往往更复杂。因此,开发一种多功能光催化材料用于光催化降解不同有机污染物显得尤为重要。采用一步无模板溶剂热法合成了核壳结构的C-TiO_(2)复合材料前驱体,并在氩气气氛下煅烧得到高结晶度的C-TiO_(2)复合光催化材料。运用SEM、TEM、XRD和TG等表征手段对材料进行表征,结论如下:550℃煅烧时的样品为包含少量碳的高结晶度的锐钛矿相TiO 2,且550℃煅烧时的样品依然保持了完整的核壳结构。此外,C-TiO_(2)复合材料的比表面积高达85.69 m 2·g^(-1),平均孔径为16.4 nm以及孔体积为0.423 m 3·g^(-1)。在UV-Vis光照射下,C-TiO_(2)复合材料分别对罗丹明B(RhB)、亚甲基蓝(MB)和刚果红(CR)3种染料显示出增强的光催化降解活性。