3D hierarchical flowerlike WS_(2) microspheres were synthesized through a facile one-pot hydrothermal route.The as-synthesized samples were characterized by powder X-ray powder diffraction (XRD),energy-dispersive spec...3D hierarchical flowerlike WS_(2) microspheres were synthesized through a facile one-pot hydrothermal route.The as-synthesized samples were characterized by powder X-ray powder diffraction (XRD),energy-dispersive spectroscopy (EDS),scanning electron microscopy (SEM) and Raman.SEM images of the samples reveal that the hierarchical flowerlike WS_(2) microspheres with diameters of about 3-5μm are composed of a number of curled nanosheets.Electrochemical tests such as charge/discharge,cyclic voltammetry,cycle life and rate performance were carried out on the WS_(2) sample.As an anode material for lithium-ion batteries,hierarchical flowerlike WS_(2) microspheres show excellent electrochemical performance.At a current density of100 mA·g^(-1),a high specific capacity of 647.8 mA·h·g^(-1) was achieved after 120 discharge/charge cycles.The excellent electrochemical performance of WS_(2) as an anode material for lithium-ion batteries can be attributed to its special 3D hierarchical structure.展开更多
CO_(2) flooding is a vital development method for enhanced oil recovery in low-permeability reservoirs,However,micro-fractures are developed in low-permeability reservoirs,which are essential oil flow channels but can...CO_(2) flooding is a vital development method for enhanced oil recovery in low-permeability reservoirs,However,micro-fractures are developed in low-permeability reservoirs,which are essential oil flow channels but can also cause severe CO_(2) gas channeling problems.Therefore,anti-gas channeling is a necessary measure to improve the effect of CO_(2) flooding.The kind of anti-gas channeling refers to the plugging of fractures in the deep formation to prevent CO_(2) gas channeling,which is different from the wellbore leakage.Polymer microspheres have the characteristics of controllable deep plugging,which can achieve the profile control of low-permeability fractured reservoirs.In acidic environments with supercritical CO_(2),traditional polymer microspheres have poor expandability and plugging properties.Based on previous work,a systematic evaluation of the expansion performance,dispersion rheological properties,stability,deep migration,anti-CO_(2) channeling and enhanced oil recovery ability of a novel acid-resistant polymer microsphere(DCNPM-A)was carried out under CQ oilifield conditions(salinity of85,000 mg/L,80℃,pH=3).The results show that the DCNPM-A microsphere had a better expansion performance than the traditional microsphere,with a swelling rate of 13.5.The microsphere dispersion with a concentration of 0.1%-0.5%had the advantages of low viscosity,high dispersion and good injectability in the low permeability fractured core.In the acidic environment of supercritical CO_(2),DCNPM-A microspheres showed excellent stability and could maintain strength for over 60 d with less loss.In core experiments,DCNPM-A microspheres exhibited delayed swelling characteristics and could effectively plug deep formations.With a plugging rate of 95%,the subsequent enhanced oil recovery of CO_(2) flooding could reach 21.03%.The experimental results can provide a theoretical basis for anti-CO_(2)channeling and enhanced oil recovery in low-permeability fractured reservoirs.展开更多
TiO2@Ni(OH)2 core-shell microspheres were synthesized by a facile strategy to obtain a perfect 3D flower-like nanostructure with well-arranged Ni(OH)2 nanoflakes on the surfaces of TiO2 microspheres;this arrangement l...TiO2@Ni(OH)2 core-shell microspheres were synthesized by a facile strategy to obtain a perfect 3D flower-like nanostructure with well-arranged Ni(OH)2 nanoflakes on the surfaces of TiO2 microspheres;this arrangement led to a six-fold enhancement in photocatalytic hydrogen evolution. The unique p-n type heterostructure not only promotes the separation and transfer of photogenerated charge carriers significantly, but also offers more active sites for photocatalytic hydrogen production. A photocatalytic mechanism is proposed based on the results of electrochemical measurements and X-ray photoelectron spectroscopy.展开更多
The TiO2 microspheres were deposited on the glass substrates under certain conditions via hydro-thermal reaction using 0.15 mol·L?1 TiCl3 saturated NaCl aqueous solution adding urea as an additive. The TiO2 is ch...The TiO2 microspheres were deposited on the glass substrates under certain conditions via hydro-thermal reaction using 0.15 mol·L?1 TiCl3 saturated NaCl aqueous solution adding urea as an additive. The TiO2 is characterized rutile by results of SEM,TEM and XRD techniques,the TiO2 microspheres are large scale assembled from TiO2 nanorods. The affections on the products by the factors of the con-tents of urea being an additive(the key techniques) ,the reaction temperature,the reaction time and the concentration of TiCl3 were studied. The optimum condition was found,and the mechanism of reac-tions was discussed also.展开更多
TiO2hollow microspheres(TiO2‐HMSs)have attracted much attention because of their high photoreactivity,low density,and good permeability.However,anatase TiO2‐HMSs have poor thermal stability.In this study,surface‐fl...TiO2hollow microspheres(TiO2‐HMSs)have attracted much attention because of their high photoreactivity,low density,and good permeability.However,anatase TiO2‐HMSs have poor thermal stability.In this study,surface‐fluorinated TiO2‐HMSs were assembled from hollow nanoparticles by the hydrothermal reaction of the mixed Ti(SO4)2–NH4HF–H2O2solution at180°C.The effect of the calcination temperature on the structure and photoreactivity of the TiO2‐HMSs was systematically investigated,which was evaluated by photocatalytic oxidation of acetone in air under ultraviolet irradiation.We found that after calcination at300°C,the photoreactivity of the TiO2‐HMSs decreases from1.39×10?3min?1(TiO2‐HMS precursor)to0.82×10?3min?1because of removal of surface‐adsorbed fluoride ions.With increasing calcination temperature from300to900°C,the building blocks of the TiO2‐HMSs evolve from truncated bipyramidal shaped hollow nanoparticles to round solid nanoparticles,and the photoreactivity of the TiO2‐HMSs steady increases from0.82×10?3to2.09×10?3min?1because of enhanced crystallization.Further increasing the calcination temperature to1000and1100°C results in a decrease of the photoreactivity,which is ascribed to a sharp decrease of the Brunauer–Emmett–Teller surface area and the beginning of the anatase–rutile phase transformation at1100°C.The effect of surface‐adsorbed fluoride ions on the thermal stability of the TiO2‐HMSs is also discussed.展开更多
Highly homogeneous, well dispersed SiO_2@Au@TiO_2(SAT) microspheres decorated with Au nanoparticles(AuNPs) were prepared and incorporated into the photoanode with an optimized concentration gradientascent. The effects...Highly homogeneous, well dispersed SiO_2@Au@TiO_2(SAT) microspheres decorated with Au nanoparticles(AuNPs) were prepared and incorporated into the photoanode with an optimized concentration gradientascent. The effects of SAT microspheres and the gradient-ascent architecture on the light absorption and the photoelectric conversion efficiency(PCE) of the dye-sensitized solar cells(DSSCs) were investigated.Studies indicate that the introduction of SAT microspheres and the gradient-ascent architecture in the photoanode significantly enhance the light scattering and harvesting capability of the photoanode. The DSSC with the optimized SAT gradient-ascent photoanode has the maximum short circuit current density(J_(sc)) of 17.7 mA cm^(-2) and PCE of 7.75%, remarkably higher than those of the conventional DSSC by 23.7%and 28.0%, respectively. This significantly enhancement of the performance of the DSSC can be attributed to the excellent light reflection/scattering of SAT, the localized surface plasma resonance(LSPR) effect of AuNPs within the microspheres, and the gradient-ascent architecture of SAT microspheres inside the photoanode. This study demonstrates that the tri-synergies of the scattering of SAT microspheres, the LSPR of AuNPs and the gradient-ascent architecture can effectively improve the PCE of DSSC.展开更多
Hierarchically structured TiO2 microspheres were prepared at a low temperature by combining a sol-gel process with a solvothermal route and characterized by scanning electron microscopy, transmission electron microsco...Hierarchically structured TiO2 microspheres were prepared at a low temperature by combining a sol-gel process with a solvothermal route and characterized by scanning electron microscopy, transmission electron microscopy and X-ray diffraction analysis. Results indicate that the phase structure of the as-prepared TiO2 products undergoes a transformation, which changes from amorphous microspheres with a smooth surface in the sol-gel process to hierarchical anatase ones consisting of nanocrystallines after the solvothermal treatment. The hierarchical anatase TiO2 microsphere shows large surface areas and good light scattering effects as the photoelectrodes for dye sensitized solar cells (DSSCs). DSSCs based on TiO2 microspheres exhibit an improvement power conversion efficiency of 6.58% and a high short current density of 13.83 mA/cm2 as compared to the commercial P25 based DSSCs with a power conversion efficiency of 4.94% and a high short current density of 10.28 mA/cm2.展开更多
Porous titanium dioxide(TiO_2) microspheres(MS) were prepared by a facile ultrasonic spray pyrolysis process with commercial colloidal silica as a sacrificial template. The morphology structure, Brunauer–Emmett–Tell...Porous titanium dioxide(TiO_2) microspheres(MS) were prepared by a facile ultrasonic spray pyrolysis process with commercial colloidal silica as a sacrificial template. The morphology structure, Brunauer–Emmett–Teller surface areas and pore size distribution of TiO_2 microspheres were studied by changing the content and diameter of the silica template in detail. These porous micro-sized MS are composed of anatase TiO_2 nanocrystallites of 5–10 nm and have unique bimodal mesopores. The largest specific surface area of 112.3 m^2/g has been achieved using 60 wt% 20 nm silica as a template.When used as photocatalysts, the best photocatalytic activity of the as-prepared porous MS is comparable to commercial P25 nanopowders. Moreover, the micro-size and tailored properties from the design that appear during the ultrasonic spray pyrolysis process give these porous MS a promising application in photocatalytic reaction.展开更多
化工、纺织印染与农药化肥等产业的蓬勃发展推动着人类社会的进步,但同时也给环境治理带来了巨大难题。目前,光催化降解局限于在特定波长下针对单一有机污染物进行降解,然而现实中的情况往往更复杂。因此,开发一种多功能光催化材料用于...化工、纺织印染与农药化肥等产业的蓬勃发展推动着人类社会的进步,但同时也给环境治理带来了巨大难题。目前,光催化降解局限于在特定波长下针对单一有机污染物进行降解,然而现实中的情况往往更复杂。因此,开发一种多功能光催化材料用于光催化降解不同有机污染物显得尤为重要。采用一步无模板溶剂热法合成了核壳结构的C-TiO_(2)复合材料前驱体,并在氩气气氛下煅烧得到高结晶度的C-TiO_(2)复合光催化材料。运用SEM、TEM、XRD和TG等表征手段对材料进行表征,结论如下:550℃煅烧时的样品为包含少量碳的高结晶度的锐钛矿相TiO 2,且550℃煅烧时的样品依然保持了完整的核壳结构。此外,C-TiO_(2)复合材料的比表面积高达85.69 m 2·g^(-1),平均孔径为16.4 nm以及孔体积为0.423 m 3·g^(-1)。在UV-Vis光照射下,C-TiO_(2)复合材料分别对罗丹明B(RhB)、亚甲基蓝(MB)和刚果红(CR)3种染料显示出增强的光催化降解活性。展开更多
基金Funded by the Jiangsu Province Industry-University-Research Cooperation Project (No.BY2018314)the Scientific Research Foundation of Jiangsu University of Technology (No.KYY18030)Jiangsu Overseas Visiting Scholar Program for University Prominent Young&Middle-aged Teachers and Presidents。
文摘3D hierarchical flowerlike WS_(2) microspheres were synthesized through a facile one-pot hydrothermal route.The as-synthesized samples were characterized by powder X-ray powder diffraction (XRD),energy-dispersive spectroscopy (EDS),scanning electron microscopy (SEM) and Raman.SEM images of the samples reveal that the hierarchical flowerlike WS_(2) microspheres with diameters of about 3-5μm are composed of a number of curled nanosheets.Electrochemical tests such as charge/discharge,cyclic voltammetry,cycle life and rate performance were carried out on the WS_(2) sample.As an anode material for lithium-ion batteries,hierarchical flowerlike WS_(2) microspheres show excellent electrochemical performance.At a current density of100 mA·g^(-1),a high specific capacity of 647.8 mA·h·g^(-1) was achieved after 120 discharge/charge cycles.The excellent electrochemical performance of WS_(2) as an anode material for lithium-ion batteries can be attributed to its special 3D hierarchical structure.
基金supported by the Fund of State Key Laboratory of Deep Oil and Gas,China University of Petroleum (East China) (SKLDOG2024-ZYRC-06)Key Program of National Natural Science Foundation of China (52130401)+2 种基金National Natural Science Foundation of China (52104055,52250410349)Major Science and Technology Project of China National Petroleum Corporation Limited (2021ZZ01-08)Shandong Provincial Natural Science Foundation,China (ZR2021ME171)。
文摘CO_(2) flooding is a vital development method for enhanced oil recovery in low-permeability reservoirs,However,micro-fractures are developed in low-permeability reservoirs,which are essential oil flow channels but can also cause severe CO_(2) gas channeling problems.Therefore,anti-gas channeling is a necessary measure to improve the effect of CO_(2) flooding.The kind of anti-gas channeling refers to the plugging of fractures in the deep formation to prevent CO_(2) gas channeling,which is different from the wellbore leakage.Polymer microspheres have the characteristics of controllable deep plugging,which can achieve the profile control of low-permeability fractured reservoirs.In acidic environments with supercritical CO_(2),traditional polymer microspheres have poor expandability and plugging properties.Based on previous work,a systematic evaluation of the expansion performance,dispersion rheological properties,stability,deep migration,anti-CO_(2) channeling and enhanced oil recovery ability of a novel acid-resistant polymer microsphere(DCNPM-A)was carried out under CQ oilifield conditions(salinity of85,000 mg/L,80℃,pH=3).The results show that the DCNPM-A microsphere had a better expansion performance than the traditional microsphere,with a swelling rate of 13.5.The microsphere dispersion with a concentration of 0.1%-0.5%had the advantages of low viscosity,high dispersion and good injectability in the low permeability fractured core.In the acidic environment of supercritical CO_(2),DCNPM-A microspheres showed excellent stability and could maintain strength for over 60 d with less loss.In core experiments,DCNPM-A microspheres exhibited delayed swelling characteristics and could effectively plug deep formations.With a plugging rate of 95%,the subsequent enhanced oil recovery of CO_(2) flooding could reach 21.03%.The experimental results can provide a theoretical basis for anti-CO_(2)channeling and enhanced oil recovery in low-permeability fractured reservoirs.
基金supported by the National Natural Science Foundation of China(21773031)the Natural Science Foundation of Fujian Province(2018J01686)the State Key Laboratory of Photocatalysis on Energy and Environment(SKLPEE-2017A01 and SKLPEE-2017B02)~~
文摘TiO2@Ni(OH)2 core-shell microspheres were synthesized by a facile strategy to obtain a perfect 3D flower-like nanostructure with well-arranged Ni(OH)2 nanoflakes on the surfaces of TiO2 microspheres;this arrangement led to a six-fold enhancement in photocatalytic hydrogen evolution. The unique p-n type heterostructure not only promotes the separation and transfer of photogenerated charge carriers significantly, but also offers more active sites for photocatalytic hydrogen production. A photocatalytic mechanism is proposed based on the results of electrochemical measurements and X-ray photoelectron spectroscopy.
基金Supported by the State Key Project for Fundamental Research (G199064504) the Special Research Foundation of the National Natural Science Foundation of China (Grant Nos. 90306011 and 20341003)
文摘The TiO2 microspheres were deposited on the glass substrates under certain conditions via hydro-thermal reaction using 0.15 mol·L?1 TiCl3 saturated NaCl aqueous solution adding urea as an additive. The TiO2 is characterized rutile by results of SEM,TEM and XRD techniques,the TiO2 microspheres are large scale assembled from TiO2 nanorods. The affections on the products by the factors of the con-tents of urea being an additive(the key techniques) ,the reaction temperature,the reaction time and the concentration of TiCl3 were studied. The optimum condition was found,and the mechanism of reac-tions was discussed also.
基金supported by the National Natural Science Foundation of China(51672312,21373275)the Science and Technology Program of Wuhan,China(2016010101010018,2015070504020220)the Dean’s Research Fund–04257 from the Education University of Hong Kong~~
文摘TiO2hollow microspheres(TiO2‐HMSs)have attracted much attention because of their high photoreactivity,low density,and good permeability.However,anatase TiO2‐HMSs have poor thermal stability.In this study,surface‐fluorinated TiO2‐HMSs were assembled from hollow nanoparticles by the hydrothermal reaction of the mixed Ti(SO4)2–NH4HF–H2O2solution at180°C.The effect of the calcination temperature on the structure and photoreactivity of the TiO2‐HMSs was systematically investigated,which was evaluated by photocatalytic oxidation of acetone in air under ultraviolet irradiation.We found that after calcination at300°C,the photoreactivity of the TiO2‐HMSs decreases from1.39×10?3min?1(TiO2‐HMS precursor)to0.82×10?3min?1because of removal of surface‐adsorbed fluoride ions.With increasing calcination temperature from300to900°C,the building blocks of the TiO2‐HMSs evolve from truncated bipyramidal shaped hollow nanoparticles to round solid nanoparticles,and the photoreactivity of the TiO2‐HMSs steady increases from0.82×10?3to2.09×10?3min?1because of enhanced crystallization.Further increasing the calcination temperature to1000and1100°C results in a decrease of the photoreactivity,which is ascribed to a sharp decrease of the Brunauer–Emmett–Teller surface area and the beginning of the anatase–rutile phase transformation at1100°C.The effect of surface‐adsorbed fluoride ions on the thermal stability of the TiO2‐HMSs is also discussed.
基金supported financially by the National Natural Science Foundation of China (Nos.51572102,11504101,11604089 and 11364018)
文摘Highly homogeneous, well dispersed SiO_2@Au@TiO_2(SAT) microspheres decorated with Au nanoparticles(AuNPs) were prepared and incorporated into the photoanode with an optimized concentration gradientascent. The effects of SAT microspheres and the gradient-ascent architecture on the light absorption and the photoelectric conversion efficiency(PCE) of the dye-sensitized solar cells(DSSCs) were investigated.Studies indicate that the introduction of SAT microspheres and the gradient-ascent architecture in the photoanode significantly enhance the light scattering and harvesting capability of the photoanode. The DSSC with the optimized SAT gradient-ascent photoanode has the maximum short circuit current density(J_(sc)) of 17.7 mA cm^(-2) and PCE of 7.75%, remarkably higher than those of the conventional DSSC by 23.7%and 28.0%, respectively. This significantly enhancement of the performance of the DSSC can be attributed to the excellent light reflection/scattering of SAT, the localized surface plasma resonance(LSPR) effect of AuNPs within the microspheres, and the gradient-ascent architecture of SAT microspheres inside the photoanode. This study demonstrates that the tri-synergies of the scattering of SAT microspheres, the LSPR of AuNPs and the gradient-ascent architecture can effectively improve the PCE of DSSC.
基金supported by the National High Technology Research and Development Program of China (Grant No. 2009AA03Z218)the National Natural Science Foundation of China (Grant No. 90923012)+1 种基金the Xi’an Applied Material Innovation Fund Project (Grant No. XA-AM-201006)the Fundamental Research Funds for the Central Universities of China
文摘Hierarchically structured TiO2 microspheres were prepared at a low temperature by combining a sol-gel process with a solvothermal route and characterized by scanning electron microscopy, transmission electron microscopy and X-ray diffraction analysis. Results indicate that the phase structure of the as-prepared TiO2 products undergoes a transformation, which changes from amorphous microspheres with a smooth surface in the sol-gel process to hierarchical anatase ones consisting of nanocrystallines after the solvothermal treatment. The hierarchical anatase TiO2 microsphere shows large surface areas and good light scattering effects as the photoelectrodes for dye sensitized solar cells (DSSCs). DSSCs based on TiO2 microspheres exhibit an improvement power conversion efficiency of 6.58% and a high short current density of 13.83 mA/cm2 as compared to the commercial P25 based DSSCs with a power conversion efficiency of 4.94% and a high short current density of 10.28 mA/cm2.
基金supported by the National Natural Science Foundation of China (Nos. 21236003, 21506125, 91534202 and 91534122)the Basic Research Program of Shanghai (14JC1490700)+1 种基金the China Postdoctoral Science Foundation (2014M561497 and 2014M560307)the Fundamental Research Funds for the Central Universities
文摘Porous titanium dioxide(TiO_2) microspheres(MS) were prepared by a facile ultrasonic spray pyrolysis process with commercial colloidal silica as a sacrificial template. The morphology structure, Brunauer–Emmett–Teller surface areas and pore size distribution of TiO_2 microspheres were studied by changing the content and diameter of the silica template in detail. These porous micro-sized MS are composed of anatase TiO_2 nanocrystallites of 5–10 nm and have unique bimodal mesopores. The largest specific surface area of 112.3 m^2/g has been achieved using 60 wt% 20 nm silica as a template.When used as photocatalysts, the best photocatalytic activity of the as-prepared porous MS is comparable to commercial P25 nanopowders. Moreover, the micro-size and tailored properties from the design that appear during the ultrasonic spray pyrolysis process give these porous MS a promising application in photocatalytic reaction.
文摘化工、纺织印染与农药化肥等产业的蓬勃发展推动着人类社会的进步,但同时也给环境治理带来了巨大难题。目前,光催化降解局限于在特定波长下针对单一有机污染物进行降解,然而现实中的情况往往更复杂。因此,开发一种多功能光催化材料用于光催化降解不同有机污染物显得尤为重要。采用一步无模板溶剂热法合成了核壳结构的C-TiO_(2)复合材料前驱体,并在氩气气氛下煅烧得到高结晶度的C-TiO_(2)复合光催化材料。运用SEM、TEM、XRD和TG等表征手段对材料进行表征,结论如下:550℃煅烧时的样品为包含少量碳的高结晶度的锐钛矿相TiO 2,且550℃煅烧时的样品依然保持了完整的核壳结构。此外,C-TiO_(2)复合材料的比表面积高达85.69 m 2·g^(-1),平均孔径为16.4 nm以及孔体积为0.423 m 3·g^(-1)。在UV-Vis光照射下,C-TiO_(2)复合材料分别对罗丹明B(RhB)、亚甲基蓝(MB)和刚果红(CR)3种染料显示出增强的光催化降解活性。