The nanoscale titania coated silica was prepared via a two-step precipitating approach, where the nanoscale silica nuclei were first prepared by passing an aqueous solution of sodium silicate through an ion-exchange r...The nanoscale titania coated silica was prepared via a two-step precipitating approach, where the nanoscale silica nuclei were first prepared by passing an aqueous solution of sodium silicate through an ion-exchange resin bed, then coated with the precipitation from hydrolyzed butyl titanate in an ethanol-hexane mixture at a low pH value in the presence of poly(ethylene oxide) polyamine salt(PPA) at a high temperature of 90 ℃. In the second-step precipitating process, the spontaneously precipitated titania shell on the silica nuclei was stabilized in the suspension solution with the help of the adsorption of PPA on the particles. A possible precipitating mechanism was suggested. Furthermore, the amorphous titania shell could undergo crystallization from the amorphous to the anatase structure at a high temperature of 650 ℃, and a further phase transition from the anatase to the rutile structure in the different sintering processes at a rising temperature of 750 ℃.展开更多
基金Supported by the State Key L aboratory of Shanghai Institute of Ceram ics and State Key L aboratory of Surface Physicsin China
文摘The nanoscale titania coated silica was prepared via a two-step precipitating approach, where the nanoscale silica nuclei were first prepared by passing an aqueous solution of sodium silicate through an ion-exchange resin bed, then coated with the precipitation from hydrolyzed butyl titanate in an ethanol-hexane mixture at a low pH value in the presence of poly(ethylene oxide) polyamine salt(PPA) at a high temperature of 90 ℃. In the second-step precipitating process, the spontaneously precipitated titania shell on the silica nuclei was stabilized in the suspension solution with the help of the adsorption of PPA on the particles. A possible precipitating mechanism was suggested. Furthermore, the amorphous titania shell could undergo crystallization from the amorphous to the anatase structure at a high temperature of 650 ℃, and a further phase transition from the anatase to the rutile structure in the different sintering processes at a rising temperature of 750 ℃.