The relationship among microstructure,mechanical properties and texture of TA32 titanium alloy sheets during hot tensile deformation at 800℃was investigated.In the test,the original sheet exhibited relatively low flo...The relationship among microstructure,mechanical properties and texture of TA32 titanium alloy sheets during hot tensile deformation at 800℃was investigated.In the test,the original sheet exhibited relatively low flow stress and sound plasticity,and increasing the heat treatment temperature resulted in an increased ultimate tensile strength(UTS)and a decreased elongation(EL).The deformation mechanism of TA32 alloy was dominated by high angle grain boundaries sliding and coordinated by dislocation motion.The coarsening of grains and the annihilation of dislocations in heat-treated specimens weakened the deformation ability of material,which led to the increase in flow stress.Based on the high-temperature creep equation,the quantitative relationship between microstructure and flow stress was established.The grain size exponent andαphase strength constant of TA32 alloy were calculated to be 1.57 and 549.58 MPa,respectively.The flow stress was accurately predicted by combining with the corresponding phase volume fraction and grain size.Besides,the deformation behavior of TA32 alloy was also dependent on the orientation of predominantαphase,and the main slip mode was the activation of prismaticslip system.The decrease of near prism-oriented texture in heat-treated specimens resulted in the enhancement of strength of the material.展开更多
This paper reports research into the microstructures and properties of electron beam welding （EBW） joints of a Ti alloy sheet. To control the TC4 sheet joint formation during electron beam welding is not an easy tas...This paper reports research into the microstructures and properties of electron beam welding （EBW） joints of a Ti alloy sheet. To control the TC4 sheet joint formation during electron beam welding is not an easy task. However, the electron beam current has a significant influence on joint formation and a good appearance of a T-joint can be obtained by increasing the heat input and using the electron beam scan method. It was found that all acicular martensite in the fusion zone （FZ） consisted primarily of α＇ phase titanium, with some β phase present. Grain coarsening occurred in the heat-affected zone （HAZ） due to transformation of the β phase. Butt joints possessed high strength, hardness of the fusion zone, and the heataffected zone of these joints performed better than that of the parent metal. The highest shear strength of T-joint was 615 MPa and the fracture mechanism was a gliding fracture.展开更多
基金Project(51805256)supported by the National Natural Science Foundation of China。
文摘The relationship among microstructure,mechanical properties and texture of TA32 titanium alloy sheets during hot tensile deformation at 800℃was investigated.In the test,the original sheet exhibited relatively low flow stress and sound plasticity,and increasing the heat treatment temperature resulted in an increased ultimate tensile strength(UTS)and a decreased elongation(EL).The deformation mechanism of TA32 alloy was dominated by high angle grain boundaries sliding and coordinated by dislocation motion.The coarsening of grains and the annihilation of dislocations in heat-treated specimens weakened the deformation ability of material,which led to the increase in flow stress.Based on the high-temperature creep equation,the quantitative relationship between microstructure and flow stress was established.The grain size exponent andαphase strength constant of TA32 alloy were calculated to be 1.57 and 549.58 MPa,respectively.The flow stress was accurately predicted by combining with the corresponding phase volume fraction and grain size.Besides,the deformation behavior of TA32 alloy was also dependent on the orientation of predominantαphase,and the main slip mode was the activation of prismaticslip system.The decrease of near prism-oriented texture in heat-treated specimens resulted in the enhancement of strength of the material.
基金Supported by National Basic Research Program （2010CB731704） and National Natural Science Foundation of China（No. 51075089）.
文摘This paper reports research into the microstructures and properties of electron beam welding （EBW） joints of a Ti alloy sheet. To control the TC4 sheet joint formation during electron beam welding is not an easy task. However, the electron beam current has a significant influence on joint formation and a good appearance of a T-joint can be obtained by increasing the heat input and using the electron beam scan method. It was found that all acicular martensite in the fusion zone （FZ） consisted primarily of α＇ phase titanium, with some β phase present. Grain coarsening occurred in the heat-affected zone （HAZ） due to transformation of the β phase. Butt joints possessed high strength, hardness of the fusion zone, and the heataffected zone of these joints performed better than that of the parent metal. The highest shear strength of T-joint was 615 MPa and the fracture mechanism was a gliding fracture.