Nano-sized cerium-titanium pyrophosphates Ce1-xTixP2O7 （with x = 0, 0.2, 0.5, 0.7, 0.9, and 1.0） were obtained by grinding a mixture of Ce（SO4）2·4H2O, Ti（SO4）2, and Na4P2O7·10H2O in the presence of sur...Nano-sized cerium-titanium pyrophosphates Ce1-xTixP2O7 （with x = 0, 0.2, 0.5, 0.7, 0.9, and 1.0） were obtained by grinding a mixture of Ce（SO4）2·4H2O, Ti（SO4）2, and Na4P2O7·10H2O in the presence of surfactant PEG-400 at room temperature, washing the mixture with water to remove soluble inorganic salts, and drying at 100℃. The products and their calcined samples were characterized using ultraviolet-visible spectroscopy （UV-vis）, thermogravimetry and differential thermal analyses （TG/DTA）, X-ray powder diffraction （XRD）, and transmission electron microscopy （TEM）. The results show that nano-sized Ce1-xTixP2O7 behave as an excellent UV-shielding material. Thereinto, the CeP2O7 has the most excellent UV-shielding effect, and the amorphous state of Ce0.8Ti0.2P2O7 can keep at a higher temperature than CeP2O7. Therefore, the stabilization of the amorphous state of the cerium pyrophosphates was carded out by doping titanium. This stabilization is a significant improvement, which enables to apply these amorphous pyrophosphates not only to cosmetics and paints, but also plastics and films.展开更多
基金supported by the Natural Sci-ence Foundation of Guangxi Province, China (No. 0640009)
文摘Nano-sized cerium-titanium pyrophosphates Ce1-xTixP2O7 （with x = 0, 0.2, 0.5, 0.7, 0.9, and 1.0） were obtained by grinding a mixture of Ce（SO4）2·4H2O, Ti（SO4）2, and Na4P2O7·10H2O in the presence of surfactant PEG-400 at room temperature, washing the mixture with water to remove soluble inorganic salts, and drying at 100℃. The products and their calcined samples were characterized using ultraviolet-visible spectroscopy （UV-vis）, thermogravimetry and differential thermal analyses （TG/DTA）, X-ray powder diffraction （XRD）, and transmission electron microscopy （TEM）. The results show that nano-sized Ce1-xTixP2O7 behave as an excellent UV-shielding material. Thereinto, the CeP2O7 has the most excellent UV-shielding effect, and the amorphous state of Ce0.8Ti0.2P2O7 can keep at a higher temperature than CeP2O7. Therefore, the stabilization of the amorphous state of the cerium pyrophosphates was carded out by doping titanium. This stabilization is a significant improvement, which enables to apply these amorphous pyrophosphates not only to cosmetics and paints, but also plastics and films.