Microstructures of brazing zone between titanium alloy and stainless steel using various filler metals

Titanium alloy (Ti-Al-V alloy) substrate was brazed with stainless steel (STS304) using filler metal.At an optimized brazing condition,various filler metals were used.Microstructures were observed at each condition.Filler metals were titanium based 40Ti-20Zr-20Cu-20Ni,silver based Ag 5Pd,and nickel based Ni-7Cr-3.1B-4.5Si-3Fe-0.06C (BNi2) and Ni-14Cr-10P-0.06C (BNi7).To select a good filler metal for brazing process,wetting test was performed at 880-1050 °C.It was not brazed using silver based filler metals,but at the conditions using titanium and nickel based filler metals had brazed zone between titanium alloy and stainless steel.However,titanium alloy was eroded during brazing using titanium based filler metals.Nickel based filler metal has a good brazed zone between titanium alloy and stainless steel among the filler metals.

Effect of nitrogen content on the microstructure and mechanical properties of titanium-bearing nonquenched and tempered steel after hot forging

The microstructure and mechanical properties of titanium(Ti)-bearing medium-carbon nonquenched and tempered steel with different nitrogen content before and after hot forging were investigated through smelting,forging,and laboratory tests.The results show that the grain size of nonquenched and tempered steel was gradually refined,and the ferrite content gradually increased with an increase in nitrogen content.The grain size of the material with low nitrogen content increased abnormally,and its impact properties significantly decreased after hot forging.The grain size of nonquenched and tempered steel with higher nitrogen content was slightly larger than that before forging,and the tensile and yield strength increased,but the impact toughness was not significantly reduced.The Ti-bearing nonquenched and tempered steel showed better strength and toughness after hot forging with the addition of 0.010%0.015%nitrogen.

Zr-Ti-Ni-Cu Amorphous Brazing Fillers Applied to Brazing Titanium TA2 and Q235 Steel

Ti-Zr-Cu-Ni amorphous filler with good performance is suitable for joining TC and TB titanium alloy, but its melting temperature is higher than 882.5°C, the α→β phase transition temperature of TA2, which makes the ductility of TA2 fall and the microstructure of the joint coarse. In this paper, Ti-Zr-Cu-Ni amorphous filler was redesigned and optimized by using orthogonal experiment to obtain three easy-to-use Zr-Ti-Ni-Cu amorphous fillers with low melting points and good plasticity. The fast cooling equipment was used to fabricate the brazing filler foils to implement the braze welding of TA2 and Q235 with high frequency inductance. The results indicate that all the brazing foils are amorphous structure with lower melting temperature, for example, Zr52Ti22Ni18Cu8 filler’s is 538°C. The technical parameters in brazing welding are: welding temperature T = 800°C;heating electric current I =25 A;heating time t = 15 s and holding time t = 15 s, in the case of these conditions, the jointing head shear strength of TA2/Zr52Ti24Ni13Cu11/Q235 is 139 MPa. Fracture is mainly located in the brazing seam. The white brittle intermetallic TiFe, TiFe2 and enhancement TiC spread in the center zone of brazing seam.

Interfacial structure and mechanical properties of hot-roll bonded joints between titanium alloy and stainless steel using niobium interlayer

The hot-roll bonding was carried out in vacuum between titanium alloy and stainless steel using niobium interlayer. The interfacial structure and mechanical properties were analyzed. The results show that the plasticity of bonded joint is improved significantly. When the bonding temperature is 800 °C or 900 °C, there is not intermetallic layer at the interface between stainless steel and niobium. When the bonding temperature is 1000 °C or 1050 °C, Fe-Nb intermetallic layer forms at the interface. When the bonding temperature is 1050 °C, cracking occurs between stainless steel and intermetallic layer. The maximum strength of -417.5 MPa is obtained at the bonding temperature of 900 °C, the reduction of 25% and the rolling speed of 38 mm/s, and the tensile specimen fractures in the niobium interlayer with plastic fracture characteristics. When the hot-roll bonded transition joints were TIG welded with titanium alloy and stainless steel respectively, the tensile strength of the transition joints after TIG welding is -410.3 MPa, and the specimen fractures in the niobium interlayer.

Contact reactive brazing of Al alloy/Cu/stainless steel joints and dissolution behaviors of interlayer

Contact reactive brazing of 6063 Al alloy and 1Cr18Ni9Ti stainless steel was researched by using Cu as interlayer. Effect of brazing time on microstructure of the joints, as well as the dissolution behaviors of Cu interlayer was analyzed. The results show that the product of reaction zone near 1Cr18Ni9Ti is composed of Fe2Al5, FeAl3 intermetallic compound （IMC）, and Cu-Al IMC; the near by area is composed of Al-Cu eutectic structure with Al （Cu） solid solution. With increasing the brazing time, the thickness of IMC layer at the interface increases, while the width of Al-Cu eutectic structure with Al（Cu） solution decreases. Calculation shows the dissolution rate of Cu interlayer is very fast. The complete dissolution time is about 0.47 s for Cu interlayer with 10 μm in thickness used in this study.

Microstructural characteristics of joint region during diffusion-brazing of magnesium alloy and stainless steel using pure copper interlayer

A novel joining method,double-stage diffusion-brazing of an AZ31 magnesium alloy and a 304L austenitic stainless steel,was carried out using a pure copper interlayer.The solid-state diffusion bonding of 304L to copper was conducted at 850 ℃ for 20 min followed by brazing to AZ31 at 520 ℃ and 495 ℃ for various time.Microstructural characteristics of the diffusion-brazed joints were investigated in detail.A defect free interface of Fe-Cu diffusion area appeared between the Cu alloy and the 304L steel.Cu-Mg reaction products were formed between AZ31 and Cu alloys.A layered structure including AZ31/Cu-Mg compounds/Cu/Fe-Cu diffusion layer/304L was present in the joint.With time prolonging,the reduction in the width of Cu layer was balanced by the increase in the width of Cu-Mg compounds zone.Microhardness peaks in the zone between AZ31 and Cu layer were attributed to the formation of Mg-Cu compounds in this zone.

Effect of intermetallic compounds on heat resistance of hot roll bonded titanium alloy-stainless steel transition joint

The effect of intermetallic compounds on the heat resistance of transition joint was investigated. The experiment of post-weld heat treatment for the hot roll bonded titanium alloy-stainless steel joint using nickels interlayer was carried out, and the interface microstructure evolution due to heat treatment was presented. There was not found significant interdiffusion at stainless steel/nickel interface, when the specimens were heat treated in the temperature range of 600-800 °C for 10 and 30 min, while micro-cracks occurred at the stainless steel/nickel interface heat treated at 700 °C for 30 min. The thickness of intermetallic layers at nickel/titanium alloy interface increased at 600 °C, and micro-cracks occurred at 700 and 800 °C. The micro-cracks occurred between intermetallic layers or between intermetallic layer and nickel interlayer as well. The tensile strength of the transition joint decreased with the increase of heat treatment temperature or holding time.

Influences of different filler metals on electron beam welding of titanium alloy to stainless steel

Electron beam welding experiments of titanium alloy to stainless steel were carried out with different filler metals, such as Ni, V, and Cu. Microstructures of the joints were examined by optical microscopy, scanning electron microscopy and X-ray diffraction analysis. Mechanical properties of the joints were evaluated according to tensile strength and microhardness. As a result, influences of filler metals on microstructures and mechanical properties of electron beam welded titanium-stainless steel joints were discussed. The results showed that all the filler metals were helpful to restrain the Ti-Fe intermetallics. The welds with different filler metals were all characterized by solid solution and interfacial intermetallics. For each type of the filler metal, the type of solid solution and interfacial intermetallics depended on the metallurgical reactions between the filler metals and base metals. The interfacial intermetallics were Fe2Ti＋Ni3Ti＋NiTi2, TiFe, and Cu2Ti＋CuTi＋CuTi2 in the joints welded with Ni, V, and Cu filler metals, respectively. The tensile strengths of the joints were dependent on the hardness of the interfacial intermetallics. The joint welded with Ag filler metal had the highest tensile strength, which is about 310 MPa.

Delayed Fracture Behavior of CrMo-Type High Strength Steel Containing Titanium

The delayed fracture behaviors of CrMo-type high strength steels containing different amount of titanium(0to 0.10%)were studied.The steels were quenched at 880℃ and tempered from 400℃ to 650℃,and a wide range of tensile strength was obtained.The sustained load tensile test was carried out by using notched tensile specimens in Walpole solution.The experimental results showed that with higher strength,the Ti-microalloyed steels show higher resistance to delayed fracture compared with non-microalloyed steel due to titanium beneficial role and microstructure changes.The undissolved TiC is uniformly distributed as strong hydrogen traps,retarding or preventing the diffusion and accumulation of hydrogen to lower-interaction energy sites,such as prior austenite and martensite lath boundaries in stress concentration area.Meanwhile,the grain refining effect of titanium is also an important factor to improve the delayed fracture resistance of Ti-microalloyed steels.The characteristics of delayed fracture remain nearly the same with titanium addition.

Effect of interface morphology on the mechanical properties of titanium clad steel plates

Interface morphology has important influence on the bond quality of titanium clad steel plates. The mechanical properties of titanium clad steel plates with wavy and straight interfaces were investigated by tensile-shear tests and bending tests. The interface morphology of the plates was examined by optical microscopy （OM） and scanning electron microscopy （SEM）. The experimental results show that the shear strength of a wavy interface is higher than that of a straight interface. A wavy interface is the guarantee for obtaining high shear strength to provide a greater shear resistance. During the maerobending process, cracks appear in the swirl of the wave tip and ferrotitanium intermetallies. For in-situ observing the bending process by SEM, the wave tip of a wavy interface and the massive ferrotitartium intermetallies of a straight interface are places where cracks initiate and propagate. The results are the same as those observed in the macrobending process. Became of high hardness, the wave tip and the massive ferrotitanium intermetallies are hard in terms of compatible deformation.

Microstructure,properties and first principles calculation of titanium alloy/steel by Nd: YAG laser self-fluxing welding

The experiment of Nd： YAG pulsed laser self-fluxing welding for 304 stainless steel/Ti6Al4V titanium alloy dissimilar metal was carried out. The microstructure properties of welded joint were analyzed by SEM, EDS and XRD. The equilibrium lattice constants, enthalpies of formation, cohesive energies, mechanical properties, Debye temperatures and valence electron structures of Ti-Fe intermetallic compounds （IMCs） were calculated by the first principle pseudopotential plane wave method based on density functional theory （DFT）. According to the thermodynamic data of Ti-Fe-Cr compounds, the Gibbs free energy per mole of compound at different temperatures was calculated and their thermal stability was compared. The results show that there are no macroscopic cracks in the welded joints, and the IMCs distributed evenly along the welding interface exhibits 3 distinct layers of microstructure with different colors. The welds interface generates IMCs of TiFe, TiFe 2 and a small amount of Ti 5Cr 7Fe 17 IMCs. Ti-Fe IMCs with high thermodynamic stability and easy alloying formation. The results of Gibbs free energies show that the sequence of precipitates in the interface is Ti 5Cr 7Fe 17 , TiFe 2 and TiFe in high temperature during the metallurgical reaction. The G/B values of Ti-Fe IMCs are greater than the critical value of 0.5, indicating that it is an intrinsic brittleness.

Effects of aluminum and titanium on the microstructure of ODS steels fabricated by hot pressing

Three oxide-dispersion-strengthened(ODS)steels with compositions of Fe-14Cr-2W-0.2V-0.07Ta-0.3Y_2O_3(wt%,so as the follows)(14Y),Fe-14Cr-2W-0.2V-0.07Ta-1Al-0.3Y_2O_3(14YAl),and Fe-14Cr-2W-0.2V-0.07Ta-0.3Ti-0.3 Y_2O_3(14YTi)were fabricated by hot pressing.Transmission electron microscopy(TEM)was used to characterize the microstructures and nanoparticles of these ODS steels.According to the TEM results,14Y,14YAl,and 14YTi ODS steels present similar bimodal structures containing both large and small grains.The addition of Al or Ti has no obvious effect on the microstructure of the steels.The spatial and size distribution of the nanoparticles was also analyzed.The results indicate that the average size of nanoparticles in the 14YTi ODS steel is smaller than that in the 14YAl ODS steel.Nanoparticles such as Y_2O_3,Y_3Al_5O_(12) and YAlO_3,and Y_2Ti_2O_7 were identified in the 14Y,14YAl,and 14YTiODS steels,respectively.

Electron beam welding of Ti-15-3 titanium alloy to 304 stainless steel with copper interlayer sheet

Electron beam welding of Ti-15-3 titanium alloy to 304 stainless steel with a copper sheet as interlayer was carried out.Microstructures of the joint were studied by optical microscopy(OM),scanning electron microscopy(SEM) and X-ray diffractometry(XRD).In addition,the mechanical properties of the joint were evaluated by tensile test and the microhardness was measured.These two alloys were successfully welded by adding copper transition layer into the weld.Solid solution with a certain thickness was located at the interfaces between weld and base metal in both sides.Regions inside the weld and near the stainless steel were characterized by solid solution of copper with TiFe2 intermetallics dispersedly distributed in it.While weld near titanium alloy contained Ti-Cu and Ti-Fe-Cu intermetallics layer,in which the hardness of weld came to the highest value.Brittle fracture occurred in the intermetallics layer when the joint was stretched.

Comparison of explosive welding of pure titanium/SUS 304 austenitic stainless steel and pure titanium/SUS 821L1 duplex stainless steel

Pure commercial titanium was welded with two types of stainless steel,namely SUS 304 austenitic stainless steel and SUS 821L1 duplex stainless steel.The wavy interface of SUS 821L1 was smaller than that of SUS 304.The vortex zone was observed from both longitudinal and transverse directions,and its composition was analyzed.The interface of Ti/SUS 821L11 was able to bear 401−431 MPa shear load while that of Ti/SUS 304 could withstand 352−387 MPa.The weldability window was used to analyze experimental phenomenon.Furthermore,the smoothed particle hydrodynamics(SPH)numerical simulation method was used to simulate the wavy interface.The trend of wavelength and amplitude change with strength and the stand-offs was consistent with the experimental results.

Titanium microalloying of steel:A review of its effects on processing,microstructure and mechanical properties

Carbon neutrality of the steel industry requires the development of high-strength steel.The mechanical properties of low-alloy steel can be considerably improved at a low cost by adding a small amount of titanium(Ti)element,namely Ti microalloying,whose performance is related to Ti-contained second phase particles including inclusions and precipitates.By proper controlling the precipitation behaviors of these particles during different stages of steel manufacture,fine-grained microstructure and strong precipitation strengthening effects can be obtained in low-alloy steel.Thus,Ti microalloying can be widely applied to produce high strength steel,which can replace low strength steels heavily used in various areas currently.This article reviews the characteristics of the chemical and physical metallurgies of Ti microalloying and the effects of Ti microalloying on the phase formation,microstructural evolution,precipitation behavior of low-carbon steel during the steel making process,especially the thin slab casting and continuous rolling process and the mechanical properties of final steel products.Future development of Ti microalloying is also proposed to further promote the application of Ti microalloying technology in steel to meet the requirement of low-carbon economy.

Interfacial microstructure and property of resistance spot welding joints of titanium to stainless steel

Commercially pure titanium and stainless steel sheets were welded using the technique of resistance spot welding with an aluminum alloy insert. The interfacial microstructure of the joint was observed and analyzed using electron microscopy; the tensile shear strength was investigated. An approximate 160 nm thick layer of Al solid solution supersaturated with Ti was observed at the interface between titanium and aluminum alloy. The solid solution layer contained the precipitates TiAla. And an approximate 1. 5 μm thick serrate reaction layer was observed at the interface between stainless steel and aluminum alloy. The maximum tensile shear load of 5.38 kN was obtained from the joint welded at the welding current of 10 kA. The results reveal that the property of the joint between titanium and stainless steel can be improved by using an aluminum alloy insert.

Thermodynamics Behavior of Titanium for BOF Smelting Bearing Steel

When titanium element appears in bearing steel, it is very easy to create titanium nitride inclusion, which reduces the fatigue life of bearing steel. Based on the production data of bearing steel produced by BOF, it is found that the titanium takes its source in bearing steel; the factors-affecting titanium content, and the thermodynamics behavior of titanium under smelting condition were studied. The results show that the prime reasons of titanium content increment are the soluble aluminum content and the titanium oxide of slag. The comparison between the experimental data and theoretical ones shows that there is a big declination when the soluble aluminum content of steel is higher, which is caused by the nonequilibrium reaction of slag and steel. The apparent equilibrium distribution coefficient of titanium between slag and steel is Obtained by use of experimental data.

Improving pulsed laser weldability of duplex stainless steel to 5456 aluminum alloy via friction stir process reinforcing of aluminum by BNi-2 brazing alloy

Effects of laser pulse distance and reinforcing of 5456 aluminum alloy were investigated on laser weldability of Al alloy to duplex stainless steel (DSS) plates. The aluminum alloy plate was reinforced by nickel-base BNi-2 brazing powder via friction stir processing. The DSS plates were laser welded to the Al5456/BNi-2 composite and also to the Al5456 alloy plates. The welding zones were studied by scanning electron microscopy, X-ray diffractometry, micro-hardness and shear tests. The weld interface layer became thinner from 23 to 5 μm, as the laser pulse distance was increased from 0.2 to 0.5 mm. Reinforcing of the Al alloy modified the phases at interface layer from Al-Fe intermetallic compounds (IMCs) in the DSS/Al alloy weld, to Al-Ni-Fe IMCs in the DSS/Al composite one, since more nickel was injected in the weld pool by BNi-2 reinforcements. This led to a remarkable reduction in crack tendency of the welds and decreased the hardness of the interface layer from ~950 HV to ~600 HV. Shear strengths of the DSS/Al composite welds were significantly increased by ~150%, from 46 to 114 MPa, in comparison to the DSS/Al alloy ones.

Study on resistance spot brazing process and joint performance of pure aluminum 1060/galvanized steel

Resistance spot brazing was used to perform the lap test of pure aluminum 1060 and SGCC hot-dip galvanized steel plate,the joint interface structure was studied,and the mechanical properties of the joint were tested.The results show that the aluminum-silicon(Al-Si)alloy solder used in the test has good wetting,and an intermetallic compound with a double-layer structure and uneven thickness is produced at the welded joint interface after welding.The thickness is<10μm.The welding current is at 7.8 kA,the tensile shear load of the joint reaches a peak value of about 4.72 kN.Under the same process parameters,the tensile shear load of the resistance spot brazed joint is significantly higher than that of the spot welded joint.The joint fracture mostly occurs on the aluminum plate side,and mainly at the heat-affected zone and not at the welding point.It indicates that the quality of the spot brazed joint is good,but due to the local"unbrazed"defect on the aluminum side interface of the weld,tensile stress will occur at the weld interface and the stress effect on the intermetallic compound.It is easy to produce cracks.

Laser brazing with filler wire for galvanized steel sheets

The process properties and interface behavior of CO_2 laser brazing with automatic wire feed for galvanized steel sheets were investigated, in which the brazing filler metal was CuSi3 and no flux was used. As to the appearance quality of the brazing seams, the roles of the processing parameters, such as brazing speed, wire feeding rate, inclination and feeding direction of the wire, laser power, spot diameter and heating position, were assessed. The further investigation indicates that the behavior of the active elements Si, Mn and Zn are significantly influenced by energy input. At the interface, the microstructure of the base metal was composed of columnar crystals and the acicular α solid solution was found on the filler metal side.