Tl-based superconducting devices have been drawn much attention for their high transition temperature(T_c), which allow the high temperature superconductors(HTS) devices to operate at temperature near 100 K. The reali...Tl-based superconducting devices have been drawn much attention for their high transition temperature(T_c), which allow the high temperature superconductors(HTS) devices to operate at temperature near 100 K. The realization of Tlbased devices will promote the research and application of HTS devices. In this work, we present transport properties of Tl_(2) Ba_(2) CaCu_(2) O_(8)(Tl-2212) microbridges across a low-angle step on LaAlO_(3)(LAO) substrate. We experimentally demonstrate intrinsic Josephson effects(IJEs) in Tl-2212 films by tailoring the geometry, i.e., reducing the width of the microbridges. In the case of a 1 μm width microbridge, in addition to the observation of voltage branches and remarkable hysteresis on the current–voltage(I–V) characteristics, the temperature dependence of differential resistance shows a finite resistance above 60 K when the bias current is below the critical current. For comparison, the wider microbridges are also investigated, exhibiting a highly critical current but do not showing obvious IJEs.展开更多
A new improved two-step method in fabricating Tl2Ba2 CaCu2O8（Tl-2212） thin films is presented in this paper. In the first process of dc magnetron sputtering, the thallium content in the precursor film is largely inc...A new improved two-step method in fabricating Tl2Ba2 CaCu2O8（Tl-2212） thin films is presented in this paper. In the first process of dc magnetron sputtering, the thallium content in the precursor film is largely increased by adjusting the ratio of thallium in the sputtering targets. After the second annealing process in the absence of additional thallium pellets or powder source, high-quality Tl-2212 thin films can be obtained. The proper content of thallium in the precursor film provides a relatively stable atmosphere to guarantee the growth of Tl-2212 film. This method avoids the repeated production of the thallium pellets in the post-annealing process, the repeatability and controllability of the experiment are greatly improved. X-ray diffraction（XRD） scans show that all of the sharp peaks of the sample films can be assigned to the（00 l） peaks of Tl-2212 phase. The highest superconducting critical temperature（Tc） of the films is 105 K and the critical current density（Jc） can achieve 1.93 MA/cm2 in zero magnetic field at 77 K for a 600 nm film.展开更多
The rocking curve of Tl-2212 thin films in Fig.2 of our original paper[1]should be replaced with the following new one.Accordingly,in the fifth paragraph of Section 3 of the original paper,the statement“The full widt...The rocking curve of Tl-2212 thin films in Fig.2 of our original paper[1]should be replaced with the following new one.Accordingly,in the fifth paragraph of Section 3 of the original paper,the statement“The full width at half maximum(FWHM)of the(0012)peak of the Tl-2212 phase is about 0.24°”should be“The full width at half maximum(FWHM)of the(0012)peak of the Tl-2212 phase is about 0.42°”.展开更多
文摘Tl-based superconducting devices have been drawn much attention for their high transition temperature(T_c), which allow the high temperature superconductors(HTS) devices to operate at temperature near 100 K. The realization of Tlbased devices will promote the research and application of HTS devices. In this work, we present transport properties of Tl_(2) Ba_(2) CaCu_(2) O_(8)(Tl-2212) microbridges across a low-angle step on LaAlO_(3)(LAO) substrate. We experimentally demonstrate intrinsic Josephson effects(IJEs) in Tl-2212 films by tailoring the geometry, i.e., reducing the width of the microbridges. In the case of a 1 μm width microbridge, in addition to the observation of voltage branches and remarkable hysteresis on the current–voltage(I–V) characteristics, the temperature dependence of differential resistance shows a finite resistance above 60 K when the bias current is below the critical current. For comparison, the wider microbridges are also investigated, exhibiting a highly critical current but do not showing obvious IJEs.
基金Project supported by the National Natural Science Foundation of China(Grant No.51002081)the Fundamental Research Funds for the Central Universities,Chinathe Research Program of Application Foundation and Advanced Technology of Tianjin,China(Grant No.15JCQNJC01300)
文摘A new improved two-step method in fabricating Tl2Ba2 CaCu2O8（Tl-2212） thin films is presented in this paper. In the first process of dc magnetron sputtering, the thallium content in the precursor film is largely increased by adjusting the ratio of thallium in the sputtering targets. After the second annealing process in the absence of additional thallium pellets or powder source, high-quality Tl-2212 thin films can be obtained. The proper content of thallium in the precursor film provides a relatively stable atmosphere to guarantee the growth of Tl-2212 film. This method avoids the repeated production of the thallium pellets in the post-annealing process, the repeatability and controllability of the experiment are greatly improved. X-ray diffraction（XRD） scans show that all of the sharp peaks of the sample films can be assigned to the（00 l） peaks of Tl-2212 phase. The highest superconducting critical temperature（Tc） of the films is 105 K and the critical current density（Jc） can achieve 1.93 MA/cm2 in zero magnetic field at 77 K for a 600 nm film.
文摘The rocking curve of Tl-2212 thin films in Fig.2 of our original paper[1]should be replaced with the following new one.Accordingly,in the fifth paragraph of Section 3 of the original paper,the statement“The full width at half maximum(FWHM)of the(0012)peak of the Tl-2212 phase is about 0.24°”should be“The full width at half maximum(FWHM)of the(0012)peak of the Tl-2212 phase is about 0.42°”.