The Ho：YAP crystal is grown by the Czochralski technique. The room-temperature polarized absorption spectra of Ho：YAP crystal was measured on a c-cut sample with 1 at% holmium. According to the obtained Judd-Ofelt i...The Ho：YAP crystal is grown by the Czochralski technique. The room-temperature polarized absorption spectra of Ho：YAP crystal was measured on a c-cut sample with 1 at% holmium. According to the obtained Judd-Ofelt intensity parameters Ω2 = 1.42 × 10^-20cm^2, Ω4 = 2.92 ×10^-20 cm^2, and Ω6 =1.71 ×10^-20cm^2, this paper calculated the fluorescence lifetime to be 6 ms for ^5I7→^5Is transition, and the integrated emission cross section to be 2.24 × 10^-18 cm^2. It investigates the room-temperature Ho：YAP laser end-pumped by a 1.91-μm Tm：YLF laser. The maximum output power was 4.1 W when the incident 1.91-μm pump power was 14.4W. The slope efficiency is 40.8%, corresponding to an optical-to-optical conversion efficiency of 28.4%. The Ho：YAP output wavelength was centred at 2118 nm with full width at half maximum of about 0.8nm.展开更多
A narrow linewidth continuous wave Ho：YAP laser with two Fabry-Perot etalons pumped by a Tm：YLF laser is reported. The maximum output power reaches 8.3 W when the incident pump power is 15.8 W, with 52.5% optical-to...A narrow linewidth continuous wave Ho：YAP laser with two Fabry-Perot etalons pumped by a Tm：YLF laser is reported. The maximum output power reaches 8.3 W when the incident pump power is 15.8 W, with 52.5% optical-to- optical conversion efficiency and 62.6% slope efficiency. A stable laser output at 2118.1 nm is achieved, with a linewidth less than 0.4 nm （full width at half maximum）. The beam quality factor is M2- 1.25, measured by the traveling knife-edge method.展开更多
基金supported by the Program of Excellent Team in Harbin Institute of Technology of China
文摘The Ho：YAP crystal is grown by the Czochralski technique. The room-temperature polarized absorption spectra of Ho：YAP crystal was measured on a c-cut sample with 1 at% holmium. According to the obtained Judd-Ofelt intensity parameters Ω2 = 1.42 × 10^-20cm^2, Ω4 = 2.92 ×10^-20 cm^2, and Ω6 =1.71 ×10^-20cm^2, this paper calculated the fluorescence lifetime to be 6 ms for ^5I7→^5Is transition, and the integrated emission cross section to be 2.24 × 10^-18 cm^2. It investigates the room-temperature Ho：YAP laser end-pumped by a 1.91-μm Tm：YLF laser. The maximum output power was 4.1 W when the incident 1.91-μm pump power was 14.4W. The slope efficiency is 40.8%, corresponding to an optical-to-optical conversion efficiency of 28.4%. The Ho：YAP output wavelength was centred at 2118 nm with full width at half maximum of about 0.8nm.
基金Project supported by the Fundamental Research Funds for the Central Universities,China(Grant No.GK2030260112)
文摘A narrow linewidth continuous wave Ho：YAP laser with two Fabry-Perot etalons pumped by a Tm：YLF laser is reported. The maximum output power reaches 8.3 W when the incident pump power is 15.8 W, with 52.5% optical-to- optical conversion efficiency and 62.6% slope efficiency. A stable laser output at 2118.1 nm is achieved, with a linewidth less than 0.4 nm （full width at half maximum）. The beam quality factor is M2- 1.25, measured by the traveling knife-edge method.