Polyoxymethylene dimethyl ethers(OMEs)with physical properties similar to those of diesel has received significant attention as green additives for soot emission suppression.Herein,series of SO_(4)^(2-)/ZrO_(2)-TiO_(2...Polyoxymethylene dimethyl ethers(OMEs)with physical properties similar to those of diesel has received significant attention as green additives for soot emission suppression.Herein,series of SO_(4)^(2-)/ZrO_(2)-TiO_(2)catalysts were developed for OMEs production from dimethoxymethane(DMM)and1,3,5-trioxane through sequential formaldehyde monomer insertion into C-O bond of DMM.Not Lewis but Bronsted acid sites were identified to be active for the decomposition of 1,3,5-trioxane into formaldehyde unit,however,both of them are effective for the chain propagation of DMM via formaldehyde unit insertion into C-O bond.Kinetic studies indicated each chain growth step exhibited the same parameters and activation barrier on corresponding Bronsted and Lewis acid sites due to the same reaction mechanism and very similar chemical structure of OMEs.Also,the catalytic stability investigation suggested the deactivation behavior was derived from the carbon deposition,and the decay factor could be exponentially correlated with the amount of coke accumulation.展开更多
A series of SO 2- 4/TiO 2 SiO 2 catalysts with different mass fractions of SiO 2 were prepared by sol gel method. The effect of adding SiO 2 on the crystal structure, specific surface area, oxygen adsorption, and acid...A series of SO 2- 4/TiO 2 SiO 2 catalysts with different mass fractions of SiO 2 were prepared by sol gel method. The effect of adding SiO 2 on the crystal structure, specific surface area, oxygen adsorption, and acidity of SO 2- 4/TiO 2 catalyst and its photocatalytic property for degradation of bromomethane was studied. The results showed that the specific surface area and amount of oxygen adsorption of catalyst were increased by addition of SiO 2, leading to the obvious increase on photocatalytic activity of SO 2- 4/TiO 2 SiO 2 catalysts and mineralization ratio of bromomethane. Comparing with SO 2- 4/TiO 2, the acidic strength and anti moisture ability of SO 2- 4/TiO 2 SiO 2 catalyst were decreased.展开更多
The syntheis of diphenyletylane with xylol and styrene as reactants and solid superacid SO42-/TiO2 doped rare-earth metal ion La3+ as a catalyst was reported.The results showed that the optimal conditions were using 1...The syntheis of diphenyletylane with xylol and styrene as reactants and solid superacid SO42-/TiO2 doped rare-earth metal ion La3+ as a catalyst was reported.The results showed that the optimal conditions were using 1% of catalyst with the molar ration of xylol to styrene being 7.5:1,at temperature of 140℃ for 3 h;The yield of diphenylethylane under such conditions was about 97.5%.展开更多
基金the fund from the National Natural Science Foundation of China(22208349)the Innovation Academy for Green Manufacture(Chinese Academy of Sciences,IAGM2020C20)+1 种基金Shandong Provincial Natural Science Youth Fund(ZR2022QB244)Japan Society for the Promotion of Science(P20345)。
文摘Polyoxymethylene dimethyl ethers(OMEs)with physical properties similar to those of diesel has received significant attention as green additives for soot emission suppression.Herein,series of SO_(4)^(2-)/ZrO_(2)-TiO_(2)catalysts were developed for OMEs production from dimethoxymethane(DMM)and1,3,5-trioxane through sequential formaldehyde monomer insertion into C-O bond of DMM.Not Lewis but Bronsted acid sites were identified to be active for the decomposition of 1,3,5-trioxane into formaldehyde unit,however,both of them are effective for the chain propagation of DMM via formaldehyde unit insertion into C-O bond.Kinetic studies indicated each chain growth step exhibited the same parameters and activation barrier on corresponding Bronsted and Lewis acid sites due to the same reaction mechanism and very similar chemical structure of OMEs.Also,the catalytic stability investigation suggested the deactivation behavior was derived from the carbon deposition,and the decay factor could be exponentially correlated with the amount of coke accumulation.
文摘A series of SO 2- 4/TiO 2 SiO 2 catalysts with different mass fractions of SiO 2 were prepared by sol gel method. The effect of adding SiO 2 on the crystal structure, specific surface area, oxygen adsorption, and acidity of SO 2- 4/TiO 2 catalyst and its photocatalytic property for degradation of bromomethane was studied. The results showed that the specific surface area and amount of oxygen adsorption of catalyst were increased by addition of SiO 2, leading to the obvious increase on photocatalytic activity of SO 2- 4/TiO 2 SiO 2 catalysts and mineralization ratio of bromomethane. Comparing with SO 2- 4/TiO 2, the acidic strength and anti moisture ability of SO 2- 4/TiO 2 SiO 2 catalyst were decreased.
文摘The syntheis of diphenyletylane with xylol and styrene as reactants and solid superacid SO42-/TiO2 doped rare-earth metal ion La3+ as a catalyst was reported.The results showed that the optimal conditions were using 1% of catalyst with the molar ration of xylol to styrene being 7.5:1,at temperature of 140℃ for 3 h;The yield of diphenylethylane under such conditions was about 97.5%.