Progress and future prospects of application technology for tubing and casing 被引量:1
1
作者 LI Youfeng1)and SUN Decheng2)1)Tube & Pipe Technology Center,Research Institute,Baoshan Iron & Steel Co.,Ltd.,Shanghai 201900,China2)Drilling Engineering Co.,Ltd.,CNPC,Daqing 163453,Heilongjiang,China 《Baosteel Technical Research》 CAS 2010年第4期45-49,共5页
The main failure modes of tubing and casing in current service conditions are represented in this study.The progress of the tubing and casing application technology and the problems that should be focused on during ap... The main failure modes of tubing and casing in current service conditions are represented in this study.The progress of the tubing and casing application technology and the problems that should be focused on during application are introduced,with special attention paid to the reliability of the pipe string design and the connection sealing properties.The necessary work that should be undertaken in future research is also summarized. 展开更多
关键词 tubing and casing service condition failure mode pipe string design thread connection and sealing
下载PDF
Effect of abrasive blasting on the internal surface of L80-13Cr tubing and casing
2
作者 WANG Minghua ZHANG Chunxia 《Baosteel Technical Research》 CAS 2022年第1期36-41,共6页
In this study,two sandblasting textures,namely,quartz and high-chromium(Cr)stainless steel sands,were used for sandblasting of the internal surface L80-13Cr tubing and casing.The contrastive analysis on the properties... In this study,two sandblasting textures,namely,quartz and high-chromium(Cr)stainless steel sands,were used for sandblasting of the internal surface L80-13Cr tubing and casing.The contrastive analysis on the properties of the pipes before and after abrasive blasting was conducted,including the metallographic phase detection of the internal surface,simulating accelerated corrosion tests,and residual stress tests for the pipe after abrasive blasting.Based on the analysis results,it is explained why the API standard requires that no scale appears on the internal surface of L80-13Cr and iron contamination when internal sandblasting media are applied.The results show that abrasive blasting can effectively remove scales on the internal surface of L80-13Cr tubing and casing and improve corrosion resistance.The abrasive blasting process does not produce obvious residual stress on the internal surface of the tubing and casing.Also,the de-rusting effect of stainless sand is better than that of quartz sand,and the former does not produce iron contamination. 展开更多
关键词 L80-13Cr tubing and casing abrasive blasting CORROSION