Twinning-detwinning(TDT)behavior in a strongly basal-textured Mg-Li alloy during two-step compression(RD)-compression(ND)process was investigated using quasi-in-situ EBSD.TDT behavior and TDT variants selection were s...Twinning-detwinning(TDT)behavior in a strongly basal-textured Mg-Li alloy during two-step compression(RD)-compression(ND)process was investigated using quasi-in-situ EBSD.TDT behavior and TDT variants selection were statistically discussed with the loading path for the first time.Non-Schmid twinning behavior was observed in the first step compression,owing to the local stress fluctuations by neighboring twins;in contrast,Schmid’s law well predicted the detwinning variants selection.This asymmetrical TDT behavior was first investigated to date related with the strong basal texture and loading path.Besides,with the progress of compression,Schmid factors for twinning demonstrated a decreasing tendency;however,those for detwinning during the second step displayed an abnormally increasing trend,fundamentally stemming from prior twinning behavior.展开更多
Mg-RE(magnesium-rare earth)alloys exhibit pronounced in-plane anisotropy of mechanical response under quasi-static monotonic loading resulting from the RE texture,as extensively reported.In this work,an obvious in-pla...Mg-RE(magnesium-rare earth)alloys exhibit pronounced in-plane anisotropy of mechanical response under quasi-static monotonic loading resulting from the RE texture,as extensively reported.In this work,an obvious in-plane anisotropy of cyclic deformation behavior was observed in an extruded Mg-3Y alloy sheet during strain-controlled tension-compression low-cycle fatigue(LCF)at room temperature.The extrusion direction(ED)samples displayed better fatigue resistance with almost symmetrical hysteresis loops and longer fatigue life compared with the transverse direction(TD)samples.The influences of texture on the deformation modes,cracking modes,and mechanical behavior of Mg-Y alloy sheets under cyclic loading were studied quantitatively and statistically.The activation of various slip/twinning-detwinning systems was measured at desired fatigue stages via EBSD observations together with in-grain misorientation axes(IGMA)analysis.The results indicate that the activation of deformation modes in the TD sample was featured by the cyclic transition,i.e.,prismatic slip(at the tensile interval)→{10–12}tension twinning(at the compressive reversal)→detwinning+prismatic slip(at the re-tensile reversal).In the case of the ED sample,the cyclic deformation was dominated by the basal slip throughout the fatigue life.For cracking modes,intergranular cracking and persistent slip bands(PSB)cracking were the primary cracking modes in the ED sample while the TD sample showed a high tendency of{10–12}tension twinning cracking(TTW cracking).The underlying mechanisms influencing the activation of various slip/twinning-detwinning systems,as well as cracking modes and cyclic mechanical behavior,were discussed.展开更多
基金supported by the grant from the Natural Science Foundation of China(51871244)the Hunan Provincial Innovation Foundation for Postgraduate(CX20200172)the Fundamental Research Funds for the Central Universities of Central South University(1053320190103)。
文摘Twinning-detwinning(TDT)behavior in a strongly basal-textured Mg-Li alloy during two-step compression(RD)-compression(ND)process was investigated using quasi-in-situ EBSD.TDT behavior and TDT variants selection were statistically discussed with the loading path for the first time.Non-Schmid twinning behavior was observed in the first step compression,owing to the local stress fluctuations by neighboring twins;in contrast,Schmid’s law well predicted the detwinning variants selection.This asymmetrical TDT behavior was first investigated to date related with the strong basal texture and loading path.Besides,with the progress of compression,Schmid factors for twinning demonstrated a decreasing tendency;however,those for detwinning during the second step displayed an abnormally increasing trend,fundamentally stemming from prior twinning behavior.
基金co-supported by the National Natural Science Foundation of China(51575068 and 51501023)the State Key Research and Development Program of MOST,China(2016627 YFB0701204)+3 种基金Project No.2020CDJDPT001 supported by the Fundamental Research Funds for the Central UniversitiesChongqing Natural Science Foundation,No.cstc2018jcyj AX0364the“111” Project(B16007)by the Ministry of Education for financial supportChongqing Natural Science Foundation,No.cstc2021jcyjmsxmX0699。
文摘Mg-RE(magnesium-rare earth)alloys exhibit pronounced in-plane anisotropy of mechanical response under quasi-static monotonic loading resulting from the RE texture,as extensively reported.In this work,an obvious in-plane anisotropy of cyclic deformation behavior was observed in an extruded Mg-3Y alloy sheet during strain-controlled tension-compression low-cycle fatigue(LCF)at room temperature.The extrusion direction(ED)samples displayed better fatigue resistance with almost symmetrical hysteresis loops and longer fatigue life compared with the transverse direction(TD)samples.The influences of texture on the deformation modes,cracking modes,and mechanical behavior of Mg-Y alloy sheets under cyclic loading were studied quantitatively and statistically.The activation of various slip/twinning-detwinning systems was measured at desired fatigue stages via EBSD observations together with in-grain misorientation axes(IGMA)analysis.The results indicate that the activation of deformation modes in the TD sample was featured by the cyclic transition,i.e.,prismatic slip(at the tensile interval)→{10–12}tension twinning(at the compressive reversal)→detwinning+prismatic slip(at the re-tensile reversal).In the case of the ED sample,the cyclic deformation was dominated by the basal slip throughout the fatigue life.For cracking modes,intergranular cracking and persistent slip bands(PSB)cracking were the primary cracking modes in the ED sample while the TD sample showed a high tendency of{10–12}tension twinning cracking(TTW cracking).The underlying mechanisms influencing the activation of various slip/twinning-detwinning systems,as well as cracking modes and cyclic mechanical behavior,were discussed.