The poor fatigue properties and high rigidity of cement asphalt emulsion treated mis(CETM) have for a long time been problems restricting its further development making it impossible for C-ETMto be used as surface lay...The poor fatigue properties and high rigidity of cement asphalt emulsion treated mis(CETM) have for a long time been problems restricting its further development making it impossible for C-ETMto be used as surface layer materials. In this paper, a new kind of cement asphalt emulsion composite-rubberized asphalt emulsion modified Portland cement concrete (RACC) was proposed, which was formed by dispersing rubberized aSPhalt emulsion coated coarse aggregates into cement mortar matrix. In order to evaluate systematically the performance of RACC, laboratory tests with nearly one thousand SPecimen were conducted for resilient modulus, fatigue properties, ultimate ban and length,abrasion, temperature contraction, and dry shrinkage. The experimental results show that the problems existed in C-ETM have to a great extends been solved by RACc. To verify the field performance and inquire into paving technology, teSt road appearsatlsfactory it is concluded that when thed ape surface laycr of semi-rigid base course, RACC is more for surface layer material than both Portland cement concrete(PCC) and asphalt concrete(AC)展开更多
The influence of nanofiberwood on the properties of the fresh condition of cement based mortars is not known in detail,despite recent advances in nanocellulose technology and it is related composite materials.Nanofibe...The influence of nanofiberwood on the properties of the fresh condition of cement based mortars is not known in detail,despite recent advances in nanocellulose technology and it is related composite materials.Nanofiber wood from industrial waste,produced by high-pressure homogenization,was used as cement partial replacement for cement paste at a content ranging from 0%to 2%by weight of cement.The effect of the nanofiber wood content on the porosity,the compressive strength and the degree of hydration of the cement was investigated.Results have shown an improvement in the compressive strength by more than 50%with 1%of added fiber wood.The chemical modification of nanofibers wood by grafting of chains alkyls in their surfaces can reduce the quantity of water absorbed by the sample.The addition of an anionic additive(SDBS)in the water of mixing improves of more the surface of samples by minimizing the size of pores by emulsion effect,from where the absorption of water reduces.The degree of hydration of the cement has increased with the cellulose content containing nanofibrils.The analyze revealed that the presence of nanofiber wood favored the hydration of the cement by producing more calcium silicate gel and portlandite,probably the main reason for this improvement in compressive strength.展开更多
Nanofibrillated wood fiber was used as fillers in the partial cement matrix replacing the cement to a content of up to 2%by weight of cement.The nanofibrillated effect of wood fibers on porosity,thermal properties and...Nanofibrillated wood fiber was used as fillers in the partial cement matrix replacing the cement to a content of up to 2%by weight of cement.The nanofibrillated effect of wood fibers on porosity,thermal properties and compressive strength was studied.The results obtained showed an improvement in compressive strength of more than 40%with 1%by weight of wood fiber nanofibrillate.The addition of nanofibrillated wood fiber shows a good pore reduction,and the best result was obtained with emulsion of a mixture incorporating 1%by weight of wood fiber nanofibrillate in the presence of an anionic surfactant(SDBS).Thermal conductivity measurements and thermal expansion coefficient,compared to nanofibrillated wood fiber reinforced cement pastes,showed the reinforcing efficiency of cellulose fiber nanofibrillate.The degree of hydration of the cement increased with nanofibrillated wood fibers.This property has been confirmed by Fourier transform infrared spectroscopy.These analyzes revealed that the presence of nanofibrillated wood fibers generates and promotes the hydration of the cement,producing more portlandite and calcium silicate gel,which influences the compressive strength which gives a strong improvement.展开更多
Wood nanofibers from industrial waste have been used as polymeric material to reinforce the cement paste to a content of up to 2%by weight of cement.The effect of the wood nanofibre content on the porosity,the compres...Wood nanofibers from industrial waste have been used as polymeric material to reinforce the cement paste to a content of up to 2%by weight of cement.The effect of the wood nanofibre content on the porosity,the compressive strength and the degree of hydration of the cement was studied.The results showed an improvement in compressive strength of over 50%with 1%of added fiberwood.Chemical modification of nanofiber wood by grafting alkyl chains to their surface can reduce the amount of water absorbed by the sample.Addition of an anionic additive(SDBS)to the mixing water improves the surface of the samples more and more by minimizing the pore size by emulsion effect,hence the water absorption decreases.The degree of hydration of the cement increased with the cellulose content containing nanofibrils.The analysis revealed that the presence of nanofibers favored the hydration of the cement by producing more calcium silicate gel and portlandite,probably the main reason for this improvement in compressive strength.展开更多
文摘The poor fatigue properties and high rigidity of cement asphalt emulsion treated mis(CETM) have for a long time been problems restricting its further development making it impossible for C-ETMto be used as surface layer materials. In this paper, a new kind of cement asphalt emulsion composite-rubberized asphalt emulsion modified Portland cement concrete (RACC) was proposed, which was formed by dispersing rubberized aSPhalt emulsion coated coarse aggregates into cement mortar matrix. In order to evaluate systematically the performance of RACC, laboratory tests with nearly one thousand SPecimen were conducted for resilient modulus, fatigue properties, ultimate ban and length,abrasion, temperature contraction, and dry shrinkage. The experimental results show that the problems existed in C-ETM have to a great extends been solved by RACc. To verify the field performance and inquire into paving technology, teSt road appearsatlsfactory it is concluded that when thed ape surface laycr of semi-rigid base course, RACC is more for surface layer material than both Portland cement concrete(PCC) and asphalt concrete(AC)
文摘The influence of nanofiberwood on the properties of the fresh condition of cement based mortars is not known in detail,despite recent advances in nanocellulose technology and it is related composite materials.Nanofiber wood from industrial waste,produced by high-pressure homogenization,was used as cement partial replacement for cement paste at a content ranging from 0%to 2%by weight of cement.The effect of the nanofiber wood content on the porosity,the compressive strength and the degree of hydration of the cement was investigated.Results have shown an improvement in the compressive strength by more than 50%with 1%of added fiber wood.The chemical modification of nanofibers wood by grafting of chains alkyls in their surfaces can reduce the quantity of water absorbed by the sample.The addition of an anionic additive(SDBS)in the water of mixing improves of more the surface of samples by minimizing the size of pores by emulsion effect,from where the absorption of water reduces.The degree of hydration of the cement has increased with the cellulose content containing nanofibrils.The analyze revealed that the presence of nanofiber wood favored the hydration of the cement by producing more calcium silicate gel and portlandite,probably the main reason for this improvement in compressive strength.
文摘Nanofibrillated wood fiber was used as fillers in the partial cement matrix replacing the cement to a content of up to 2%by weight of cement.The nanofibrillated effect of wood fibers on porosity,thermal properties and compressive strength was studied.The results obtained showed an improvement in compressive strength of more than 40%with 1%by weight of wood fiber nanofibrillate.The addition of nanofibrillated wood fiber shows a good pore reduction,and the best result was obtained with emulsion of a mixture incorporating 1%by weight of wood fiber nanofibrillate in the presence of an anionic surfactant(SDBS).Thermal conductivity measurements and thermal expansion coefficient,compared to nanofibrillated wood fiber reinforced cement pastes,showed the reinforcing efficiency of cellulose fiber nanofibrillate.The degree of hydration of the cement increased with nanofibrillated wood fibers.This property has been confirmed by Fourier transform infrared spectroscopy.These analyzes revealed that the presence of nanofibrillated wood fibers generates and promotes the hydration of the cement,producing more portlandite and calcium silicate gel,which influences the compressive strength which gives a strong improvement.
文摘Wood nanofibers from industrial waste have been used as polymeric material to reinforce the cement paste to a content of up to 2%by weight of cement.The effect of the wood nanofibre content on the porosity,the compressive strength and the degree of hydration of the cement was studied.The results showed an improvement in compressive strength of over 50%with 1%of added fiberwood.Chemical modification of nanofiber wood by grafting alkyl chains to their surface can reduce the amount of water absorbed by the sample.Addition of an anionic additive(SDBS)to the mixing water improves the surface of the samples more and more by minimizing the pore size by emulsion effect,hence the water absorption decreases.The degree of hydration of the cement increased with the cellulose content containing nanofibrils.The analysis revealed that the presence of nanofibers favored the hydration of the cement by producing more calcium silicate gel and portlandite,probably the main reason for this improvement in compressive strength.