Preparation and Mechanical Properties of UV⁃Assisted Filament Winding Glass Fiber Reinforced Polymer⁃Matrix Composite

This paper studied the preparation and mechanical properties of glass fiber reinforced polymer-matrix composite rings prepared by filament winding assisted by ultraviolet(UV)curing.A ray-tracing method was used to calculate the penetration ability of UV light in the resin casting,and then a typical composite ring with dual⁃curing characteristics was prepared by UV-assisted curing.The effects of winding speed and thermal initiator concentration on the distribution of fiber fraction and mechanical properties were studied.Microscopic morphology was used for the observation of the differences in fiber volume fraction.Mechanical properties tests and scanning electron micrographs were performed to investigate the failure and damage mechanisms of the composite ring samples.The ray tracing results indicate that the UV light can pass through a single yarn thickness and the energy transmitted is sufficient to cure the back side quickly.The experimental results show that the mechanical properties of the composite ring prepared in this paper are comparable to those of the heat-cured samples,which is sufficient to meet the requirements of the flywheel.

Hardness of resin cement cured under different thickness of lithium disilicate-based ceramic

Background The lithium disilicate-based ceramic is a newly developed all-ceramic material, which is lithium disilicate-based and could be used for fabricating almost all kinds of restorations. The extent of light attenuation by ceramic material was material-dependent. Ceramic materials with different crystal composition or crystalline content would exhibit distinct light-absorbing characteristics. The aim of this study was to analyze the influence of ceramic thickness and light-curing time on the polymerization of a dual-curing resin luting material with a lithium disilicate-based ceramic. Methods A lithium disilicate-based ceramic was used in this study. The light attenuation caused by ceramic with different thickness was determined using a spectral radiometer. The commercial dual-cured resin cement was light-cured directly or through ceramic discs with different thickness （1, 2 and 3 mm, respectively） for different times （10, 20, 30, 40, 50 and 60 seconds, respectively）. The polymerization efficiency of resin cement was expressed in terms as Vickers hardness （VHN） measured after 24 hours storage. Two-way analysis of variance （ANOVA） and Tukey＇s HSD tests were used to determine differences. Results Intensity of polymerizing light transmitted through ceramic discs was reduced from 584 mW/cm2 to about 216 mW/cm2, 80 mW/cm2 and 52 mW/cm2 at thicknesses of 1 mm, 2 mm and 3 mm, respectively. Resin cement specimens self-cured alone showed significantly lower hardness values. When resin cement was light-cured through ceramic discs with a thickness of 1 mm, 2 mm and 3 mm, no further increasing in hardness values was observed when light-curing time was more than 30 seconds, 40 seconds and 60 seconds, respectively. Conclusions Within the limitation of the present study, ceramic thickness and light-curing time had remarkable influence on the polymerization of dual-cured resin cement. When resin cement is light-cured beneath a lithium disilicate ceramic with different thickness, prolonging light-curing time accordingly may still be necessary to insure complete polymerization.