Removal of Organochlorine from Model Oil Using Mg-Modified ZSM-5 Zeolite:Dechlorination Performance,Regeneration,and Thermodynamics

Various metal-modified ZSM-5 zeolite adsorbents prepared by the impregnation method were applied to the removal of organic chlorides from model naphtha.The adsorption performance and regeneration stability were investigated by static adsorption experiments.The morphologies,structural features,and physicochemical properties of the adsorbents were characterized by X-ray diffraction,Brunauer-Emmett-Teller analysis,NH3 temperature-programmed desorption,scanning electron microscopy,transmission electron microscopy,and pyridine adsorption infrared spectroscopy.The Mg/ZSM-5 zeolite adsorbent possessed a relatively high specific surface area and good metal dispersion and exhibited the best dechlorination and regeneration performance.The characterization results revealed that introduction of the metal exerted a significant influence on the acidic properties of the catalyst surface.A decrease in the ratio of Brønsted acidic sites to Lewis acidic sites and an increase in the amount of moderately acidic sites were confirmed to be responsible for the excellent adsorption performance of the Mg-modified ZSM-5 zeolite.Furthermore,the Langmuir adsorption isotherm model was applied to study the adsorption equilibrium and thermodynamics of the Mg/ZSM-5 adsorbent under mild conditions.The results revealed that the removal of 1,2-dichloroethane by the Mg/ZSM-5 adsorbent was endothermic,spontaneous,disordered,and primarily involved physical adsorption.

Synthesis and characterization of an unusual snowflake-shaped ZSM-5 zeolite with high catalytic performance in the methanol to olefin reaction

The ZSM-5 zeolite with an unusual snowflake-shaped morphology was hydrothermally synthesized for the first time,and compared with common ellipsoidal and boat-like shaped samples.These samples were characterized by N2 adsorption-desorption,X-ray fluorescence spectroscopy,scanning electron microscopy,X-ray diffraction,magic angle spinning nuclear magnetic resonance,temperature-programmed desorption of ammonia,and infrared spectroscopy of pyridine adsorption.The results suggest that the BET surface area and SiO2/Al2O3 ratio of these samples are similar,while the snowflake-shaped ZSM-5 zeolite possesses more of the（101） face,and distortion,dislocation,and asymmetry in the framework,resulting in a larger number of acid sites than the conventional samples.Catalysts for the methanol to olefin（MTO） reaction were prepared by loading Ca on the samples.The snowflake-shaped Ca/ZSM-5 zeolite exhibited excellent selectivity for total light olefin（72%） and propene（39%） in MTO.The catalytic performance influenced by the morphology can be mainly attributed to the snowflake-shaped ZSM-5 zeolite possessing distortion,dislocation,and asymmetry in the framework,and lower diffusion limitation than the conventional samples.

Preparation of Zn-modified nano-ZSM-5 zeolite and its catalytic performance in aromatization of 1-hexene

The promoting effect of introducing Zn into nano-ZSM-5 zeolites by conventional impregnation method and isomorphous substitution on the performance of 1-hexene aromatization was investigated. The nano-ZSM-5 zeolite was synthesized by a seed-induced method without organic templates. The Zn-modified nano-ZSM-5 zeolite catalysts, xZ n/HNZ5 and y Zn/Al-HNZ5, were prepared by the conventional impregnation method and isomorphous substitution, respectively. The structure, chemical composition and acidity of the catalysts were characterized by XRD, XRF, N2 adsorption, SEM, NH3-TPD and Py-IR, while the catalytic properties were evaluated at 480 °C and a weight hourly space velocity（WHSV） of 2.0 h-1 in the aromatization procedure of 1-hexene. Compared with xZ n/HNZ5, y Zn/Al-HNZ5 exhibited smaller particles and higher dispersion of Zn species, which led to greater intergranular mesopore and homogeneous acidity distribution. Experimental results indicated that the synergy effect between the Brnsted and Lewis acid sites of the isomorphously substituted nano-ZSM-5 zeolites could significantly increase aromatics yield and improve catalytic stability in the 1-hexene aromatization.

Effect of secondary pore distribution on adsorption diffusion performance of n-hexane on 5A zeolite pellets

Adsorption rates of n-hexane on the 5A zeolite at 100 to 300 ℃ and 0.01 to 10 kPa are determined by an intelligent gravimetric analyzer （IGA-100）, and the adsorption diffusion performance of n-hexane on 5A zeolite pellets with different secondary pore distributions is analyzed. The results indicate that 5A-1 and 5A-6 zeolites have similar micropore and mesopore size distribution, while the 5A-6 zeolite has a larger secondary pore volume when the pore diameter is between 0.1 and 1 μm and more secondary pores when the pore diameter is less than 0.01 μm. The effective diffusion coefficient of nhexane on the 5A-6 zeolite pellet is 10 ^-6 to 10 4 cm^2/s, about 2 to 5 times higher than that on the 5A-1 zeolite. The effective diffusion coefficient of n-hexane on the 5A-1 zeolite pellet improves from 5 × 10^-7 to 2 × 10 6cm^2/s when the temperature increases from 100 to 300 ~C. However, the effective diffusion coefficient of n-hexane on the 5A-6 zeolite remains almost unchanged at different temperatures. The molecular average free path of n-hexane decreases from 627.15-963.28 to 0.63-0, 96 Ixm with the adsorption pressure increasing from 0.01 to 10 kPa. Such a flee path is close to the secondary pore diameter, resulting in significant Knudsen diffusion in the secondary pores. Thus, the effective diffusion coefficient of n-hexane on the 5A zeolite pellets increases before 1 kPa and decreases after 1 kPa.

晶种法直接水热合成含磷ZSM-5分子筛及其芳构化性能研究

费托合成油品向高辛烷值汽油转化的流化床体系中,水蒸气的存在极易导致ZSM-5分子筛发生不可逆的水热失活,而磷的引入能提高ZSM-5分子筛的水热稳定性。采用晶种法在无胺体系下直接水热合成了含磷ZSM-5分子筛(HS-P-Z5),并与常规浸渍法得到的含磷ZSM-5分子筛(IM-P-Z5)进行了对比。通过XRD、SEM和N2吸/脱附等对水热处理前后的ZSM-5分子筛进行了表征,通过水洗实验考察了磷元素的流失情况,并以1-辛烯为探针分子评价了ZSM-5分子筛的芳构化性能。结果表明,HS-P-Z5比IM-P-Z5具有更高强度的特征衍射峰、更多的微孔结构和酸量。水洗实验和NMR表征结果表明,HS-P-Z5具有更加稳定的磷铝结构,磷物种不易被洗掉,故其具有更好的水热稳定性,在水热处理后能够保留更多分子筛的微孔结构以及强酸位点。HS-P-Z5-ST(ST表示水热处理)具有最高的芳烃选择性,在反应时间730 min时,其芳烃选择性为23.1%,高于IMP-Z5-ST(18.4%)以及Z5-ST(11.2%)。

ZSM-5分子筛形貌对苯-乙醇烷基化催化性能的调控作用

采用水热法制备了环状、薄片、类球状聚集体和小晶粒4种不同形貌和尺寸的纳米ZSM-5分子筛,用XRD、SEM、BET、MAS-NMR和NH3-TPD对所合成分子筛进行了表征,并考察分子筛形貌对苯和乙醇烷基化性能的影响.实验结果表明:在相近的硅铝比下,不同形貌的分子筛具有相似的弱酸峰强度,短b轴和中空结构的存在会降低分子筛的强酸峰强度,分子筛的强酸峰强度直接影响烷基化性能;分子筛颗粒形貌对催化烷基化性能有较大影响,4种形貌分子筛催化苯和乙醇烷基化性能优劣顺序为:薄片ZSM-5>环状ZSM-5>类球状团聚体ZSM-5>小晶粒ZSM-5.其中,具有薄片结构的H-ZSM-5分子筛在烷基化反应过程中表现出相对较好的催化性能.综合对比结果表明:较低的强酸强度、较大的比表面积和孔容、较多的直形孔道占比下,分子筛的烷基化性能较好,产物乙苯的选择性越高.

环状ZSM-5分子筛在苯和乙醇烷基化反应中的应用

低温下采用水热晶化法合成了环状中空ZSM-5分子筛,并以磷酸二氢铵为前体,制备了不同磷负载量的环状中空ZSM-5催化剂,采用XRD,SEM,NH_(3)-TPD,Py-FTIR等方法对催化剂进行表征,并在气相连续流动固定床反应器上对苯和乙醇烷基化制乙苯进行性能评价和稳定性考察。实验结果表明,环状中空ZSM-5催化剂进行磷改性后,催化剂的酸强度降低,随着磷负载量的增加,乙苯选择性逐渐增加,甲苯和丙苯选择性逐渐降低;当磷负载量达到3%(w)后,催化剂外表面强酸位基本消失,此时乙苯选择性最高;在n(苯)∶n(乙醇)=8∶1、340℃、1.0 MPa、WHSV=1 h^(-1)条件下,对该催化剂进行了寿命考察,在300 h反应过程中,乙醇转化率超过99.9%,苯的转化率维持在11%左右,乙基苯的选择性最高达到98.4%,二甲苯相对含量最低达到0.11%。

Alkali-metal-modified ZSM-5 zeolites for improvement of catalytic dehydration of lactic acid to acrylic acid

Various ZSM-5 zeolites modified with alkali metals （Li, Na, K, Rb, and Cs） were prepared using ion exchange. The catalysts were used to enhance the catalytic dehydration of lactic acid （LA） to acrylic acid （AA）. The effects of cationic species on the structures and surface acid-base distributions of the ZSM-5 zeolites were investigated. The important factors that affect the catalytic performance were also identified. The modified ZSM-5 catalysts were characterized using X-ray diffraction, tempera- ture-programmed desorptions of NH3 and CO2, pyridine adsorption spectroscopy, and N2 adsorption to determine the crystal phase structures, surface acidities and basicities, nature of acid sites, specific surface areas, and pore volumes. The results show that the acid-base sites that are adjusted by alkali-metal species, particularly weak acid-base sites, are mainly responsible for the formation of AA. The KZSM-5 catalyst, in particular, significantly improved LA conversion and AA selectivity because of the synergistic effect of weak acid-base sites. The reaction was conducted at different reaction temperatures and liquid hourly space velocities （LHSVs） to understand the catalyst selectivity for AA and trends in byproduct formation. Approximately 98% LA conversion and 77% AA selectivity were achieved using the KZSM-5 catalyst under the optimum conditions （40 wt% LA aqueous solution, 365 ℃, and LHSV 2 h-1）.

碱处理改性ZSM-5分子筛孔结构对VOCs吸附性能的影响

采用氢氧化钠和四丙基氢氧化铵混合碱溶液处理制备一系列改性ZSM-5分子筛,通过X射线衍射(XRD)、扫描电子显微镜(SEM)、N_(2)吸附、水接触角测定等手段对改性样品进行了分析表征,采用固定床吸附器对比评价5A、NaY和不同碱改性ZSM-5分子筛吸附剂对正己烷和乙酸乙酯的动态吸附性能。结果表明:氢氧化钠和四丙基氢氧化铵摩尔浓度均为0.2 mol/L的碱改性ZSM-5-G-3样品的比表面积及总孔体积分别为425 m^(2)/g和0.585 cm^(3)/g,比改性前高硅ZSM-5-G-1样品分别提高了17.7%和174.6%,介孔比表面积增加8.6倍,达到317 m^(2)/g,介孔体积增加12.3倍,达到0.531 cm^(3)/g;随着碱溶液浓度的增加,改性分子筛材料水接触角减小;25℃时,正己烷和乙酸乙酯在ZSM-5-G-3吸附剂床层上的穿透吸附量分别为76.99和101.08 mg/g,比改性前ZSM-5-G-1吸附剂床层分别提高了40.3%和17.4%。改性ZSM-5-G-3样品对挥发性有机化合物(VOCs)吸附性能的显著提高主要归因于碱改性提供了更多的吸附位和介孔结构。

Effects of Light Rare Earth on Acidity and Catalytic Performance of HZSM-5 Zeolite for Catalytic Cracking of Butane to Light Olefins

The effects of rare earth（RE）on the structure,acidity,and catalytic performance of HZSM-5 zeolite were investigated.A series of RE/HZSM-5 catalysts,containing 7.54% RE（RE=La,Ce,Pr,Nd,Sm,Eu or Gd）,were prepared by the impregnation of the ZSM-5 type zeolites（Si/Al=64：1）with the corresponding RE nitrate aqueous solutions.The catalysts were characterized by means of FT-IR,UV-Vis,NH3-TPD,and IR spectroscopy of adsorbed pyridine.The catalytic performances of the RE/HZSM-5 for the catalytic cracking of mixed butane to light olefins were also measured with a fixed bed microreactor.The results revealed that the addition of light rare earth metal on the HZSM-5 catalyst greatly enhanced the selectivity to olefins,especially to propylene,thus increasing the total yield of olefins in the catalytic cracking of butane.Among the RE-modified HZSM-5 samples,Ce/HZSM-5 gave the highest yield of total olefins,and Nd/HZSM-5 gave the highest yield of propene at a reaction temperature of 600℃.The presence of rare earth metal on the HZSM-5 sample,not only modified the acidic properties of HZSM-5 including the amount of acid sites and acid type,that is,the ratio of L/B（Lewis acid/Brnsted acid）,but also altered the basic properties of it,which in turn promoted the catalytic performance of HZSM-5 for the catalytic cracking of butane.

Aromatization over nanosized Ga-containing ZSM-5 zeolites prepared by different methods:Effect of acidity of active Ga species on the catalytic performance

Nanosized Ga-containing ZSM-5 zeolites were prepared via isomorphous substitution and impregnation followed by characterized using various techniques. The catalytic performance of the zeolites for the aromatization of 1-hexene was investigated. The results indicate that isomorphous substitution promotes the incorporation of Ga heteroatoms into the framework along with the formation of extra-framework GaO;species（[GaO;]a） that have stronger interactions with the negative potential of the framework. In addition, based on the Py-IR results and catalytic performance, the [GaO;]aspecies with stronger Lewis acid sites produced a better synergism with moderate Br?nsted acid sites and thus improved the selectivity to aromatic compounds. However, the impregnation results in the formation of Ga;O;phase and small amounts of GaO;species that are mainly located on the external surface（[GaO;];）, which contribute to weaker Lewis acid sites due to weaker interactions with the zeolite framework. During 1-hexene aromatization, the nanosized Ga isomorphously substituted ZSM-5 zeolite samples（Gax-NZ5） exhibited better catalytic performance compared to the impregnated samples, and the highest aromatic yield（i.e.,65.4 wt%） was achieved over the Ga4.2-NZ5 sample, which contained with the highest Ga content.

Thermal and hydrothermal stabilities of the alkali-treated HZSM-5 zeolites

HZSM-5 zeolites with the micro-mesopore hierarchical porosity have been prepared by the post-synthesis of alkali-treatment, and their thermal and hydrothermal stabilities were studied using DTA, XRD, and NH3-TPD characterization techniques. Compared to the unmodified zeolite, the thermal and hydrothermal stabilities of the alkali-treated ZSM-5 zeolites were slightly deteriorated because of the introduction of mesopores caused by the desilication. Nevertheless, the alkali-treated zeolite framework could be maintained until the temperature increased to 1175 ℃.

Adsorption of Benzene and Propylene in Zeolite ZSM-5:Grand Canonical Monte Carlo Simulations

The adsorption behavior of benzene and propylene in zeolite ZSM-5 was studied by Grand Canonical Monte Carlo（GCMC） simulations. It could be found that benzene and propylene molecules showed different adsorption behavior in the zeolite cavities. The loadings of propylene were significantly larger than those of benzene at 100 kPa. From the figures of potential energy distribution, the potential energy of benzene/zeolite was more negative than that of propylene/zeolite, so benzene could be adsorbed more stably than propylene. When the temperature was in- creased from 298 to 443 K at 100 kPa, the loading ofpropylene was reduced from 99 to 82 molecules, whereas that of benzene changed little. When benzene and propylene were adsorbed in zeolite simultaneously, the competitive adsorption of them occurred; therefore, the potential energy distribution could be changed significantly. Besides, the adsorption isotherms of benzene and propylene in ZSM-5 at 298 and 443 K were simulated. The results exhibit that the different factors influenced the molecular adsorption at various temperatures and pressures, leading to the diffe- rent rules for the adsorption of benzene and propylene molecules in the zeolite. At a low pressure, the unfavorable energy of propylene/zeolite and the ＂commensurate freezing＂ phenomenon of benzene would make the loadings of itself higher than those of propylene. When pressure was higher than 5 kPa, the adsorption of benzene in ZSM-5 would nearly reach saturation.

Effect of combining the metals of group VI supported on H-ZSM-5 zeolite as catalysts for non-oxidative conversion of natural gas to petrochemicals

The most prestigious catalyst applied in natural gas （methane） non-oxidative conversion to petrochemicals is 6%Mo/H-ZSM-5. Chromium, molybdenum and tungsten are the group VI metals. Hence, in this work, 6%Mo/H-ZSM-5 was correlated with 3%Cr＋3%Mo/H-ZSM-5 and 3%W＋3%Mo/H-ZSM-5 as catalysts to examine their promoting or inhibiting effects on the various reactions taking place during methane conversion. The catalytic activities of these catalysts were tested in a continuous flow fixed bed reactor at 700℃ and a GHSV of 1500 ml·g^-1·h^-1 Characterization of the catalysts using XRD, TGA and TPD were investigated. XRD and NH3-TPD showed greater interaction between the W-phase and the Bronsted acid sites in the channels of the zeolite than between Cr-phase and the acid sites in the zeolite.

等级孔结构协同Fe改性提升ZSM-5分子筛催化苯甲醇烷基化性能

针对ZSM-5分子筛微孔扩散限制和催化活性位单一的问题,使用有序大孔-介孔碳模板为硬模板并结合原位引入金属策略,一步晶化合成了具有高结晶度、高比表面积的有序贯通大孔-介孔-微孔等级结构的Fe/ZSM-5分子筛单晶.通过X射线衍射(XRD)、紫外-可见光谱(UV-Vis)、H_(2)程序升温还原实验(H2-TPR)和X射线光电子能谱(XPS)等手段对催化剂中活性Fe的存在形式进行了表征.结果表明,该材料中位于离子交换位及铁氧八面体(六配位)的孤立Fe(III)是主要的氧化还原活性中心,当Fe负载量(质量分数)为1%时,苯甲醇转化率最高为59.3%,产物选择性为83.2%,最终收率达到49.3%,在循环使用5次后仍保持高催化活性.

Effects of Calcination Temperature on the Acidity and Catalytic Performances of HZSM-5 Zeolite Catalysts for the Catalytic Cracking of n-Butane

The acidic modulations of a series of HZSM-5 catalysts were successfully made by calcination at different treatment temperatures, i.e. 500, 600, 650, 700 and 800 ℃, respectively. The results indicated that the total acid amounts, their density and the amount of B-type acid of HZSM-5 catalysts rapidly decreased, while the amounts of L-type acid had almost no change and thus the ratio of L/B was obviously enhanced with the increase of calcination temperature （excluding 800 ℃）. The catalytic performances of modified HZSM-5 catalysts for the cracking of n-butane were also investigated. The main properties of these catalysts were characterized by means of XRD, N2 adsorption at low temperature, NH3-TPD, FTIR of pyridine adsorption and BET surface area measurements. The results showed that HZSM-5 zeolite pretreated at 800 ℃ had very low catalytic activity for n-butane cracking. In the calcination temperature range of 500-700 ℃, the total selectivity to olefins, propylene and butene were increased with the increase of calcination temperature, while, the selectivity for arene decreased with the calcination temperature. The HZSM-5 zeolite calcined at 700 ℃ produced light olefins with high yield, at the reaction temperature of 650 ℃ the yields of total olefins and ethylene were 52.8% and 29.4%, respectively. Besides, the more important role is that high calcination temperature treatment improved the duration stability of HZSM-5 zeolites. The effect of calcination temperature on the physico-chemical properties and catalytic performance of HZSM-5 for cracking of n-butane was explored. It was found that the calcination temperature had large effects on the surface area, crystallinity and acid properties of HZSM-5 catalyst, which further affected the catalytic performance for n-butane cracking.

Disproportionation of Toluene by Modified ZSM-5 Zeolite Catalysts with High Shape-selectivity Prepared Using Chemical Liquid Deposition with Tetraethyl Orthosilicate

Shape-selective catalysts for the disproportionation of toluene were prepared by the modification of the cylinder-shaped ZSM-5 zeolite extrudates with chemical liquid deposition with TEOS （tetraethyl orthosilicate）.Various parameters for preparing catalysts were changed to investigate the suitable conditions.The resulting cata-lysts were tested in a pressured fixed bed reactor and characterized by SEM （scanning electron microscopy）.The conversion of toluene and para-xylene selectivity were influenced remarkably by the n（SiO2）/n（Al2O3） ratio of ZSM-5 zeolite,the type and amount of deposition agent,acid and solvent used,and the time and cycle of deposition treatment.TEOS was proved to be a more efficient agent than the conventional polysiloxanes when the deposition amount was low.The catalyst prepared at the suitable conditions exhibited a high para-xylene selectivity of 91.1% with considerable high conversion of 25.6%.SEM analyses confirmed the formation of a layer of amorphous silica on the external surface of ZSM-5 zeolie crystals,which was responsible for the highly enhanced shape-selectivity.

Ce改性HZSM-5分子筛催化甲醇与丁烯耦合转化制丙烯性能研究

为了进一步提高HZSM-5分子筛在甲醇与丁烯耦合转化制丙烯反应中的催化性能,采用浸渍法对HZSM-5分子筛进行Ce改性,得到了一系列具有不同Ce负载量的x Ce/HZSM-5催化剂。考察了Ce负载量和反应条件(甲醇与丁烯物质的量之比、反应温度和空时)对催化性能的影响,并结合催化剂表征结果,分析了Ce改性对催化性能和物化性质的影响,探讨了x Ce/HZSM-5催化剂的构效关系。结果表明,在温度550℃、压力0.1 MPa、甲醇与丁烯物质的量之比0.8、空时2.3(g cat·h)mol CH_(2)的最佳反应条件下,Ce负载量(w)为2.5%的2.5Ce HZSM-5催化剂具有最高的丙烯收率,为41.9%。Ce与HZSM-5分子筛上羟基官能团(OH)发生相互作用,降低了B酸酸量,同时生成新的L酸中心Ce(OH)^(2+),调变了催化剂表面酸中心密度和酸类型分布,提高了丙烯选择性和收率。

磷改性ZSM-5分子筛的制备及其催化苯酚烷基化反应性能

为了解决ZSM-5分子筛催化苯酚烷基化对甲酚选择性低的问题,采用等体积浸渍法对制备的ZSM-5分子筛进行硅、磷、镁改性得到系列改性ZSM-5催化剂。采用XRD、Py-IR和BET等手段对改性前后ZSM-5分子筛进行表征,并采用固定床反应器考察了改性ZSM-5分子筛催化苯酚烷基化反应性能。结果表明:磷负载质量分数15%的15P-ZSM-5分子筛的比表面积和总酸量分别从未改性前的395 m^(2)/g和406μmol/g降低到了309 m^(2)/g和128μmol/g,外表面酸量从未改性前的18μmol/g降低到了3μmol/g;在质量空速12 h^(-1)、反应温度420℃、反应压力1.5 MPa条件下进行催化苯酚烷基化反应,磷负载质量分数10%的10P-ZSM-5分子筛作用下的苯酚转化率为52.4%、对甲酚选择性为15.4%;磷改性可以通过磷酸根离子覆盖ZSM-5分子筛外表面的酸位点对表面酸性酸量进行调节,提高对甲酚的选择性,与其他改性分子筛相比,磷改性分子筛具有最佳的苯酚烷基化反应性能。

碱处理制备高硅多级孔ZSM-5催化MTP反应

以水热法合成母体硼硅沸石(BS),然后使用氢氧化钠(NaOH)溶液单独处理以及氢氧化钠和十六烷基三甲基溴化铵(CTAB)混合溶液处理,并在碱溶液中加入铝源,制备一系列高硅多级孔ZSM-5分子筛样品(命名为BHZ-A和BHZ-AB系列样品)。采用XRD、SEM、ICP、Ar物理吸附、NH3-TPD和热重分析等手段表征样品的孔结构和酸性质等,并提出了CTAB的保护作用:在碱处理过程中,CTAB抑制NaOH的脱硅作用从而保护分子筛不被过度刻蚀。在压力0.1 MPa、温度743 K、水/醇摩尔比为1/1和甲醇质量空速为3 h^(-1)条件下,采用固定床反应器评价BHZ(含B的H型ZSM-5)分子筛样品催化甲醇制丙烯(MTP)反应72 h的性能。结果表明:通过碱处理制备得到的高硅多级孔ZSM-5分子筛的强酸量是影响其MTP反应性能和积炭的主要因素,由于BHZ-0.1A和BHZ-0.1AB样品具有丰富的介孔和合适的酸性,其MTP反应性能优异,丙烯选择性均约为50%,积炭量均约为1.5%。