Effect of Ni content on the weldability of middle-chromium hyperpure ferritic stainless steels 00Cr21Ti

Excellent weldability substantially contributes to the intrinsic quality of steels,while appropriate chemical composition plays a primary role in the essential weldability of steels.The poor weldability of ferritic stainless steels could be improved through modification with minor alloy elements while minimally increasing the cost.Therefore,studying the effect of minor alloy elements on the weldability of steels is of considerable importance.In this study,several steels of middle-chromium hyperpure ferritic stainless 00Cr21Ti with different Ni content(0.3%,0.5%,0.8%,and 1.0%)were developed,and their weldabilities of butt joint samples welded using the metal inert gas welding process,including the influence of welded joints on the microstructure,tensile performance,corrosion resistance,and fatigue property,were investigated.Results show that the steels with w(Ni)≥0.8%exhibit excellent mechanical properties compared with those with low-Ni content steels,further,their impact toughness at normal atmospheric temperature meets the industrial application standard and the fatigue property is similar to that of 304 austenitic stainless steel.Moreover,results show that the corrosion resistance of all the samples is almost at the same level.The results acquired in this study are supposed to be useful for the optimization of the chemical composition of stainless steels aiming to improve weldability.

Effects of TiC on the microstructure and formation of acicular ferrite in ferritic stainless steel

The formation mechanism of acicular ferrite and its microstructural characteristics in 430 ferrite stainless steel with TiC additions were studied by theory and experiment.Using an"edge?to?edge matching"model,a 5.25 mismatch between TiC(FCC structure)and ferritic stainless steel(BCC structure)was identified,which met the mismatch requirement for the heterogeneous nucleation of 430 ferritic stainless steel.TiC was found to be an effective nucleation site for the formation of acicular ferrite in a smelting experiment,as analyzed by metallographic examination,Image-Pro Plus 6.0 analysis software,and SEM–EDS.Furthermore,small inclusions in the size of 2–4?m increased the probability of acicular ferrite nucleation,and the secondary acicular ferrite would grow sympathetically from the initial acicular ferrite to produce multi-dimensional acicular ferrites.Moreover,the addition of Ti C can increase the average microstrain and dislocation density of 430 ferrite stainless steel,as calculated by Williamson-Hall(WH)method,which could play some role in strengthening the dislocation.

IN SITU OBSERVATION OF GROWTH BEHAVIOR AND MORPHOLOGY OF DELTA-FERRITE AS FUNCTION OF SOLIDIFICATION RATE IN AN AISI304 STAINLESS STEEL

It was presented the in situ observation of growth behavior and morphology of delta-ferrite as a function of solidification rate in an AISI304 stainless steel. The specimens have been solidified and observed using confocal scanning laser microscopy (CSLM). The δ-phase always appears like cells on the sample surface when critical supercooling occurs, during which the L→δ transformation starts. The solid-liquid (S-L) interface is found to be finger shaped and has no faceted shape. γ phase appears among δ grains due to partitioning of Ni into the melt during solidification, when solidification rate is higher. The mergence of observed δ cells is possible for the steel sample cooled at 7.5℃/min. The formation of dendrites can be observed on the free surface of the steel sample cooled at 150℃/min. The size of solidified delta grains decreases from 120 to 20-80μm, and the volume fraction of solidified austenite increases with increase in solidification rate from 7.5 to 150℃/min. The relation between the tip radius of δ cell and its growth rate is deduced, and the results agree with the experimental values.

In-situ three-dimensional visualization of dynamic tension deformation in ferrite stainless steels

An improved three-dimensional （3-D） experimental visualization methodology is presented tor evaluating the fracture mechanisms of ferritic stainless steels by in-situ tensile testing with an environmental scanning electron microscope （ESEM）. The samples were machined with a radial notched shape and a sloped surface. Both planar surface deformation and sloping surface deformation-induced microvoids were observed during dynamic tension experiments, where a greater amount of information could be obtained from the sloping surface. The results showed that microvoids formed at the grain boundaries of highly elongated large grains. The microvoids nucleated in the severely deformed regions grew nearly parallel to the tensile axis, predominantly along the grain boundaries. The microvoids nucleated at the interface of particles and the matrix did not propagate due to the high plasticity of the matrix. The large microvoids propagated and showed a zigzag shape along the grain boundaries,seemingly a consequence of the fracture of the slip bands caused by dislocation pile-ups. The final failure took place due to the reduction of the load-beating area.

Effect of heat treatment on the behavior ofδ-ferrite in B410D martensitic stainless steel

The morphology and the evolution of δ-ferrite existing in B410D slabs, hot-rolled plates, annealed plates and quenched plates were studied through metallographic observation. Results show that δ-ferrite forms during the solidification process and that it easily grows and increases in quantity during high temperature annealing. Band-shaped δ-ferrite in hotrolled plates is difficult to be eliminated by conventional heat treatment and hard to recrystallize.

Development of high strength ferrite-martensite stainless steels ( FMSSs) for railway cargo transportation

Two ferrite-martensite stainless steels （FMSSs） were developed by Baosteel based on the T4003 composition, through optimizing the manganese and nickel contents ,reducing silicon, carbon and nitrogen contents, controlling remnant niobium and molybdenum ,adding sufficient titanium and controlling the processing. In this study ,the physical metallurgy of such FMSSs was investigated with the emphasis on the alloying effect on the phase balance during processing and the transformation behavior during welding for different microstructures. In addition, the mechanical behavior and the weldability were investigated. The results indicate that such steels have a good combination of strength and toughness and better weldability compared with the traditional 1. 4003 steel. Such high strength steels are highly suitable for railway cargo transportation where the wall thickness of the wagons can be reduced,resulting in weight savings.

Ultra-Pure Ferritic Stainless Steels-Grade,Refining Operation,and Application

The grades of ultra-pure ferritic stainless steels, especially the grades used in automobile exhaust system, were reviewed. The dependence of properties on alloying elements, the refining facilities, and the mechanism of the reactions in steel melts were described in detail. Vacuum, strong stirring, and powder injection proved to be effective technologies in the melting of ultra-pure ferritic stainless steels. The application of the ferritic grades was also briefly introduced.

Effect of welding parameters on the heat-affected zone of AISI409 ferritic stainless steel

One of the main problems during the welding of ferritic stainless steels is severe grain growth within the heat-affected zone （HAZ） In the present study, the microstmctural characteristics of tungsten inert gas （TIG） welded AISI409 ferritic stainless steel were investigated by electron backscattered diffraction （EBSD）, and the effects of welding parameters on the grain size, local misorientation, and low-angle grain boundaries were studied. A 3-D finite element model （FEM） was developed to predict the effects of welding parameters on the holding time of the HAZ above the critical temperature of grain growth. It is found that the base metal is not fully recrystallized. During the welding, complete recrystallization is followed by severe grain growth. A decrease in the number of low-angle grain boundaries is observed within the HAZ. FEM results show that the final state of residual sWains is caused by competition between welding plastic strains and their release by recrystallization. Still, the decisive factor for grain growth is heat input.

Effect of tin addition on the microstructure and properties of ferritic stainless steel

This article reports the effects of Sn on the inclusions as well as the mechanical properties and hot workability of ferritic stainless steel. Precipitation phases and inclusions in Sn-bearing ferritic stainless steel were observed, and the relationship between the workability and the microstructure of the steel was established. Energy-dispersive X-ray spectroscopic analysis of the steel reveals that an almost pure Sn phase forms and MnS-Sn compound inclusions appear in the steel with a higher Sn content. Little Sn segregation was observed in grain boundaries and in the areas around sulfide inclusions;however, the presence of Sn does not adversely affect the workability of the steel con-taining 0.4wt%Sn. When the Sn content is 0.1wt%-0.4wt%, Sn improves the tensile strength and the plastic strain ratio and also improves the plasticity with increasing temperature. A mechanism of improving the workability of ferritic stainless steel induced by Sn addition was discussed：the presence of Sn lowers the defect concentration in the ultra-pure ferritic lattice and the good distribution of tin in the lattice overcomes the problem of hot brittleness that occurs in low-carbon steel as a result of Sn segregation.

Corrosion behavior of ferritic stainless steel with 15wt% chromium for the automobile exhaust system

The effect of chloride ion concentration, pH value, and grain size on the pitting corrosion resistance of a new ferritic stainless steel with 15wt% Cr was investigated using the anodic polarization method. The semiconducting properties of passive films with different chloride ion concentrations were performed using capacitance measurement and Mott-Schottky analysis methods. The aging precipitation and intergranular corrosion behavior were evaluated at 400- 900℃. It is found that the pitting potential decreases when the grain size increases. With the increase in chloride ion concentration, the doping density and the flat-bland potential increase but the thickness of the space charge layer decreases. The pitting corrosion resistance increases rapidly with the decrease in pH value. Precipitants is identified as Nb（C,N） and NbC, rather than Cr-carbide. The intergranular corrosion is attributed to the synergistic effects of Nb（C,N） and NbC precipitates and Cr segregation adjacent to the precipitates.

Interfacial Microstructure of Diffusion Bonded Inconel 738 and Ferritic Stainless Steel Couple

In this study, Inconel 738 alloy was diffusion bonded to a ferritic stainless steel. The effect of bonding temperature on the microstructural development across the joint region was investigated. Following the diffusion bonding, conventional characterization techniques such as scanning electron microscopy （SEM）, energy dispersive X-ray （EDX） and microhardness were used to examine the interracial microstructure. It was seen that bonding temperature was effective on the diffusion of Ni from Inconel 738 to ferritic stainless steel that affected the microstructure of the interface. Austenite phase was formed at the interface as a result of Ni diffusion from the Inconel 738 to the interface.

Tensile and Impact Properties of Shielded Metal Arc Welded AISI 409M Ferritic Stainless Steel Joints

The present study is concerned with the effect of filler metals such as austenitic stainless steel, ferritic stainless steel and duplex stainless steel on tensile and impact properties of the ferritic stainless steel conforming to AISI 409M grade. Rolled plates of 4 mm thickness were used as the base material for preparing single pass butt welded joints. Tensile and impact properties, microhardness, microstructure and fracture surface morphology of the joints fabricated by austenitic stainless steel, ferritic stainless steel and duplex stainless steel filler metals were evaluated and the results were reported. From this investigation, it is found that the joints fabricated by duplex stainless steel filler metal showed higher tensile strength and hardness compared to the joints fabricated by austenitic and ferritic stainless steel filler metals. Joints fabricated by austenitic stainless steel filler metal exhibited higher ductility and impact toughness compared with the joints fabricated by ferritic stainless steel and duplex stainless steel filler metals.

Activating Flux Design for Laser Weldingof Ferritic Stainless Steel

The behaviors of YAG laser welding process of ferritic stainless steel with activating fluxes were investigatedin this study. Some conventional oxides, halides and carbonates were applied in laser welding. The resultsshowed that the effect of oxides on the penetration depth was more remarkable. Most activating fluxes improved thepenetration more effectively at low power than that at high power. The uniform design was adopted to arrange theformula of multicomponent activating fluxes, showing that the optimal formula can make the penetration depth up to2.23 times as large as that without flux, including 50% ZrO2, 12.09% CaCO3, 10.43% CaO and 27.48% MgO. Throughthe high-speed photographs of welding process, CaF2 can minimize the plasma volume but slightly improve the penetrationcapability.

Effect of Cr, Mo, and Nb additions on intergranular cohesion of ferritic stainless steel: First-principles determination

Effects of Cr, Mo, and Nb on the ferritic stainless steel ]2（210） grain boundary and intragranularity are investigated using the first-principles principle. Different positions of solute atoms are considered. Structural stability is lowered by Cr doping and enhanced by Mo and Nb doping. A ranking on the effect of solute atoms enhancing the cohesive strength of the grain boundary, from the strongest to the weakest is Cr, Mo, and Nb. Cr clearly prefers to locate in the intragranular region of Fe rather than in the grain boundary, while Mo and Nb tend to segregate to the grain boundary. Solute Mo and Nb atoms possess a strong driving force for segregation to the grain boundary from the intragranular region, which increases the grain boundary embrittlement. For Mo- and Nb-doped systems, a remarkable quantity of electrons accumulate in the region close to Mo （Nb）. Therefore, the bond strength may increase. With Cr, Mo, and Nb additions, an anti-parallel island is formed around the center of the grain boundary.

Test research on sticking mechanism during hot rolling of SUS 430 ferritic stainless steel

The sticking phenomenon during hot rolling of SUS 430 ferritic stainless steel was investigated by means of a two-disc type high-temperature wear tester. The test results indicate that sticking particles on the surfaces of high chromium steel （HiCr） and high-speed steel （HSS） rolls undergo nucleation, growth, and saturation stages. Grooves on the roll surface generated by grinding provide nucleation sites for sticking particles. The number of sticking particles on the HiCr roll surface is greater than that on the HSS roll surface. The average surface roughnesses （Ra） of HiCr and HSS rolls change from 0.502 and 0.493 μm at the initial stage to 0.837 and 0.530 μm at the saturation stage, respectively. The test further proves that the sticking behavior is strongly dependent on roll materials, and the HSS roll is more benefi- cial to prevent particles sticking compared with the HiCr roll under the same hot-rolling conditions.

Application and failure evaluation of ferritic stainless steels for automotive exhaust systems

In recent years, with attention paid to global environmental problems, there have been requirements for continuous improvement of automobile fuel economy and exhaust gas purification rate. The properties of the ferritic stainless steels （FSS） used to make automobile parts have been improved. This paper introduces the construction of automotive exhaust systems and describes their main failure behaviors and corrosion evaluation procedures.

Effect of micro-alloying Nb and Ti on solidification structure in 430 ferritic stainless steel

With the increase in the content of carbon, nitrogen and titanium in 430 ferritic stainless steel, the refinement of the solidification structure is obvious and the proportion of equiaxed grain increases remarkably as well. This is attributed to the increasing role of the inhomogeneous nucleation by TiN particles during solidification. In addition, more fine precipitations of （Ti ,Nb）N are found in steel with increased carbon and nitrogen content.

Surface segregation of copper in antibacterial ferritic stainless steel

By using auger electron spectroscopy （AES） and diffusion theory to analyze the surface segregation of copper in antibacterial ferritic stainless steel, establishing a diffusion model, and calculating the activation energy of diffusion of the copper in ferrite, the affect of surface segregation on the antibacterial capabilities were researched. The results show that the concentration of the copper surface at 973 K and 1 073 K could be expressed asln X^sCu/X^bCu = k0 √Dt/d（-△Hv^Cu＋△Hf^tron＋ △Hs^Cu）/3RT , with the parameters relating to the concentration of the diffusion layer, the coefficient of diffusion, the length of diffusion, the latent heat of evaporation and the latent heat of fusion. The activation energy of diffusion of copper in ferrite is approximately 221. 688 kJ/mol. The antibacterial property of the steel is improved as the surface segregation of the copper is increased. At 1 073 K for 60 min, the concentration of the surface copper is over three times higher than the basic concentration. The antibacterial property of the stainless steel can reach approximately 99.9%.

Effect of stabilizing elements Nb and Ti on the microstructure and properties of low carbon ferritic stainless steel

The effect of stabilizing elements, such as Nb and Ti, on the microstructure and properties of low carbon ferritic stainless steel （FSS） has been investigated. The results of the Thermo-calc simulation have shown that the interstitial elements, such as C and N, may be completely stabilized by the addition of Nb and Ti. With the increase of Nb and Ti contents ,the α ＋ γ two phases gradually transfer to a single α-phase under a high temperature condition ,and the content of the carbide M23 C6 gradually decreases. The microstructure has indicated that the combined addition of Nb and Ti can promote the recrystallization of the band structure and form more uniform equiaxed grains. Also, with the increase of Nb and Ti contents,the elongation, the r-value and the corrosion resistance of cold-rolled and annealed sheets are improved prominently. In comparison with the effect of Ti ,the addition of Nb is more beneficial to the increase of r-value and the corrosion resistance.

Study on the corrosion properties of 0Cr11 ferritic stainless steel for automotive exhaust systems

This study investigates the corrosion properties of 0Cr11Ti and 0Cr11NbTi ferritic stainless steels （FSS） for automotive exhaust systems. The results indicate that the base metal and weld seam of 0Cr11NbTi steel exhibit better intergranular and condensate corrosion resistant properties because carbon and nitrogen are stabilized by Nb and Ti, and the precipitation of Cr carbide is retarded in grain boundaries.