A series of(Y_(1-y), Gdy)_(0.95-x)(P_y, V_(1-y))O_4 :0.05Eu^(3+), xBi^(3+)+phosphors have been successfully prepared by a subsection method. The crystal structure, surface morphology and luminescence properties were i...A series of(Y_(1-y), Gdy)_(0.95-x)(P_y, V_(1-y))O_4 :0.05Eu^(3+), xBi^(3+)+phosphors have been successfully prepared by a subsection method. The crystal structure, surface morphology and luminescence properties were investigated. It was found that the sintered samples crystallized in a tetragonal crystal system with space group I_(41)/amd(a = b = 0.7119 nm, c = 0.6290 nm). The products presented rod-like morphology with length of 100-150 nm and width of 50-100 nm. A maximum peak at 619 nm(~5D_0 →~7F_2) was observed in emission spectrum of the phosphors. It was also found that co-doping of Bi^(3+)+, P5+and Gd^(3+)ions into YVO_4:Eu^(3+)can not only made the right edge of the excitation band shift to the long-wavelength region, but also increased the emission intensity at 619 nm sharply and decreased the lifetime of fluorescence decay. These results may expand the application scope of the phosphors.展开更多
基金supported by the Program for New Material Development & Application innovative Research Team of Higher Education in Chong Qing of China (Grant No. 201042)
文摘A series of(Y_(1-y), Gdy)_(0.95-x)(P_y, V_(1-y))O_4 :0.05Eu^(3+), xBi^(3+)+phosphors have been successfully prepared by a subsection method. The crystal structure, surface morphology and luminescence properties were investigated. It was found that the sintered samples crystallized in a tetragonal crystal system with space group I_(41)/amd(a = b = 0.7119 nm, c = 0.6290 nm). The products presented rod-like morphology with length of 100-150 nm and width of 50-100 nm. A maximum peak at 619 nm(~5D_0 →~7F_2) was observed in emission spectrum of the phosphors. It was also found that co-doping of Bi^(3+)+, P5+and Gd^(3+)ions into YVO_4:Eu^(3+)can not only made the right edge of the excitation band shift to the long-wavelength region, but also increased the emission intensity at 619 nm sharply and decreased the lifetime of fluorescence decay. These results may expand the application scope of the phosphors.