A new method of preparing V_2O_3 by thermal decomposition from hydrazine-containing vanadium salt was described. The process was investigated by thermal analysis (TG and DSC) and the thermally decomposed product was s...A new method of preparing V_2O_3 by thermal decomposition from hydrazine-containing vanadium salt was described. The process was investigated by thermal analysis (TG and DSC) and the thermally decomposed product was studied by S.E.M., chemical analysis and X-ray diffraction. The result indicated that the product obtained in this way was V_2O_3.展开更多
The flux agents in common mould fluxes were fluoride and sodium oxide, which would do great harm to environments. B2O3 was selected as flux. The physical properties of B2O3-containing mould fluxes were studied. The co...The flux agents in common mould fluxes were fluoride and sodium oxide, which would do great harm to environments. B2O3 was selected as flux. The physical properties of B2O3-containing mould fluxes were studied. The corresponding physical properties of 37. 91% CAO-43.09% SiO2-5% Al2O3-5% MgO-2% Li20-7% B2O3 mould fluxes were as follows： the melting point was 909℃, the flowing temperature was 1 160℃, the viscosity and surface tension at 1300 ℃ were 0. 4 Pa · s and 0.32 N/m respectively, which could meet the demands for certain kinds of steels for mould fluxes in continuous casting.展开更多
V2O5/WO3‐TiO2 and V2O5/WO3‐TiO2‐SiO2 catalysts were prepared by a wetness impregnation method, and both the catalysts were hydrothermally aged at 750℃ in 10 vol%H2O/air for 24 h. The catalysts were evaluated for N...V2O5/WO3‐TiO2 and V2O5/WO3‐TiO2‐SiO2 catalysts were prepared by a wetness impregnation method, and both the catalysts were hydrothermally aged at 750℃ in 10 vol%H2O/air for 24 h. The catalysts were evaluated for NOx conversion using NH3 as the reductant. Hydrothermal ageing decreased the NOx conversion of V2O5/WO3‐TiO2 catalyst severely over the entire measured tem‐perature range. Interestingly, the NH3‐SCR activity of the silica‐modified catalyst at 220–480℃ is enhanced after ageing. The catalysts were characterized by X‐ray diffraction, nitrogen adsorption, X‐ray fluorescence, Raman spectroscopy, H2 temperature‐programmed reduction, and NH3 temper‐ature‐programmed desorption. The addition of silica inhibited the phase transition from anatase to rutile titania, growth of TiO2 crystallite size and shrinkage of catalyst surface area. Consequently, the vanadia species remained highly dispersed and the hydrothermal stability of the V2O5/WO3‐TiO2 catalyst was significantly improved.展开更多
文摘A new method of preparing V_2O_3 by thermal decomposition from hydrazine-containing vanadium salt was described. The process was investigated by thermal analysis (TG and DSC) and the thermally decomposed product was studied by S.E.M., chemical analysis and X-ray diffraction. The result indicated that the product obtained in this way was V_2O_3.
基金Item Sponsored by National Natural Science Foundation of China (50474037) Jiangsu Province Natural Science Foundation forUniversity of China (04BJK430022)
文摘The flux agents in common mould fluxes were fluoride and sodium oxide, which would do great harm to environments. B2O3 was selected as flux. The physical properties of B2O3-containing mould fluxes were studied. The corresponding physical properties of 37. 91% CAO-43.09% SiO2-5% Al2O3-5% MgO-2% Li20-7% B2O3 mould fluxes were as follows： the melting point was 909℃, the flowing temperature was 1 160℃, the viscosity and surface tension at 1300 ℃ were 0. 4 Pa · s and 0.32 N/m respectively, which could meet the demands for certain kinds of steels for mould fluxes in continuous casting.
基金supported by the National Natural Science Foundation of China (51372137)the National High Technology Research and Development Program of China (863 Program,2015AA034603)~~
文摘V2O5/WO3‐TiO2 and V2O5/WO3‐TiO2‐SiO2 catalysts were prepared by a wetness impregnation method, and both the catalysts were hydrothermally aged at 750℃ in 10 vol%H2O/air for 24 h. The catalysts were evaluated for NOx conversion using NH3 as the reductant. Hydrothermal ageing decreased the NOx conversion of V2O5/WO3‐TiO2 catalyst severely over the entire measured tem‐perature range. Interestingly, the NH3‐SCR activity of the silica‐modified catalyst at 220–480℃ is enhanced after ageing. The catalysts were characterized by X‐ray diffraction, nitrogen adsorption, X‐ray fluorescence, Raman spectroscopy, H2 temperature‐programmed reduction, and NH3 temper‐ature‐programmed desorption. The addition of silica inhibited the phase transition from anatase to rutile titania, growth of TiO2 crystallite size and shrinkage of catalyst surface area. Consequently, the vanadia species remained highly dispersed and the hydrothermal stability of the V2O5/WO3‐TiO2 catalyst was significantly improved.
基金Supported by Fundamental Research Funds for Central Universities(HEUCF201403002)Advanced Technique Project Funds of the Manufacture and Information Ministry