针对目前城市管道建设中广泛存在的传统手工焊和半自动焊接工艺所导致的焊接质量不稳定等问题,设计了一种自保护药芯焊丝管道全位置自动焊接工艺。采用氩弧自动焊根焊+自保护药芯焊丝自动焊填充及盖面焊的焊接方法,选用22°U形坡口...针对目前城市管道建设中广泛存在的传统手工焊和半自动焊接工艺所导致的焊接质量不稳定等问题,设计了一种自保护药芯焊丝管道全位置自动焊接工艺。采用氩弧自动焊根焊+自保护药芯焊丝自动焊填充及盖面焊的焊接方法,选用22°U形坡口及Φ1.6 mm JC-29Ni1焊丝。结果表明,焊接接头力学性能能够达到标准要求。该工艺能够为城市管道全位置自动焊提供参考。展开更多
A V-shaped bending device was established to evaluate the effects of temperature and bending fillet radius on springback behavior of 2219-W aluminum alloy at cryogenic temperatures.The cryogenic springback mechanism w...A V-shaped bending device was established to evaluate the effects of temperature and bending fillet radius on springback behavior of 2219-W aluminum alloy at cryogenic temperatures.The cryogenic springback mechanism was elucidated through mechanical analyses and numerical simulations.The results indicated that the springback angle at cryogenic temperatures was greater than that at room temperature.The springback angle increased further as the temperature returned to ambient conditions,attributed to the combined effects of the “dual enhancement effect” and thermal expansion.Notably,a critical fillet radius made the springback angle zero for 90° V-shaped bending.The critical fillet radius at cryogenic temperatures was smaller than that at room temperature,owing to the influence of temperature variations on the bending moment ratio between the forward bending section at the fillet and the reverse bending section of the straight arm.展开更多
Thin-walled metal parts with functional micro-featured surface have broad application prospects in the fields of resistance reduction,noise reduction,etc.In this study,a novel micro-rolling&incremental sheet formi...Thin-walled metal parts with functional micro-featured surface have broad application prospects in the fields of resistance reduction,noise reduction,etc.In this study,a novel micro-rolling&incremental sheet forming hybrid process(μR-ISF)is proposed to fabricate thin-walled metal parts with microgroove arrays.An analytical model which relates the rolling force and microgroove depth in the micro-rolling stage was first established.Then,the formation mechanism of microgroove morphology during both micro-rolling stage and macro-shape forming stage are investigated.After the micro-grooved sheet being incrementally formed,a significant reduction(between 21%to nearly 60%)is occurred in the depth of both transverse and longitudinal grooves compared to the flat sheet.Meanwhile,the width of transverse grooves decreases slightly by about 10%on average,while the width of longitudinal microgrooves increases significantly by more than 30%on average.After micro-rolling,85°{102}tensile twins appear on the micro-grooved sheet and the percentage of 65°{112}compressive twins increases.After incremental forming,the percentage of low-angle grain boundaries and the density of geometrically necessary dislocations in the formed part increase significantly,and the grain size distribution becomes more uniform.The present work provides a new strategy for the fabrication of 3D metal thin-walled components with surface micro-features.展开更多
文摘针对目前城市管道建设中广泛存在的传统手工焊和半自动焊接工艺所导致的焊接质量不稳定等问题,设计了一种自保护药芯焊丝管道全位置自动焊接工艺。采用氩弧自动焊根焊+自保护药芯焊丝自动焊填充及盖面焊的焊接方法,选用22°U形坡口及Φ1.6 mm JC-29Ni1焊丝。结果表明,焊接接头力学性能能够达到标准要求。该工艺能够为城市管道全位置自动焊提供参考。
基金the financial supports from the National Key Research and Development Program of China (No. 2019YFA0708804)。
文摘A V-shaped bending device was established to evaluate the effects of temperature and bending fillet radius on springback behavior of 2219-W aluminum alloy at cryogenic temperatures.The cryogenic springback mechanism was elucidated through mechanical analyses and numerical simulations.The results indicated that the springback angle at cryogenic temperatures was greater than that at room temperature.The springback angle increased further as the temperature returned to ambient conditions,attributed to the combined effects of the “dual enhancement effect” and thermal expansion.Notably,a critical fillet radius made the springback angle zero for 90° V-shaped bending.The critical fillet radius at cryogenic temperatures was smaller than that at room temperature,owing to the influence of temperature variations on the bending moment ratio between the forward bending section at the fillet and the reverse bending section of the straight arm.
基金This work is supported by the National Natural Science Foundation of China(Nos.51975328,52275348)Taishan Scholar Project of Shandong Province(No.tsqn202306006)Youth Innovation Technology Support Program of Shandong Provincial Universities(No.2022KJ041).
文摘Thin-walled metal parts with functional micro-featured surface have broad application prospects in the fields of resistance reduction,noise reduction,etc.In this study,a novel micro-rolling&incremental sheet forming hybrid process(μR-ISF)is proposed to fabricate thin-walled metal parts with microgroove arrays.An analytical model which relates the rolling force and microgroove depth in the micro-rolling stage was first established.Then,the formation mechanism of microgroove morphology during both micro-rolling stage and macro-shape forming stage are investigated.After the micro-grooved sheet being incrementally formed,a significant reduction(between 21%to nearly 60%)is occurred in the depth of both transverse and longitudinal grooves compared to the flat sheet.Meanwhile,the width of transverse grooves decreases slightly by about 10%on average,while the width of longitudinal microgrooves increases significantly by more than 30%on average.After micro-rolling,85°{102}tensile twins appear on the micro-grooved sheet and the percentage of 65°{112}compressive twins increases.After incremental forming,the percentage of low-angle grain boundaries and the density of geometrically necessary dislocations in the formed part increase significantly,and the grain size distribution becomes more uniform.The present work provides a new strategy for the fabrication of 3D metal thin-walled components with surface micro-features.