不同因素对V2O5-WO3-TiO2催化剂低温NO转化率的影响

考察不同V2O5负载量、O2体积分数、NO体积分数、SO2体积分数、H2O体积分数、n(NH3)/n(NO)、空速和在线加热再生等因素对浸渍法制备的V2O5-WO3/Ti O2催化剂低温NO转化率的影响.综合分析,选定V2O5最佳负载质量分数为3%,当反应温度为160℃时,NO转化率为93. 7%. 110~320℃时,N2选择性大于98%,SO2氧化率低于1. 0%. NO转化率随O2体积分数增加而明显上升,随入口NO体积分数增加而有不同程度下降,但NOx去除量逐渐提高. n(NH3)/n(NO)≤1时,催化剂最优活性约等于各自n(NH3)/n(NO),n(NH3)/n(NO)> 1对催化剂活性没有明显提升.增大空速,催化剂高活性温区变窄,活性呈现不同程度的下降.表征结果表明,在含有SO2和H2O的选择性催化还原法(selective catalytic reduction,SCR)反应后,催化剂比表面积和孔容减小,活性组分流失,且沉积了包含NH4+和SO42-的副反应产物.热再生过程中催化剂延缓硫酸铵盐分解,导致催化剂抗中毒能力变差,活性难以恢复.

不锈钢板负载V_2O_5-WO_3-TiO_2催化剂制备及其催化还原脱硝性能

以溶胶-凝胶法制备的TiO2粉末为载体,偏钒酸铵和水合钨酸铵溶液为浸渍液,采用分步浸渍法制备了V2O5-WO3-TiO2催化剂,以聚乙烯醇-硅溶胶为黏合剂,采用涂覆法将催化剂粘合于经硫酸和钛酸丁酯溶胶处理过的不锈钢板板材表面,获得不锈钢板负载的V2O5-WO3-TiO2催化剂。采用XRD、FT-IR和SEM等表征手段对催化剂进行表征,结果表明,V2O5-WO3-TiO2催化剂可均匀负载于不锈钢板表面。采用氨选择性催化还原氮氧化物法研究了催化剂的脱硝性能,结果表明,在空速8 000 L·(kg·h)-1和反应温度360℃的条件下,NOx脱除率超过92%,且制备的催化剂具有良好的稳定性和耐硫性。

V_2O_5-WO_3-TiO_2催化体系中V的取代对催化性能的影响

采用浸渍法制备了不同比例Fe2O3和50%CuO、50%LaOx分别替代催化体系中V的V2O5-WO3-TiO2催化剂,并对其理化性能和催化活性进行了表征.结果表明:质量分数为9%的WO3能够保证500℃煅烧后的替代和未替代V2O5-WO3-TiO2催化剂具有较高的比表面积和较纯净的锐钛矿晶型,而氧化物替代对比表面积影响不大;当活性氧化物负载量的质量分数不高于3%时,Fe2O3替代对V2O5-WO3-TiO2催化剂的SCR催化性能影响不大;而LaOx替代使得催化剂的低温活性有所提高,同时高活性温度窗口也有一定程度的拓宽;CuO替代催化剂的活性明显低于其他几种催化剂;空气流速增加,Fe2O3替代催化剂的活性首先缓慢下降,在空气流速超过80 000 h-1以后,转化效率急速下降;水蒸气使Fe2O3替代催化剂的温度-转化率曲线向高温方向移动约50℃,但最高活性和高活性温度窗口变化不大.

MoO3改性V2O5/TiO2 SCR催化剂的低温脱硝研究

采用浸渍法制备了低温脱硝MoO3改性V2O5/TiO2催化剂。将催化剂置于固定床反应器中研究其SCR的脱硝性能、抗硫性能。实验模拟烟气条件为NO:500×10-6,NH3:500×10-6,O2:8%,SO2:100×10-6,N2:平衡气体,空速36000h-1。结果表明,浸渍法制备的催化剂具有良好的低温脱硝性能和低温抗硫性能。催化剂的最佳配比为3%V2O5-6%MoO3-91%TiO2(质量分数)。在180~260℃时,脱硝效率为80%~93%,SO2的氧化率小于1%。

纳米负载型V_2O_5-WO_3/TiO_2催化剂碱中毒及再生研究

实验制备了陶瓷颗粒为骨架的纳米级V2O5-WO3/TiO2(C)催化剂。采用浸渍法模拟碱金属中毒,研究了中毒及再生对催化剂脱硝活性的影响,运用XRD、FT-IR、H2-TPR、XPS技术表征分析了碱金属对催化剂的失活作用。实验表明,碱金属能使催化剂活性降低,钾的毒性大于钠。FT-IR结果显示,催化剂以Lewis酸作为活性酸位。H2-TPR、XPS结果表明,钾的加入降低了催化剂的氧化能力,主要影响了催化剂表面的吸附氧。采用单纯的水洗方法并不能提高催化剂活性,而酸洗再生后催化剂在较高反应温度下活性得到较好的恢复。

K2O对V2O5-WO3／TiO2催化剂的中毒作用

实验室制备了V2O5-WO3/TiO2的脱硝催化剂,采用模拟中毒法,在此催化剂上负载碱金属氧化物K2O,通过BET,XRD,SEM等方法对微观结构进行表征.在SCR活性试验台上研究不同含量K2O对催化剂脱硝活性,N2O生成率和SO2氧化率的影响.结果发现:K2O对于催化剂的毒性较强,随着添加量的增大,NO脱除率急剧下降,SO2的氧化率大大提高;较大含量的K2O(nK/nV=1,摩尔比)使催化剂比表面积有所减少,催化剂颗粒发生轻微团聚,微观结构变化不大,但NO的脱除率小于50%(380℃),N2O的生成率和SO2的氧化率均增加;K2O通过与V2O5的活性酸性位结合,使催化剂中有效活性位数量大为降低,导致脱硝活性下降.

蜂窝状V_2O_5-WO_3/TiO_2催化剂脱硝性能研究

实验室制备了蜂窝状V2O5-WO3／TiO2的脱硝催化剂，通过BET、XRD、SEM等方法对微观结构进行表征。在自制SCR活性试验台上测试各种运行工况（温度、空速比等）和烟气组成（[NH3]／[NO]、水蒸气等）对催化剂的脱硝活性、选择性、SO，的氧化率和氨逃逸量的影响。研究结果表明，自制蜂窝状催化剂在空速比小于3500h^-1、NH3／NO在0．9-1．0、温度320-420℃范围内的NO脱除率较高、SO2氧化率和氨逃逸量较低，基本达到工业应用的要求；低含量（低于2％）水蒸气可以提高高温段NO脱除率，而高含量的水蒸气对催化剂NO脱除具有明显的抑制作用，但水蒸气的加入会使NO脱除温度范围拓宽；由于催化剂自身含有较多的硫酸盐，未观察到SO2对脱硝反应有促进作用。

V2O5-WO3/TiO2烟气脱硝催化剂的载体选择

在选择性催化还原试验台上对4种不同TiO2为载体制备的催化剂的脱硝性能进行测试,采用BET、X射线衍射、傅里叶转换红外光谱、扫描电镜-能谱分析、X射线荧光分析和热重分析等技术进行微观表征,并与商业催化剂进行对比。以硫酸法制备的纳米级锐钛型TiO2适合作为选择性催化还原催化剂载体,制备的催化剂脱硝效率高,温度窗口宽,选择性好,其中硫酸盐质量分数为8%～10%时最为有利;以氯化法制备纳米TiO2过程中,生成了V3Ti6O17的聚合物导致NO脱除率较低,因此不适合作为催化剂载体。以工业级TiO2为载体制备的催化剂氨氮比为1.0时,在355～420℃的温度范围内NO脱除率为80%～85%,但由于成本很低,因此可以用于脱硝要求不高的场合。由钛酸丁酯溶胶法制备TiO2为载体制备的SCR催化剂性能不及硫酸法制备的纳米级锐钛型TiO2制备的催化剂,且操作复杂,技术难度大,不适宜推广。

钒和钨负载量对V_2O_5-WO_3/TiO_2表面形态及催化性能的影响

采用浸渍法制备了一系列不同钒和钨负载量的V2O5-WO3/TiO2催化剂样品,对样品NH3选择性催化还原NO性能进行了评价,并用BET、XRD、XPS等手段对催化剂样品的表面形态进行了表征.研究发现,钒的负载量对催化剂的比表面积和催化活性有显著影响,当钒负载量从1%升高到8%时,催化剂比表面积下降了16 m2/g,最高活性温度降低了约100℃.钨起到稳定剂和助剂的双重作用,当钒负载量为1%时,钨负载量从0升高到6%,催化剂比表面积仅下降了3 m2/g,而活性温度窗口向高温和低温各拓宽了约50℃.研究表明钒和钨负载量都能影响催化剂表面的VOx物种,但对催化剂的表面晶型没有明显影响.

商业V_2O_5-WO_3/TiO_2催化剂SCR脱硝过程中PM_(2.5)的排放特性及影响因素研究

针对V2O5-WO3/Ti O2商用催化剂,采用电称低压冲击器(ELPI)、PM10/PM2.5采样器、X-射线衍射(XRD)、场发射扫描电镜-能谱分析(FSEM-EDX)等对SCR烟气脱硝中形成的细颗粒粒径分布、形貌、元素及物相组成进行了测试分析,并研究了烟气组分及反应条件对SCR脱硝系统出口细颗粒物性的影响。结果表明,SCR脱硝过程中会形成不少亚微米级颗粒,主要成分为硫酸铵以及硫酸氢氨,晶型呈块状。细颗粒生成量随反应温度的升高和NH3/NO摩尔比的增加而增加,在脱硝效率较高时,颗粒物形成量也趋于增多;烟气中SO2、H2O和O2浓度的增加均会导致细颗粒物形成量的增加。导致细颗粒物产生的主要原因可归结于催化剂的活性组分对SO2的氧化以及SCR脱硝反应中NH3的逃逸。

Effects of silica additive on the NH_3-SCR activity and thermal stability of a V_2O_5/WO_3-TiO_2 catalyst

V2O5/WO3‐TiO2 and V2O5/WO3‐TiO2‐SiO2 catalysts were prepared by a wetness impregnation method, and both the catalysts were hydrothermally aged at 750℃ in 10 vol%H2O/air for 24 h. The catalysts were evaluated for NOx conversion using NH3 as the reductant. Hydrothermal ageing decreased the NOx conversion of V2O5/WO3‐TiO2 catalyst severely over the entire measured tem‐perature range. Interestingly, the NH3‐SCR activity of the silica‐modified catalyst at 220–480℃ is enhanced after ageing. The catalysts were characterized by X‐ray diffraction, nitrogen adsorption, X‐ray fluorescence, Raman spectroscopy, H2 temperature‐programmed reduction, and NH3 temper‐ature‐programmed desorption. The addition of silica inhibited the phase transition from anatase to rutile titania, growth of TiO2 crystallite size and shrinkage of catalyst surface area. Consequently, the vanadia species remained highly dispersed and the hydrothermal stability of the V2O5/WO3‐TiO2 catalyst was significantly improved.

燃煤烟气中砷对V_2O_5-WO_3/TiO_2 SCR脱硝催化剂性能的影响

通过将商业V_2O_5-WO_3/TiO_2脱硝催化剂暴露于含As_2O_3烟气中,制备了砷中毒催化剂,并运用X射线衍射(XRD)、比表面积(BET)、NH3化学吸附、傅里叶变换红外光谱(FT-IR)、X射线光电子能谱等技术表征分析了砷对催化剂性能的影响,并提出了催化剂砷中毒机理。结果表明,砷对催化剂具有严重的毒害作用,As_2O_3会吸附在催化剂表面,并被催化剂氧化形成As_2O_5覆盖层,减小催化剂比表面积,减少催化剂V活性位,阻止催化剂对NH3的吸附,造成催化剂失活。

Fe_2O_3对V_2O_5-WO_3/TiO_2催化剂表面性质及其性能的影响

催化剂是选择性催化还原(SCR)脱硝技术的核心,研究Fe对钒钛系SCR催化剂脱硝活性及SO_2/SO_3转化率的影响具有重要意义。采用等体积浸渍法制备了不同Fe/V质量比的Fe_2O_3-V2O_5-WO_3/TiO_2催化剂,并进行表征,研究Fe对钒钛系SCR催化剂脱硝活性及SO_2/SO_3转化率的影响,并讨论Fe对于钒钛系SCR催化剂表面性质的影响。结果表明,随着催化剂表面Fe_2O_3含量增加,催化剂的脱硝效率及二氧化硫氧化率均是先上升后下降,当Fe/V质量比为3.0时,催化剂的脱硝效率和二氧化硫氧化率均达到最大值91.78%、1.01%。XPS及H_2-TPR结果表明,随着Fe_2O_3含量增加,催化剂表面钒活性组分的相对含量及V^(4+)/V^(5+)比减小,催化剂表面吸附氧(Oα)浓度增加,催化剂的氧化能力增强。NO-TPD结果表明,随着Fe_2O_3含量增加,催化剂表面吸附NO的能力增强。

纳米负载型V_2O_5-WO_3/TiO_2催化剂碱及碱土金属中毒

实验制备了陶瓷颗粒为骨架的纳米级V2O5-WO3/TiO2(C)催化剂,采用浸渍法模拟碱及碱土金属中毒,研究中毒对催化剂脱硝活性的影响,通过BET、XPS、NH3-TPD技术分析了碱及碱土金属对催化剂的失活作用.结果表明,碱及碱土金属K、Na、Ca能够明显降低催化剂脱硝活性,350℃时,K、Na中毒催化剂活性降低了约30%左右,Ca中毒催化剂降低了20%.碱及碱土金属没有改变催化剂表面物种组成,催化剂活性与催化剂表面强氨气吸附位数量具有线性关系,K、Na、Ca与催化剂表面活性酸位结合,使催化剂中毒.

负载型V_2O_5-WO_3/TiO_2催化剂的砷中毒研究

在实验室模拟了负载型V2O5-WO3/TiO2催化剂砷的中毒。采用催化剂活性测试,NH3-TPD、H2-TPR、XPS技术表征催化剂中毒特性。实验表明,砷中毒使催化剂活性降低明显。NH3-TPD、H2-TPR、XPS表征结果表明,As中毒使催化剂表面酸性降低,催化剂中W、Ti化学形态不受砷中毒的影响,而砷中毒改变了催化剂表面钒的化学形态,认为酸性降低和钒化学形态的改变引起了催化剂的中毒。

V_2O_5-WO_3/TiO_2-SiO_2制备及其选择性催化还原脱硝活性

以硫酸氧钛和硅溶胶为原料,通过共沉淀法制备得到高比表面积的TiO2-SiO2复合氧化物(Ti/Si=1:1atom),并以此复合氧化物为载体用浸渍法制备了V2O5-WO3/TiO2-SiO2脱硝催化剂,考察了催化剂脱硝性能。结果表明,TiO2-SiO2复合氧化物载体出现较多的隧道孔,提高了载体的比表面积,同时Ti元素更易分布在复合氧化物的表面。相比较于纯TiO2,以复合氧化物为载体的V2O5-WO3催化剂表现出更好的活性温度窗口,催化剂表面酸性更强,催化剂对NH3的吸附性能更好,在低的NH3/NO摩尔比情况下(0.8～1.0mol?mol?1),仍然具有较好的脱硝活性,反应温度280～350℃时,脱硝率可达到98%。

碱金属氧化物对V_2O_5-WO_3/TiO_2催化剂脱硝性能的影响

在V2O5-WO3/TiO2催化剂上负载碱金属氧化物(K2O,Na2O),通过BET,XRD和SEM等方法对微观结构进行表征,研究不同含量碱金属氧化物对催化剂脱硝活性、N2O生成率和SO2氧化率的影响.结果发现,较大含量的碱金属对催化剂微观结构有一定影响.碱金属氧化物与催化剂表面V物种的结合生成部分碱金属盐(如KVO3),改变了催化剂的表面结构,使催化剂中有效活性位的数量大大降低,从而导致催化剂活性降低.两种碱金属氧化物对催化剂的毒性顺序为K2O>Na2O.

化学气相沉积制备V_2O_5-WO_3/TiO_2催化剂及表征

以蜂窝堇青石为基体,采用化学气相沉积技术结合浸渍工艺制备出V2O5-WO3/TiO2脱硝催化剂,通过SEM、BET、XRD和EDS完成载体以及催化剂微观结构和成分表征,并利用活性评价装置测试了催化剂NO脱出率。试验结果表明,化学气相沉积技术制备的载体表面为锐钛矿型TiO2,其颗粒聚集成团块状,BET为62.73m2/g,平均孔径为9.8nm。制备的V2O5-WO3/TiO2催化剂孔结构规律与TiO2载体相似,V2O5在TiO2载体上无定形态单层分散,微量V2O5在微区长大成针状,宽度<100nm;在350℃、4000h-1、n(NH3)/n(NO)=1时,催化剂NO脱出率ηNO达到96.7%。

前驱体溶液pH值对V_2O_5-WO_3/TiO_2催化剂的低温NH_3-SCR性能的影响(英文)

采用调节前驱体溶液pH值的方法制备了用于低温NH3-SCR的V2O5-WO3/Ti O2催化剂。通过XPS、Raman光谱、H2-TPR、NH3-TPD、NH3-DRIFT、XRD及物理吸附等手段对催化剂进行了表征分析,并对其脱硝催化活性进行了测试。结果表明,前驱体溶液酸性的增强能够提高催化剂表面聚合态钒物种和V4+(3+)/V5+的比值以及表面酸性,增加活性位数量、降低反应的活化能、提高其脱硝催化性能。因此,通过提高前驱体溶液的酸性,有助于制备出脱硝活性较好的NH3-SCR催化剂。

关于商用SCR(V_2O_5-WO_3/TiO_2)催化剂的再生和回收研究概述

对失活脱硝催化剂进行再生和回收利用方法的研究现状进行总结,主要有酸洗再生、干法再生、改性再生、电泳再生、催化剂的钛白粉回收利用、V和W的回收利用、综合回收等方法,并对以上方法进行总结评价。