Titanium tetrachloride (TiCl4) treatment was employed to TiO2 coating deposited on fluoride-doped tin oxide (FTO) conducting glass and indium oxide doped tin oxide (ITO) conducting glass, respectively. The nano-crysta...Titanium tetrachloride (TiCl4) treatment was employed to TiO2 coating deposited on fluoride-doped tin oxide (FTO) conducting glass and indium oxide doped tin oxide (ITO) conducting glass, respectively. The nano-crystalline TiO2 coating was deposited using a composite powder composed of polyethylene glycol (PEG) and 25 nm TiO2 particles by vacuum cold spraying (VCS) process. A commercial N-719 dye was used to adsorb on the surface of TiO2 coating to prepare TiO2 electrode, which was applied to assemble dye-sensitized solar cell (DSC). The cell performance was measured under simulated solar light at an intensity of 100 mW·cm-2. Results show that with an FTO substrate the DSC composed of a VCS TiO2 electrode untreated by TiCl4 gives a short-circuit current density of 13.1 mA·cm-2 and an open circuit voltage of 0.60 V corresponding to an overall conversion efficiency of 4.4%. It is found that after TiCl4 treatment to the VCS TiO2 electrode with an FTO substrate, the short circuit current density of the cell increases by 31%, the open-circuit voltage increases by 60 mV and a higher conversion yield of 6.5% was obtained. However, when an ITO substrate is used to deposit TiO2 coating by VCS, after TiCl4 treatment, the conversion efficiency of the assembled cell reduces slightly due to corrosion of the conducting layer on the ITO glass by TiCl4.展开更多
The effect of vacuum heat treatment on the microstructure and microhardness of cold-sprayed Cu-4%Cr-2%Nb alloy coating was investigated. The heat treatment was conducted under the temperatures from 250 ℃ to 950 ℃ wi...The effect of vacuum heat treatment on the microstructure and microhardness of cold-sprayed Cu-4%Cr-2%Nb alloy coating was investigated. The heat treatment was conducted under the temperatures from 250 ℃ to 950 ℃ with a step of 100 ℃ for 2 h. It was found that a dense thick Cu-4Cr-2Nb coating could be formed by cold spraying. After heat treatment, a Cr2Nb phase was uniformly distributed in the matrix, which was transferred from the gas-atomized feedstock. A little grain growth of Cr2Nb phase was observed accompanying with the healing-up of the incomplete interfaces between the deposited particles at the elevated temperatures. The coating microhardness increases a little with increasing the temperature to 350 ℃, and then decreases with further increasing temperature up to 950 ℃. This fact can be attributed to the microstructure evolution during the heat treatment.展开更多
This paper introduces working principle and technical features of vacuum filter in emulsion system for tandem cold strip mill.Based on specific cases,this paper analyses and assesses the effect before and after using ...This paper introduces working principle and technical features of vacuum filter in emulsion system for tandem cold strip mill.Based on specific cases,this paper analyses and assesses the effect before and after using the emulsion system with the usage of the vacuum filter for strip mill.Compare with the effect when using the first generation vacuum filter,the emulsion quality is improved significantly by using the second generation vacuum filter,which at the same time ensures steady operation of the rolling mill and surface quality of the mill products. As a result,investment and running costs are lowered,emissions of the waste emulsion are reduced,waste water treatment costs are reduced and so as the environmental pollution.It can be seen the second generation vacuum filter has obvious economic and environmental benefits.Therefor,it suggests that the filter should be used widely in the field of automotive,environmental protection rolling steel and nonferrous metals.展开更多
文摘Titanium tetrachloride (TiCl4) treatment was employed to TiO2 coating deposited on fluoride-doped tin oxide (FTO) conducting glass and indium oxide doped tin oxide (ITO) conducting glass, respectively. The nano-crystalline TiO2 coating was deposited using a composite powder composed of polyethylene glycol (PEG) and 25 nm TiO2 particles by vacuum cold spraying (VCS) process. A commercial N-719 dye was used to adsorb on the surface of TiO2 coating to prepare TiO2 electrode, which was applied to assemble dye-sensitized solar cell (DSC). The cell performance was measured under simulated solar light at an intensity of 100 mW·cm-2. Results show that with an FTO substrate the DSC composed of a VCS TiO2 electrode untreated by TiCl4 gives a short-circuit current density of 13.1 mA·cm-2 and an open circuit voltage of 0.60 V corresponding to an overall conversion efficiency of 4.4%. It is found that after TiCl4 treatment to the VCS TiO2 electrode with an FTO substrate, the short circuit current density of the cell increases by 31%, the open-circuit voltage increases by 60 mV and a higher conversion yield of 6.5% was obtained. However, when an ITO substrate is used to deposit TiO2 coating by VCS, after TiCl4 treatment, the conversion efficiency of the assembled cell reduces slightly due to corrosion of the conducting layer on the ITO glass by TiCl4.
文摘The effect of vacuum heat treatment on the microstructure and microhardness of cold-sprayed Cu-4%Cr-2%Nb alloy coating was investigated. The heat treatment was conducted under the temperatures from 250 ℃ to 950 ℃ with a step of 100 ℃ for 2 h. It was found that a dense thick Cu-4Cr-2Nb coating could be formed by cold spraying. After heat treatment, a Cr2Nb phase was uniformly distributed in the matrix, which was transferred from the gas-atomized feedstock. A little grain growth of Cr2Nb phase was observed accompanying with the healing-up of the incomplete interfaces between the deposited particles at the elevated temperatures. The coating microhardness increases a little with increasing the temperature to 350 ℃, and then decreases with further increasing temperature up to 950 ℃. This fact can be attributed to the microstructure evolution during the heat treatment.
文摘This paper introduces working principle and technical features of vacuum filter in emulsion system for tandem cold strip mill.Based on specific cases,this paper analyses and assesses the effect before and after using the emulsion system with the usage of the vacuum filter for strip mill.Compare with the effect when using the first generation vacuum filter,the emulsion quality is improved significantly by using the second generation vacuum filter,which at the same time ensures steady operation of the rolling mill and surface quality of the mill products. As a result,investment and running costs are lowered,emissions of the waste emulsion are reduced,waste water treatment costs are reduced and so as the environmental pollution.It can be seen the second generation vacuum filter has obvious economic and environmental benefits.Therefor,it suggests that the filter should be used widely in the field of automotive,environmental protection rolling steel and nonferrous metals.