The effect of post-weld heat treatment on the microstructure characterization of electron beam welded(EBW) joints of Ti3Al-Nb was investigated.The results show that the microstructure of the weld is predominantly meta...The effect of post-weld heat treatment on the microstructure characterization of electron beam welded(EBW) joints of Ti3Al-Nb was investigated.The results show that the microstructure of the weld is predominantly metastable,the columnar crystal metastructure of B2 phase.The microstructure morphology of the weld is significantly influenced by the method of the heat treatment.The microstructure of the weld is laminar structure(Widmanstaten structure) consisted of interphase α2 and B2 after post-weld heat treatment of 1000 ℃/2 h.The mechanism of the post-weld heat treatment makes the hardness distribution of joints homogeneous,but makes the whole joint somehow softened.展开更多
A bond coat for thermal barrier coating (TBC), NiCrAlY coating, is subjected to vac-uum heat treatment in order to remove internal stress before ceramic top coat is de-posited. The effect of vacuum heat treatment on t...A bond coat for thermal barrier coating (TBC), NiCrAlY coating, is subjected to vac-uum heat treatment in order to remove internal stress before ceramic top coat is de-posited. The effect of vacuum heat treatment on the oxidation behavior of the sputtered NiCrAlY coating has been investigated. The as-sputtered NiCrAlY coating consists of γ-Ni and b-NiAl phases. After vacuum heat treatment, the sputtered NiCrAlY coating mainly consists of γ'-Ni3Al, β-NiAl, γ-Ni, and trace of α-Al2O3 phases. The isothermal oxidation of sputtered NiCrAlY coating with and without vacuum heat treatment has been performed at 1000℃. It is shown that a-Al2O3 formed during vacuum heat treatment acts as nuclei for the formation of a-Al2O3, and the protective a-Al2O3 scale is formed more rapidly on the vacuum heat treated NiCrAlY coating than that formed on the untreated coating. Also the a-Al2O3 scale has a better adherence to the vacuum heat treated NiCrAlY coating. Therefore the vacuum heat treatment improves the oxidation resistance of sputtered NiCrAlY coating.展开更多
7XXX series aluminium alloys generally present low weldability by fusion welding methods because of the sensitivity to weld solidification cracking, vaporization of strengthening alloys and other defects in the fusion...7XXX series aluminium alloys generally present low weldability by fusion welding methods because of the sensitivity to weld solidification cracking, vaporization of strengthening alloys and other defects in the fusion zone. Friction stir welding(FSW) can be deployed successfully with aluminium alloys. We presented the effect of post-weld heat treatment(PWHT) on the microstructure and mechanical properties of SSM7075 joints. Semi solid plates were butt-welded by FSW at a rotation speed of 1110 r/min, welding speeds of 70 and 110 mm/min. Solution treatment, artificial aging, and T6(solution treatment and artificial aging combined) were applied to the welded joints, each with three samples. It was found that the T6 joints at the speed of 70 mm/min yielded the highest tensile strength of 459.23 MPa. This condition best enhanced the mechanical properties of FSW SSM7075 aluminium alloy joints.展开更多
The purpose of this study was to prepare high-quality Al-Si-Mg-Mn alloy with a good combination of strength and ductility employing the vacuum-assisted high-pressure die cast process. An orthogonal study of heat treat...The purpose of this study was to prepare high-quality Al-Si-Mg-Mn alloy with a good combination of strength and ductility employing the vacuum-assisted high-pressure die cast process. An orthogonal study of heat treatments was conducted to design an optimized T6 heat treatment process for both Al-10%Si-0.3%Mg-Mn and Al-11%Si-0.6%Mg-Mn alloys. The results demonstrate that no obvious blisters and warpage were observed in these two alloys with solid solution treatment. After the optimal T6 heat treatment of 530°C×3 h + 165°C×6 h, Al-11%Si-0.6%Mg-Mn alloy has better mechanical properties, of which tensile strength, yield strength and elongation reached 377.3 MPa, 307.8 MPa and 9%, respectively. The improvement of mechanical properties can be attributed to the high density of needle-like β″(Mg_5Si_6) precipitation after aging treatment and the fine and spherical eutectic Si particles uniformly distributed in the α-Al matrix.展开更多
IN the past five years the process combination of vacuum hardening, respectively vacuum carburizing with high-pressure gas quenching was successfully introduced to the market, especially in the manufacture of gears. I...IN the past five years the process combination of vacuum hardening, respectively vacuum carburizing with high-pressure gas quenching was successfully introduced to the market, especially in the manufacture of gears. In the meantime furnace concepts for various applications are available to the industry. In the following report three plant varieties are introduced, which differ in process flexibility and throughput. This report also explains criteria for the selection of a furnace in view of the existing application requirements. Besides this a short introduction is given into the vacuum carburizing process and the high-pressure gas quenching technology.展开更多
A nonlinear finite element model of vacuum heat treatment process was developed. In this model, influence of many factors, such as nonlinear heat radiation, temperature-dependent thermal physical properties of materia...A nonlinear finite element model of vacuum heat treatment process was developed. In this model, influence of many factors, such as nonlinear heat radiation, temperature-dependent thermal physical properties of material are considered. The temperature field of GH4169 alloy workpiece during vacuum heat treatment process was calculated using finite element software MSC.Marc, and the thermal hysteresis time of the workpiece was predicted. An experiment of vacuum heat treatment of GH4169 superalloy workpiece was carried out to verify the calculation. The experimental results of temperature profile agree well with the simulated results. This work lays a theoretical foundation for optimizing technical parameter of vacuum heat treatment process.展开更多
The effect of vacuum heat treatment on the microstructure and microhardness of cold-sprayed Cu-4%Cr-2%Nb alloy coating was investigated. The heat treatment was conducted under the temperatures from 250 ℃ to 950 ℃ wi...The effect of vacuum heat treatment on the microstructure and microhardness of cold-sprayed Cu-4%Cr-2%Nb alloy coating was investigated. The heat treatment was conducted under the temperatures from 250 ℃ to 950 ℃ with a step of 100 ℃ for 2 h. It was found that a dense thick Cu-4Cr-2Nb coating could be formed by cold spraying. After heat treatment, a Cr2Nb phase was uniformly distributed in the matrix, which was transferred from the gas-atomized feedstock. A little grain growth of Cr2Nb phase was observed accompanying with the healing-up of the incomplete interfaces between the deposited particles at the elevated temperatures. The coating microhardness increases a little with increasing the temperature to 350 ℃, and then decreases with further increasing temperature up to 950 ℃. This fact can be attributed to the microstructure evolution during the heat treatment.展开更多
The electroless Ni-P-SiC composite coatings were prepared and the influence of vacuum heat treatment on its structure and properties was analyzed. The Ni-P-SiC composite coatings were characterized by morphology,struc...The electroless Ni-P-SiC composite coatings were prepared and the influence of vacuum heat treatment on its structure and properties was analyzed. The Ni-P-SiC composite coatings were characterized by morphology,structure and micro-hardness. The morphology and structure of the Ni-P-SiC composite coatings were studied by scanning electron microscopy(SEM) and X-ray diffractometry(XRD),respectively. A great deal of particles incorporation and uniform distribution were found in Ni-P-SiC composite coatings. XRD results show a broad peak of nickel and low intensity SiC peaks present on as-deposited condition. Micro-hardness of as-deposited Ni-P-SiC composite coatings is improved greatly,and the best micro-hardness is obtained after heat treatment in a high vacuum at 400 ℃ .展开更多
The electron beam local post-weld heat treatment (EBLPWHT) is a rather new method that provides the advantages of high precision, flexibility and efficiency, energy saving and higher productivity. This paper studies t...The electron beam local post-weld heat treatment (EBLPWHT) is a rather new method that provides the advantages of high precision, flexibility and efficiency, energy saving and higher productivity. This paper studies the effect of two post-weld heat treatment processes on the microstructure, mechanical properties and fracture toughness of an electron beam welded joints in 30CrMnSiNi2A steel. EBLPWHT, in a vacuum chamber, immediately after welding and a traditional furnace whole post-weld heat treatment (FWPWHT) were compared. The experimental results show that, after EBLPWHT treatment, the main microstructure of weld was changed from coarse acicular martensite into lath martensite, HAZ was changed from lath martensite, bainite into lower bainite, and base metal was changed from ferrite and pearlite into upper bainite and residual austenite. The microstructures of different zones of joints in FWPWHT condition were tempered sorbite. The properties of welded joints can be improved by the EBLPWHT in some extent, and especially largely for the fracture toughness of welded joints. However the value of fracture toughness of base metal is comparatively low, so appropriate heat treatment parameters should be explored in the future.展开更多
The influence of temperature during post-weld heat treatment on the microstructure and properties of KMN steel joints was investigated. The results reveal that after heat treatment, the martensite transformed to tempe...The influence of temperature during post-weld heat treatment on the microstructure and properties of KMN steel joints was investigated. The results reveal that after heat treatment, the martensite transformed to tempered sorbite, causing the softening of the resultant joints. XRD test shows that the residual austenite content decreased obviously when the joint was heattreated at 550 ℃ and 580 ℃, which degraded the impact toughness of heat-affected zone ( HAZ). When the heat treatment temperature increased further, the dispersion strengthening from the precipitation of alloying elements improved the impact toughness of HAZ. The aggregation and coarsening of carbide also contributed to the improvement of impact toughness of HAZ.展开更多
The distributions of temperature and residual stresses in thin plates of BT20titanium alloy are numerically analyzed by three-dimensional finite element software duringelectron beam welding and electron beam local pos...The distributions of temperature and residual stresses in thin plates of BT20titanium alloy are numerically analyzed by three-dimensional finite element software duringelectron beam welding and electron beam local post-weld heat treatment (EBLPWHT). Combined withnumerical calculating results, the effects of different EBLPWHT mode and parameters, including heattreating position, heating width and heating time, on the distribution of welding residual stressesare analyzed. The results show that, the residual tensile stresses in weld center can be largelydecreased when the weld is heat treated at back preface of the plate. The numerical results alsoindicated that the magnitude of the residual longitudinal stresses of the weld and the zone vicinityof the weld is decreased, and the range of the residual longitudinal stresses is increased alongwith the increase of heating width and heating time.展开更多
9Cr-1Mo ferritic steels have been used in the conventional power generation plants due to their excellent creep resistance. However, one of the main obstacles in welding 9Cr-1Mo steels is the formation of undesirable ...9Cr-1Mo ferritic steels have been used in the conventional power generation plants due to their excellent creep resistance. However, one of the main obstacles in welding 9Cr-1Mo steels is the formation of undesirable coarse columnar grains in weld metal whieh ean severely compromise the toughness. A new post-weld heat treatment (PWHT) is developed in the present work. Unlike the conventional processes in which the post-weld heat treatment is carried out below Ac1 , the use of temperatures above the Ac1 of 9Cr-1Mo alloy is considered. The new PWHT at a temperature above Ac1 improves the toughness of 9Cr-1Mo weld metals effectively. The improvement in toughness is mainly due to refinement and homogenization of mierostruetures. Key words展开更多
X-ray diffraction was utilized to measure the residual stress of 45 mm UNS N08810 plates after post-weld heat treatment at temperatures of 680℃ and 900℃, which showed reductions of 86.9% and 71.6% in the residual st...X-ray diffraction was utilized to measure the residual stress of 45 mm UNS N08810 plates after post-weld heat treatment at temperatures of 680℃ and 900℃, which showed reductions of 86.9% and 71.6% in the residual stress, respectively. This indicates that post-weld heat treatment can play a significant role in reducing residual stress, while no significant effects on tensile stress and micro-hardness of the welding joint were observed after treatment.展开更多
The continuous constructive challenge to improve the functionality and efficiency of components always results in higher demands on production engineering, against the background of the generally increasing cost press...The continuous constructive challenge to improve the functionality and efficiency of components always results in higher demands on production engineering, against the background of the generally increasing cost pressure. In many cases, you will just succeed in producing competitive and innovative products by combining and coupling of different procedures to an independent (hybrid) technology. The use of hybrid procedures for metal joining and heat treatment of metallic materials finds more and more industrial fields of application. Modern vacuum lines with integrated pressurized gas quenching are considered high-performance and flexible means of production for brazing and heat treatment tasks as well in the turbine industry as in the mould making and tool manufacturing industry. In doing so, the heat treatment is coupled with the brazing cycle in a combined process so that the brazing temperatures and soak times are adapted to the necessary temperatures and times for solution heat treatment and austeniting. This user-oriented article describes on the one hand examples of brazing of turbine components, but above all the practical experience from the plastics processing industry, where the requirement for a high-efficient cooling of injection moulding dies gains more and more importance. The combined procedure "Vacuum Brazing and Hardening" offers plenty of possibilities to produce mould inserts with an efficient tempering system in an economic way.展开更多
Onion-like Fullerenes were produced at high-temperature in vacuum. The morphology of the carbon nano onion-like fullerenes was examined and characterized by high-resolution transmission electron microscopy (HRTEM). It...Onion-like Fullerenes were produced at high-temperature in vacuum. The morphology of the carbon nano onion-like fullerenes was examined and characterized by high-resolution transmission electron microscopy (HRTEM). It can be seen that the nano-sized, onion-like fullerenes possess high degree of graphization. The results suggested that the catalyst is the main factor affecting the size and yield of the fullerenes. The method is very promising for simple mass production.展开更多
The vacuum heat treatment with overpressure gas quenching is more and more accepted due to considerable advantages compared to the traditional oil and salt bath processes. Continuous further developments and new conce...The vacuum heat treatment with overpressure gas quenching is more and more accepted due to considerable advantages compared to the traditional oil and salt bath processes. Continuous further developments and new concepts like multi-directional cooling systems, a separate quenching chamber and "sub zero" systems lead towards an oxidation free and low distortion vacuum heat treatment for a broad range of parts and materials. Short and energy saving processes guarantee a high economic efficiency and environmental compatibility. The "sub zero" system which is integrated into the standard vacuum furnace achieves a heat treatment result with a high conversion of retained austenite in fully automatic hardening and tempering processes.展开更多
An effective vacuum melting technique based on the improved vacuum degassing technique was used to produce thick-walled seamless pipes of 9Cr-1Mo-V-Nb-N martensitic heat resistant steels in order to reduce the content...An effective vacuum melting technique based on the improved vacuum degassing technique was used to produce thick-walled seamless pipes of 9Cr-1Mo-V-Nb-N martensitic heat resistant steels in order to reduce the contents of harmful impurity such as oxygen, phosphorus. Then the pipe was heat treated by using optimized process technique. Both static and dynamic mechanical properties at room temperature and 566℃ were measured respectively and evaluated by means of comprehensive analysis of standard deviation and statistic test. The results show that the comprehensive mechanical properties of this pipe are much better than those of pipes untreated with the improved vacuum degassing technique and heat-treated by using original heat-treatment process and almost the same as those of imported P91 thick-walled seamless steel pipe.展开更多
文摘The effect of post-weld heat treatment on the microstructure characterization of electron beam welded(EBW) joints of Ti3Al-Nb was investigated.The results show that the microstructure of the weld is predominantly metastable,the columnar crystal metastructure of B2 phase.The microstructure morphology of the weld is significantly influenced by the method of the heat treatment.The microstructure of the weld is laminar structure(Widmanstaten structure) consisted of interphase α2 and B2 after post-weld heat treatment of 1000 ℃/2 h.The mechanism of the post-weld heat treatment makes the hardness distribution of joints homogeneous,but makes the whole joint somehow softened.
基金The authors thank Prof.H. Y. Lou for sputtering NiCrAlY coating.
文摘A bond coat for thermal barrier coating (TBC), NiCrAlY coating, is subjected to vac-uum heat treatment in order to remove internal stress before ceramic top coat is de-posited. The effect of vacuum heat treatment on the oxidation behavior of the sputtered NiCrAlY coating has been investigated. The as-sputtered NiCrAlY coating consists of γ-Ni and b-NiAl phases. After vacuum heat treatment, the sputtered NiCrAlY coating mainly consists of γ'-Ni3Al, β-NiAl, γ-Ni, and trace of α-Al2O3 phases. The isothermal oxidation of sputtered NiCrAlY coating with and without vacuum heat treatment has been performed at 1000℃. It is shown that a-Al2O3 formed during vacuum heat treatment acts as nuclei for the formation of a-Al2O3, and the protective a-Al2O3 scale is formed more rapidly on the vacuum heat treated NiCrAlY coating than that formed on the untreated coating. Also the a-Al2O3 scale has a better adherence to the vacuum heat treated NiCrAlY coating. Therefore the vacuum heat treatment improves the oxidation resistance of sputtered NiCrAlY coating.
基金Partially Funded by National Research Universities(NRU)(ENG 5805855)Faculty of Engineering,Prince of Songkla University,Hatyai Songkhla,Thailand
文摘7XXX series aluminium alloys generally present low weldability by fusion welding methods because of the sensitivity to weld solidification cracking, vaporization of strengthening alloys and other defects in the fusion zone. Friction stir welding(FSW) can be deployed successfully with aluminium alloys. We presented the effect of post-weld heat treatment(PWHT) on the microstructure and mechanical properties of SSM7075 joints. Semi solid plates were butt-welded by FSW at a rotation speed of 1110 r/min, welding speeds of 70 and 110 mm/min. Solution treatment, artificial aging, and T6(solution treatment and artificial aging combined) were applied to the welded joints, each with three samples. It was found that the T6 joints at the speed of 70 mm/min yielded the highest tensile strength of 459.23 MPa. This condition best enhanced the mechanical properties of FSW SSM7075 aluminium alloy joints.
基金financially supported by the Jiangsu province transformation of scientific and technological achievements program(BA2015041)the Jiangsu key laboratory for advanced metallic materials(BM2007204)
文摘The purpose of this study was to prepare high-quality Al-Si-Mg-Mn alloy with a good combination of strength and ductility employing the vacuum-assisted high-pressure die cast process. An orthogonal study of heat treatments was conducted to design an optimized T6 heat treatment process for both Al-10%Si-0.3%Mg-Mn and Al-11%Si-0.6%Mg-Mn alloys. The results demonstrate that no obvious blisters and warpage were observed in these two alloys with solid solution treatment. After the optimal T6 heat treatment of 530°C×3 h + 165°C×6 h, Al-11%Si-0.6%Mg-Mn alloy has better mechanical properties, of which tensile strength, yield strength and elongation reached 377.3 MPa, 307.8 MPa and 9%, respectively. The improvement of mechanical properties can be attributed to the high density of needle-like β″(Mg_5Si_6) precipitation after aging treatment and the fine and spherical eutectic Si particles uniformly distributed in the α-Al matrix.
文摘IN the past five years the process combination of vacuum hardening, respectively vacuum carburizing with high-pressure gas quenching was successfully introduced to the market, especially in the manufacture of gears. In the meantime furnace concepts for various applications are available to the industry. In the following report three plant varieties are introduced, which differ in process flexibility and throughput. This report also explains criteria for the selection of a furnace in view of the existing application requirements. Besides this a short introduction is given into the vacuum carburizing process and the high-pressure gas quenching technology.
文摘A nonlinear finite element model of vacuum heat treatment process was developed. In this model, influence of many factors, such as nonlinear heat radiation, temperature-dependent thermal physical properties of material are considered. The temperature field of GH4169 alloy workpiece during vacuum heat treatment process was calculated using finite element software MSC.Marc, and the thermal hysteresis time of the workpiece was predicted. An experiment of vacuum heat treatment of GH4169 superalloy workpiece was carried out to verify the calculation. The experimental results of temperature profile agree well with the simulated results. This work lays a theoretical foundation for optimizing technical parameter of vacuum heat treatment process.
文摘The effect of vacuum heat treatment on the microstructure and microhardness of cold-sprayed Cu-4%Cr-2%Nb alloy coating was investigated. The heat treatment was conducted under the temperatures from 250 ℃ to 950 ℃ with a step of 100 ℃ for 2 h. It was found that a dense thick Cu-4Cr-2Nb coating could be formed by cold spraying. After heat treatment, a Cr2Nb phase was uniformly distributed in the matrix, which was transferred from the gas-atomized feedstock. A little grain growth of Cr2Nb phase was observed accompanying with the healing-up of the incomplete interfaces between the deposited particles at the elevated temperatures. The coating microhardness increases a little with increasing the temperature to 350 ℃, and then decreases with further increasing temperature up to 950 ℃. This fact can be attributed to the microstructure evolution during the heat treatment.
基金Projects(05B008) supported by Scientific Research Fund of Hunan Provincial Education Departmentproject(104014) supported by Fok Ying Tong Education Foundation of Ministry of Education
文摘The electroless Ni-P-SiC composite coatings were prepared and the influence of vacuum heat treatment on its structure and properties was analyzed. The Ni-P-SiC composite coatings were characterized by morphology,structure and micro-hardness. The morphology and structure of the Ni-P-SiC composite coatings were studied by scanning electron microscopy(SEM) and X-ray diffractometry(XRD),respectively. A great deal of particles incorporation and uniform distribution were found in Ni-P-SiC composite coatings. XRD results show a broad peak of nickel and low intensity SiC peaks present on as-deposited condition. Micro-hardness of as-deposited Ni-P-SiC composite coatings is improved greatly,and the best micro-hardness is obtained after heat treatment in a high vacuum at 400 ℃ .
文摘The electron beam local post-weld heat treatment (EBLPWHT) is a rather new method that provides the advantages of high precision, flexibility and efficiency, energy saving and higher productivity. This paper studies the effect of two post-weld heat treatment processes on the microstructure, mechanical properties and fracture toughness of an electron beam welded joints in 30CrMnSiNi2A steel. EBLPWHT, in a vacuum chamber, immediately after welding and a traditional furnace whole post-weld heat treatment (FWPWHT) were compared. The experimental results show that, after EBLPWHT treatment, the main microstructure of weld was changed from coarse acicular martensite into lath martensite, HAZ was changed from lath martensite, bainite into lower bainite, and base metal was changed from ferrite and pearlite into upper bainite and residual austenite. The microstructures of different zones of joints in FWPWHT condition were tempered sorbite. The properties of welded joints can be improved by the EBLPWHT in some extent, and especially largely for the fracture toughness of welded joints. However the value of fracture toughness of base metal is comparatively low, so appropriate heat treatment parameters should be explored in the future.
文摘The influence of temperature during post-weld heat treatment on the microstructure and properties of KMN steel joints was investigated. The results reveal that after heat treatment, the martensite transformed to tempered sorbite, causing the softening of the resultant joints. XRD test shows that the residual austenite content decreased obviously when the joint was heattreated at 550 ℃ and 580 ℃, which degraded the impact toughness of heat-affected zone ( HAZ). When the heat treatment temperature increased further, the dispersion strengthening from the precipitation of alloying elements improved the impact toughness of HAZ. The aggregation and coarsening of carbide also contributed to the improvement of impact toughness of HAZ.
基金This project is supported by Foundation of National Defense Technology Key Laboratory, China (No.99JS50.3.2JW1402).
文摘The distributions of temperature and residual stresses in thin plates of BT20titanium alloy are numerically analyzed by three-dimensional finite element software duringelectron beam welding and electron beam local post-weld heat treatment (EBLPWHT). Combined withnumerical calculating results, the effects of different EBLPWHT mode and parameters, including heattreating position, heating width and heating time, on the distribution of welding residual stressesare analyzed. The results show that, the residual tensile stresses in weld center can be largelydecreased when the weld is heat treated at back preface of the plate. The numerical results alsoindicated that the magnitude of the residual longitudinal stresses of the weld and the zone vicinityof the weld is decreased, and the range of the residual longitudinal stresses is increased alongwith the increase of heating width and heating time.
文摘9Cr-1Mo ferritic steels have been used in the conventional power generation plants due to their excellent creep resistance. However, one of the main obstacles in welding 9Cr-1Mo steels is the formation of undesirable coarse columnar grains in weld metal whieh ean severely compromise the toughness. A new post-weld heat treatment (PWHT) is developed in the present work. Unlike the conventional processes in which the post-weld heat treatment is carried out below Ac1 , the use of temperatures above the Ac1 of 9Cr-1Mo alloy is considered. The new PWHT at a temperature above Ac1 improves the toughness of 9Cr-1Mo weld metals effectively. The improvement in toughness is mainly due to refinement and homogenization of mierostruetures. Key words
文摘X-ray diffraction was utilized to measure the residual stress of 45 mm UNS N08810 plates after post-weld heat treatment at temperatures of 680℃ and 900℃, which showed reductions of 86.9% and 71.6% in the residual stress, respectively. This indicates that post-weld heat treatment can play a significant role in reducing residual stress, while no significant effects on tensile stress and micro-hardness of the welding joint were observed after treatment.
文摘The continuous constructive challenge to improve the functionality and efficiency of components always results in higher demands on production engineering, against the background of the generally increasing cost pressure. In many cases, you will just succeed in producing competitive and innovative products by combining and coupling of different procedures to an independent (hybrid) technology. The use of hybrid procedures for metal joining and heat treatment of metallic materials finds more and more industrial fields of application. Modern vacuum lines with integrated pressurized gas quenching are considered high-performance and flexible means of production for brazing and heat treatment tasks as well in the turbine industry as in the mould making and tool manufacturing industry. In doing so, the heat treatment is coupled with the brazing cycle in a combined process so that the brazing temperatures and soak times are adapted to the necessary temperatures and times for solution heat treatment and austeniting. This user-oriented article describes on the one hand examples of brazing of turbine components, but above all the practical experience from the plastics processing industry, where the requirement for a high-efficient cooling of injection moulding dies gains more and more importance. The combined procedure "Vacuum Brazing and Hardening" offers plenty of possibilities to produce mould inserts with an efficient tempering system in an economic way.
基金supported by National Natural Science Foundation(59871032,90306014)National Excellent Youth Foundation(50025103).
文摘Onion-like Fullerenes were produced at high-temperature in vacuum. The morphology of the carbon nano onion-like fullerenes was examined and characterized by high-resolution transmission electron microscopy (HRTEM). It can be seen that the nano-sized, onion-like fullerenes possess high degree of graphization. The results suggested that the catalyst is the main factor affecting the size and yield of the fullerenes. The method is very promising for simple mass production.
文摘The vacuum heat treatment with overpressure gas quenching is more and more accepted due to considerable advantages compared to the traditional oil and salt bath processes. Continuous further developments and new concepts like multi-directional cooling systems, a separate quenching chamber and "sub zero" systems lead towards an oxidation free and low distortion vacuum heat treatment for a broad range of parts and materials. Short and energy saving processes guarantee a high economic efficiency and environmental compatibility. The "sub zero" system which is integrated into the standard vacuum furnace achieves a heat treatment result with a high conversion of retained austenite in fully automatic hardening and tempering processes.
文摘An effective vacuum melting technique based on the improved vacuum degassing technique was used to produce thick-walled seamless pipes of 9Cr-1Mo-V-Nb-N martensitic heat resistant steels in order to reduce the contents of harmful impurity such as oxygen, phosphorus. Then the pipe was heat treated by using optimized process technique. Both static and dynamic mechanical properties at room temperature and 566℃ were measured respectively and evaluated by means of comprehensive analysis of standard deviation and statistic test. The results show that the comprehensive mechanical properties of this pipe are much better than those of pipes untreated with the improved vacuum degassing technique and heat-treated by using original heat-treatment process and almost the same as those of imported P91 thick-walled seamless steel pipe.