纳米复合W-La_2O_3材料的表面行为与热发射性能

采用“液液掺杂—冷冻干燥—两段还原—SPS”法制备了纳米W La2O3发射材料,利用原位俄射电子能谱分析技术研究了高温过程中发射材料的表层元素含量以及纵向元素分布,并采用自行研制的微机控制全自动电子发射测量装置测试了材料发射性能。研究表明:纳米W La2O3发射材料的有效逸出功为2.92eV,1773K下零场发射电流密度为2.52A/cm2;加热过程中,材料体内以La2O3形式存在的镧、氧向表面扩散,在表层10nm的地方出现La、O富集区,并形成了超额La,对电子发射起积极作用。

Synthesis of Y_2O_3 particle enhanced Ni/TiC composite on TC4 Ti alloy by laser cladding

A Y2O3 particle enhanced Ni/TiC composite coating was fabricated in-situ on a TC4 Ti alloy by laser surface cladding. The phase component, microstructure, composition distribution and properties of the composite layer were investigated. The composite layer has graded microstructures and compositions, due to the fast melting followed by rapid solidification and cooling during laser cladding. The TiC powders are completely dissolved into the melted layer during melting and segregated as fine dendrites when solidified. The size of TiC dendrites decreases with increasing depth. Y2O3 fine particles distribute in the whole clad layer. The Y2O3 particle enhanced Ni/TiC composite layer has a quite uniform hardness along depth with a maximum value of HV1380, which is 4 times higher than the initial hardness. The wear resistance of the Ti alloy is significantly improved after laser cladding due to the high hardness of the composite coating.

纳米晶W-La_2O_3电极材料的电弧特性

采用高能球磨和真空热压烧结工艺制备出块体纳米晶W La2 O3 电极材料 ,研究了不同La2 O3 含量对纳米晶钨电极材料电性能的影响 ,同时用扫描电镜和能谱仪测定了燃弧后电极尖端La的分布及显微组织。结果表明 :纳米晶W La2 O3 电极的电性能优于传统的粉末冶金粗晶电极。当La2 O3 含量在 6 %～ 8%时 ,其热电子发射能力和稳定性最好。

Electrochemical codeposition of Mg-Li-Gd alloys from LiCl-KCl-MgCl_2-Gd_2O_3 melts

Mg-Li-Gd alloys were prepared by electrochemical codeposition from LiCl-KCl-MgCl 2 -Gd 2 O 3 melts on molybdenum electrode with constant current density at 823 and 973 K. The microstructure of the Mg-Li-Gd alloys was analyzed by X-ray diffraction （XRD）, optical microscopy （OM） and scanning electron microscopy （SEM）. The results show that magnesium and gadolinium deposit mainly in the first 30 min, and the alloy obtained contains 96.53% Mg, 0.27% Li and 3.20% Gd （mass fraction）. Then, the reduction of lithium ions occurs quickly. The composition of alloy can be adjusted by controlling electrolysis time or Gd 2 O 3 concentration in LiCl-KCl melts. With the addition of Gd into Mg-Li alloys, the corrosion resistance of the alloys is enhanced. XRD results suggest that Mg 3 Gd and Mg 2 Gd can be formed in Mg-Li-Gd alloys. The distribution of Gd element in Mg-Li-Gd alloys indicates that Gd element mainly distributes at the grain boundaries of Mg-Li-Gd alloys.

纳米晶W-La_2O_3电极材料的形成与烧结行为

通过高能球磨将一定成分的W,La2O3粉研磨成纳米粉,在真空热压炉中将其烧结为块体的纳米晶电极材料。利用X射线衍射仪(XRD)、透射电镜(TEM)和扫描电镜(SEM)等手段分析晶粒的变化情况。结果表明,烧结的致密化主要在于纳米颗粒的重排,而不是传统的扩散;烧结过程中出现晶粒长大现象,但长大有限;机械研磨产生的内应变、某些杂质元素的存在等对烧结有促进作用。

W-La_2O_3电极材料的研究进展

介绍了电极材料的应用和性能要求。总结了W -La2 O3电极材料的制备方法、使用性能、作用机理和研究中存在的问题。阐述了几种新近发展起来的W -La2 O3电极材料 ,并提出了现阶段W -La2 O3电极材料研究进展与方向。

Non-isothermal reduction kinetics of Fe_2O_3-NiO composites for formation of Fe-Ni alloy using carbon monoxide

The non-isothermal reduction kinetics and mechanism of Fe2O3-NiO composites with different Fe2O3-NiO compacts using carbon monoxide as reductant were investigated. The results show that the reduction degree increases rapidly with increasing the content of NiO, and the presence of NiO also improves the reduction rate of iron oxides. It is found that NiO is preferentially reduced at the beginning of the reactions, and then the metallic Ni acts as a catalyst promoting the reduction rate of iron oxides. It is also observed that the increase of the Ni O content enhances the formation of awaruite(FeNi3) but decreases the percentage of kamacite(Fe,Ni) and taenite(Fe,Ni). The particle size of the materials tends to be uniform during the reduction process due to the presence of metallic nickel, metallic iron and the formation of Fe-Ni alloy. The concentration of CO in the product gas is greater than that of CO2 at the beginning of the reaction and then slows down. The fastest reduction rate of Fe2O3-NiO composites with CO appears at 400-500 °C, and nucleation growth model can be used to elucidate the reduction mechanism. Nucleation growth process is found to be the rate controlling step when the temperature is lower than 1000 °C.

Effects of Y_2O_3 on the microstructure and wear resistance of cobalt-based alloy coatings deposited by plasma transferred arc process

Cobalt-based alloys with different Y2O3 contents were deposited on Q235A-carbon steel using plasma transferred arc （PTA） welding machine. The effect of Y2O3 on the microstructure and wear resistance properties of the cobait-based alloys were investigated using an optical microscope, a scanning electron microscope （SEM）, X-ray diffraction （XRD）, and transmission electron microscopy （TEM）. It was found that a cobalt-based solid solution with a face-centered cubic crystal structure was presented accompanied by the secondary phase M7C3 with a hexagonal crystal structure in the Y2O3-free cobalt-based alloy coating. Several stacking faults exist in the cobalt-based solid solution. The addition of Y2O3 leads to the existence of the Y2O3 phase in the Y2O3-modified coatings. Though stacking fault exists in the Y2O3-modified coatings, its density increases. The addition of Y2O3 can refine the microstructure and can increase the wear resistance properties when its contents are less than or equal to 0.8 wt.%. However, further increase of its contents will lead to the agglomeration of undissolved Y2O3 particles at the γ-Co grain boundary, and will lead to a coarse microstructure and lower wear resistance properties.

Microstructure and compression properties of fine Al2O3 particles dispersion strengthened molybdenum alloy

The Mo alloys reinforced by Al2O3 particles were fabricated by hydrothermal synthesis and powder metallurgy. The microstructures of Mo-Al2O3 alloys were studied by using XRD, SEM and TEM. The results show that Al2O3 particles, existing as a stable hexagonal phase(α-Al2O3), are uniformly dispersed in Mo matrix. The ultrafine α-Al2O3 particles remarkably refine grain size and increase dislocation density of Mo alloys. Moreover, a good interfacial bonding zone between α-Al2O3 and Mo grain is obtained. The crystallographic orientations of the interface of the Al2O3 particles and Mo matrix are [111]a-Al2O3//[111]Mo and(112)a-Al2O3//(0 11)Mo. Due to the effect of secondary phase and dislocation strengthening, the yield strength of Mo-2.0 vol.%Al2O3 alloy annealed at 1200 ℃ is approximately 56.0% higher than that of pure Mo. The results confirm that the addition of Al2O3 particles is a promising method to improve the mechanical properties of Mo alloys.

Individual and synergistic effect of gamma alumina（γ-Al2O3） and strontium on microstructure and mechanical properties of Al-20Si alloy

An optimized combination of gamma alumina (4 wt.%) and strontium (0.1 wt.%) was incorporated in cast Al-20Si alloy to obtain fine form of silicon. During casting process, the amount of γ-Al2O3 was varied from 0.5.6 wt.% to refine primary Si and Sr was varied from 0.05.0.1 wt.% to modify eutectic Si. The results showed that the average size of primary Si is 24 μm for addition of 4 wt.%γ-Al2O3 to the alloy whereas 0.1 wt.% Sr resulted in sphericity of eutectic Si to ~0.6 and average length of ~1.2 μm. The thermal analysis revealed that γ-Al2O3 can act as potential heterogeneous nucleation sites. Moreover, simultaneous addition of γ-Al2O3 and Sr does not poison γ-Al2O3 particles and inhibit their nucleation efficiency as in the case of combined addition of phosphorous and strontium to Al-20Si alloy. Therefore, it was concluded that enhanced tensile strength, i.e., ultimate tensile strength (increase by 20%) and elongation (increase by 23%) in Al-20Si.4γ-Al2O3.0.1wt.%Sr alloy as compared to as-cast Al.20Si alloy can be attributed to refinement of primary Si, modification of eutectic Si and the presence of α(Al) in the alloy as evident from eutectic shift.

Effect of nano-sized Al2O3 reinforcing particles on uniaxial and high cycle fatigue behaviors of hot-forged AZ31B magnesium alloy

The effect of hot-forging process was investigated on microstructural and mechanical properties of AZ31 B alloy and AZ31 B/1.5 vol.%Al2 O3 nanocomposite under static and cycling loading. The as-cast alloy and composite were firstly subjected to a homogenization heat treatment at 450 ℃ and then an open-die forging at 450 ℃. The results indicated that the presence of reinforcing particles led to grain refinement and improvement of dynamic recrystallization. The forging process was more effective to eliminate the porosity in the cast alloy workpiece. Microhardness of the forged composite was increased by up to 80% and 16%, in comparison with those of the cast and forged alloy samples, respectively. Ultimate tensile strength and maximum tensile strain of the composite were improved by up to 45% and 23%, compared with those of the forged alloy in similar regions. These enhancements were respectively 50% and 37% in the compression test. The composite exhibited a fatigue life improvement in the region with low applied strain;however, a degradation was observed in the high applied strain region. Unlike AZ31 B samples, tensile, compressive and high cycle fatigue behaviors of the composite showed less sensitivity to the applied strain, which can be attributed to the amount of porosity in the samples before and after the hot-forging.

Effect of SrO Content on Structure,Thermal Properties and Chemical Stability of Bi2O3-B2O3-ZnO-SrO Low-melting Glass for Si-Al Alloy Package

The 40Bi2O3-30B2O3-(30-x)ZnO-xSrO (x=0-15mol%,BBZSr) glass system was prepared by the conventional melt quenching method.The effect of SrO addition on structure,thermal properties,chemical stability and sealing performance of BBZSr glass were investigated thoroughly.The experimental results show that the total proportions of [BO3] group and [BO4] group decrease and the vibrations of [BiO3] group and [BiO6] group become weaker with the increase of SrO addition content,suggesting the glass network structure is strengthened owing to the SrO addition.Hence,both the thermal and chemical stability were significantly improved as the SrO content was increased.When the SrO content increased from 0 to 15mol%,the glass transition temperature and softening temperature slightly increased from 380 to 388 ℃ and from 392.7 to 402.2 ℃,respectively,meanwhile the coefficient of thermal expansion also increased from 10.49×10^-6 to 11.16×10^-6/℃ (30-300 ℃).The BBZSr glass with 15mol% SrO exhibited excellent comprehensive properties with low glass transition temperature(384.9 ℃),low softening temperature(400.3 ℃),high coefficient of thermal expansion (11.14×10^-6 ℃,30-300 ℃),good thermal and chemical stability.Besides,the glass had the good wetting behavior and sealing performance for Al-50%Si alloy.

Effects of Yttrium Ion on Formation Mechanism of ZrO_2-Y_2O_3 Ceramic Coatings Formed by Plasma Electrolytic Oxidation on Al-12Si Alloy

ZrO2-Y2O3 ceramic coating was produced by plasma electrolytic oxidation （PEO） on ZAlSil2Cu3Ni2 alloy. The microstructure and phase composition of the coating were investigated by SEM and XRD.： The results show that adding an appropriate amount of yttrium ion can improve the growing rate of ceramic coating at different oxidation stages and decrease arc voltage. The thickness of ZrO2-Y2O3 coating is 16 μn thicker than that of ZrO2 coating and the maximum oxidation rate improves by 0.6 μm/min. In addition, the arc voltage decreases from 227 to 172 V. It can be seen that the rate of oxidation firstly increases to some extent and then decreases with the content of yttrium ion increasing. The growth rate reaches the maximum while the content of yttrium ion is 0.05 g-L-1The maximum thickness is 90 μm.Compared to ZrO2 coating, the micropores of ZrO2-Y2O3 coating are less and the ceramic layer is repeatedly deposited by ZrO2 and Y2O3 ceramic particles. Meanwhile, the binding force between coating and substrate is better and the coating is uniform and compact. The ceramic layer is mainly composed of c-Y0.15Zr0.85O1.93□0.07, m-ZrO2, α-Al2O3, ,γ-Al2O3 and Y2O3. It is indicated that ZrO2 has beert fully stabilized by yttrium ion through the formation of solid solution.

Distribution and segregation of solute in Al_2O_3 short fiber reinforced Al-5%Cu alloy containing La by squeeze casting

Al2O3 short fiber reinforced La-bearing Al-5%Cu alloy was fabricated by squeeze casting, and the solidified structure and the solute segregation during alloy solidification were studied. The results indicated that La has been enriched near the interface which is favorable to improve the wettability between the fiber and At alloy, but the RE-rich phase was not formed at the interface. At the end of the solidification of the composites, the change of the solute in the surplus liquid phase results in the type of matrix alloy being changed because of the selective crystallization, and the segregation at the interface is finally formed. There is no special influence by La on the Cu segregation in the matrix alloy.

Microstructure Characteristics of Interaction Layer of Zn-Al Eutectic Alloy with Al_2O_3p/6061Al Composites

The interaction between Zn-AI eutectic alloy and Al203p/6061AI composites in the vacuum furnace was investigated. Great attention has been paid to the elements diffusion, the microstructure and formation of the interface between Zn-AI eutectic alloy and Al2O3p/6061AI composites. Experimental results show that Zn-AI eutectic alloy has a good wetting ability to Al2O3p/6061 Al composites and the wetting angle decreases with increasing the temperature in vacuum. After the interaction, an interaction layer forms between Zn-AI alloy and Al2O3p/6061 Al composites. The phases in the interaction layer mainly consist of α-AI(Zn), Al2O3 and CuZn5 resulted from the diffusion of elements from the Zn-AI alloy. Several porosities distribute in the region near the interface of the Zn-AI alloy/interaction layer. The amount of shrinkage voids in the interacting layer is relevant to the penetration of Zn element into Al2O3p/6061Al composites which is a function of temperature. So it is necessary to lower heating temperature in order to limit the Zn penetration.

Laser Cladding Al-Si/Al_2O_3-TiO_2 Composite Coatings on AZ31B Magnesium Alloy

To improve the wear resistance and corrosion resistance of magnesium alloys, a 5 kW continuous wave CO2 laser was used to investigate the laser surface cladding on AZ31 B magnesium alloys with Al-Si/Al2O3-TiO2 composite powders. A detailed microstructure, chemical composition, and phase analysis of the composite coatings were studied by scanning electron microscopy （SEM）, energy dispersive spectroscopy （EDS）, and X-ray diffraction （XRD）. The laser cladding shows good metallurgical bonding with the substrate. The composite coatings are composed of Mgl7Al12, Al3Mg2, Mg2Si, Al2O3, and TiO2 phases. Compared to the average microhardness （50HV0.05） of the AZ3 1 B substrate, that of the composite coatings （230HV0.05） is improved significantly. The wear resistances of the surface layers were evaluated in detail. The results demonstrate that the wear resistances of the laser surface-modified samples are considerably improved compared to the substrate. It also show that the composite coatings exhibit better corrosion resistance than that of the substrate in 3.5wt% NaCI solution.

Influence of chemical modification by Y2O3 on eutectic Si characteristics and tensile properties of A356 alloy

The modification of A356 aluminum-silicon alloy using yttrium oxide (Y2O3) was studied. Addition levels of up to 2.5 wt.% Y2O3 were investigated. A premixed powder of Al-30wt.%Y2O3 was added to the melt at about 750℃ using vortex method. Samples were then poured in sand mold. The results showed that evident modification was obtained using the Y2O3 addition. The optimum level was 1.5 wt.%, and was corresponding to a eutectic temperature depression from 568 to 557℃. The eutectic Si particles were refined in length from 44.8 to 8.3 μm, and modified in aspect ratio from 6.8 to 0.98. Higher additions of Y2O3 caused de-modification of the eutectic Si particles. The ductility of the modified specimens was enhanced by more than 20% compared to the unmodified ones. This was associated with a gradual transfer from cleavage to a more ductile mode of fracture.

Properties of Dispersion Casting of Y2O3 Particles in Hypo,Hyper and Eutectic Binary Al-Cu Alloys

In the present work,the dispersion casting of Y-2O-3 particles in aluminum-copper alloy was investigated in terms of microstructural changes with respect to Cu contents of 20 （hypo）,33 （eutectic） and 40 （hyper） wt pct by scanning electron microscopy （SEM） and energy dispersive spectroscopy （EDS）.For the fabrication of Al-Cu alloy dispersed Y-2O-3 ceramic particles,stir casting method was employed.In case of Al-20 wt pct Cu alloy （hypoeutectic）,SEM images revealed that primary Al was grown up in the beginning.After that,eutectic phase with well dispersed ceramic particles was formed.In case of eutectic composition,Y-2O-3 particles were uniformly dispersed in the matrix.When the Cu is added into Al up to 40 wt pct （hypereutectic）,primary phase was grown up without any Y-2O-3 ceramic particles in the early stage of solidification.Thereafter, eutectic phase was formed with well dispersed ceramic particles.It can be concluded that Y-2O-3 ceramic particles is mostly dispersed in case of eutectic composition in Al-Cu alloy.

Cr_2O_3 BASE CERAMIC COATING ON ALUMINUM ALLOYS FORMED BY CHEMICAL REACTIONS

A newly developed method is introduced for producing Cr 2O 3 base ceramic coating on aluminum alloys. On the basis of properly selecting base reactions, slurry is prepared and then applied onto the substrate surface. By chemical reactions taken place in situ on the surface of aluminum alloy at relative low temperature, Cr 2O 3 base ceramic coating is formed. By means of scanning electron microscopy, the coating microstructure and the bonding mechanism are studied. X ray diffraction analysis is also used to investigate the chemical composition of the coating. The coating formation mechanism is further discussed. With a pin on disk tester, wear test is made to evaluate the wear performances of the coating. The results show that by applying the coating on aluminum alloy, the wear decreases 5 times in comparation to that without coating.

Superplasticity in an Aluminum Alloy 6061/Al_2O_3p Composite

The superplasticity of an Al203p/6061Al composite, fabricated by powder metallurgy techniques, has been investigated. Instead of any special thermomechanical processing or hot rolling, simple hot extrusion has been employed to obtain a fine grained structure before superplastic testing. Superplastic tensile tests were performed at strain rates ranging from 10-2 to 10-4 s-1 and at temperatures from 833 to 893 K. A maximum elongation of 200% was achieved at a temperature of 853 K and an initial strain rate of 1.67×103 s-1. The highest value obtained for the strain rate sensitivity index (in) was 0.32. Differential scanning calorimeter was used to ascertain the possibility of any partial melting in the vicinity of optimum superplastic temperature. These results suggested that no liquid phase existed where maximum elongation was achieved and deformation took place entirely in the solid state.