W9Cr4V2Mo材料轴承磨加工工艺

针对W 9Cr4V2Mo耐热钢磨削性能差的特点,对磨加工工艺路线进行了改进,采用了三次循环二次稳定的磨削加工方法。挡边和工艺基准面进行三次循环磨削,沟道进行二次循环磨削;并进行了两次稳定处理。改进工艺后,避免了磨削应力的产生和表面烧伤,提高了加工精度。

类金刚石薄膜对W9Cr4V2Mo钢摩擦性能的影响

采用球-盘摩擦试验法研究类金刚石薄膜对W9Cr4V2Mo钢摩擦性能的影响,并用光学显微镜对盘磨损后的形貌进行分析。结果表明,与W9Cr4V2Mo钢自耦相比,镀类金刚石薄膜能够有效降低W9Cr4V2Mo钢的摩擦因数和磨损率。

W9Cr4V2Mo钢工艺和性能研究

本文研究了W9Cr4V2Mo钢的热加工和热处理工艺,测试了其高温性能,并对其碳化物相进行了初步探讨。结果表明:该钢在850～1150℃之间有很好的热塑性,但温度高于1150℃时,热塑性直线下降,1200℃时出现过烧。此钢淬火温度范围较窄,应在1220～1240℃之间适当选择。其碳化物相主要为M_6C和VC。

Surface Modification of W9Cr4V2Mo High Temperature Bearing Steel by Rare Earth Ion Implantation

Wear and corrosion are the main failure mechanisms of bearings and some measures have been proposed to prolong the working lifetime. Possible approaches include the use of more expensive materials, ion implantation, surface finish enhancement, and ion beam assisted deposition. Among them ion implantation is used extensively for the modification of surface and properties of materials and many studies have disclosed that the beating steel surface can be strengthened by ion implantation of different elements such as N, Mo, N and Mo, and so on.

混晶W9Cr4V2Mo钢的力学性能验证及处理方法

针对W9Cr4V2Mo钢在实际热处理生产中容易出现混晶现象,提出混晶后采用球化退火+重新淬火回火进行处理。对混晶及非混晶材料进行硬度、组织、冲击性能以及弯曲性能验证。试验得出经过球化退火和重新淬火回火后,材料混晶现象消失,材料的硬度、冲击以及弯曲力学性能并未降低。因此,零件混晶后可采取球化退火+重新淬火回火进行处理。