以低成本压缩空气和丙烷作为工作气体,采用超音速等离子喷涂制备了WC-17Co涂层,研究了喷涂功率对涂层组织、孔隙率和相组成的影响,测试了涂层的抗压性和耐磨性.结果表明,喷涂功率显著影响粉末的熔化和脱碳程度,功率过小时,WC颗粒熔化程...以低成本压缩空气和丙烷作为工作气体,采用超音速等离子喷涂制备了WC-17Co涂层,研究了喷涂功率对涂层组织、孔隙率和相组成的影响,测试了涂层的抗压性和耐磨性.结果表明,喷涂功率显著影响粉末的熔化和脱碳程度,功率过小时,WC颗粒熔化程度低;功率过大时,WC严重脱碳生成W_2C甚至W相.喷涂功率为65 k W制备的涂层孔隙率最低(0.87%),未出现严重脱碳产物钨,涂层具有很强的抗压入变形能力,由于高硬度WC颗粒的存在,涂层的耐磨性显著提高,其磨损量仅为基体的15%,磨损形式由基体的严重磨粒磨损+粘着磨损变为涂层的轻微磨粒磨损.展开更多
The in-flight and deposition properties of three types of WC-17 Co powder with different particle densities during a high-velocity oxygen fuel (HVOF) thermal spray process were investigated. Three types of powder ex...The in-flight and deposition properties of three types of WC-17 Co powder with different particle densities during a high-velocity oxygen fuel (HVOF) thermal spray process were investigated. Three types of powder exhibited similar velocity upon impact on the substrate surface. The powder with the lower particle density exhibited a higher temperature upon impingement process, resulting in the generation of a higher flattening ratio. Thus, the coating derived from the powder with the lower particle density possessed superior micro-hardness, porosity and surface roughness. However, the coating with the lowest particle density showed the poorest fracture toughness because of the generation of the largest amount of amorphous phase.展开更多
文摘以低成本压缩空气和丙烷作为工作气体,采用超音速等离子喷涂制备了WC-17Co涂层,研究了喷涂功率对涂层组织、孔隙率和相组成的影响,测试了涂层的抗压性和耐磨性.结果表明,喷涂功率显著影响粉末的熔化和脱碳程度,功率过小时,WC颗粒熔化程度低;功率过大时,WC严重脱碳生成W_2C甚至W相.喷涂功率为65 k W制备的涂层孔隙率最低(0.87%),未出现严重脱碳产物钨,涂层具有很强的抗压入变形能力,由于高硬度WC颗粒的存在,涂层的耐磨性显著提高,其磨损量仅为基体的15%,磨损形式由基体的严重磨粒磨损+粘着磨损变为涂层的轻微磨粒磨损.
文摘The in-flight and deposition properties of three types of WC-17 Co powder with different particle densities during a high-velocity oxygen fuel (HVOF) thermal spray process were investigated. Three types of powder exhibited similar velocity upon impact on the substrate surface. The powder with the lower particle density exhibited a higher temperature upon impingement process, resulting in the generation of a higher flattening ratio. Thus, the coating derived from the powder with the lower particle density possessed superior micro-hardness, porosity and surface roughness. However, the coating with the lowest particle density showed the poorest fracture toughness because of the generation of the largest amount of amorphous phase.