Zr/WC composite coating was prepared on the surface of Cr12MoV steel by electric spark deposition technology to change its surface properties. The surface and worn surface morphology of the coating were observed using...Zr/WC composite coating was prepared on the surface of Cr12MoV steel by electric spark deposition technology to change its surface properties. The surface and worn surface morphology of the coating were observed using scanning electron microscope. Dry friction and wear tests of the coatings were carried out at room temperature. The results show that the coating is continuous and uniform, and the thickness was about 50-60 μm. The microhardness of the coating surface was highest at 1140 HV_(200g), which was significantly higher than that of the substrate. The ear tests results show that the wear weight loss, wear volume and wear rate follow the following rules: Cr12MoV>WC coating> Zr/WC composite coating.展开更多
An experimental study has been carried out to investigate the influence of heat treatment at 300 ℃,450 ℃,550 ℃,650 ℃ and 800 ℃ on the microstructure and sliding wear behavior of Fe Al/WC intermetallic composite c...An experimental study has been carried out to investigate the influence of heat treatment at 300 ℃,450 ℃,550 ℃,650 ℃ and 800 ℃ on the microstructure and sliding wear behavior of Fe Al/WC intermetallic composite coatings produced by high velocity arc spraying (HVAS) and cored wires. The result shows, the main phases in both as sprayed and heat treated Fe Al/WC composite coatings are iron aluminide intermetallics (Fe 3Al+FeAl) and α as well as a little oxide (Al 2O 3) and carbides (WC, W 2C, Fe 2W 2C and Fe 6W 6C). After heat treated at 450-650 ℃, dispersion strengthening of Fe 2W 2C and Fe 6W 6C will lead to a rise in microhardness of the coatings. The microhardness is likely to be the most important factor which influences the sliding wear behavior of the coatings. Increasing the microhardness through heat treatment will improve the sliding wear resistance of the Fe Al/WC composite coatings.展开更多
The WC-Co composite coatings bonded tightly to steel substrate have been made by vacuum fusion sinter （VFS）. The concentration distribution of some components were measured by the electron probe, and the microstruct...The WC-Co composite coatings bonded tightly to steel substrate have been made by vacuum fusion sinter （VFS）. The concentration distribution of some components were measured by the electron probe, and the microstructure and morphology of VFS coatings were observed and analyzed by SEM, X-ray diffractometer and microhardness tester. Diffusion coefficient of every element was calculated by using the experimental results. The influence of the interracial diffusion on the microstructure, Vickers hardness and interracial bond strength of the VFS coatings was studied in detail. The experimental results show that there is a metallurgical bond area between the VFS WC-Co coatings and the steel substrate. The VFS coatings are characterized by the gradient hardness of the interface and the high bond strength to the steel substate, both of which are beneficial to the improvement of the wear resistance and corrosion resistance.展开更多
The Fe40Al-xWC(x=0,10,12,15)coatings with dense structure were successfully deposited by high-velocity oxygen fuel (HVOF)spraying of a mixture of Fe,Al and WC powders.The objective of the present work is to provide in...The Fe40Al-xWC(x=0,10,12,15)coatings with dense structure were successfully deposited by high-velocity oxygen fuel (HVOF)spraying of a mixture of Fe,Al and WC powders.The objective of the present work is to provide insight into the oxidation behavior of the as-deposited coatings at 650℃under 0.1 MPa flowing pure O2.The present results show differences in the oxidation behavior of Fe40Al coating and Fe40Al-xWC composite coatings.The irregular Fe2O3 layer is seen on the top surface of the composite coatings.Fe40Al coating and Fe40Al-15WC composite coating both suffer a catastrophic corrosion due to the formation of a porous structure during 24 h of oxidation.However,Fe40Al-10WC and Fe40Al-12WC composite coatings show a good oxidation resistance behavior due to their dense structure.展开更多
Diamond has poor interface tolerance with Al.To enhance interface bonding,in this study,tungsten carbide(WC)nanocoatings on the surface of diamond particles were prepared using sol–gel and in-situ reaction methods.WO...Diamond has poor interface tolerance with Al.To enhance interface bonding,in this study,tungsten carbide(WC)nanocoatings on the surface of diamond particles were prepared using sol–gel and in-situ reaction methods.WO_(3) sol–gel with two concentrations,0.2 mol/L,and 0.5 mol/L,was,respectively,coated on diamond particles,then sintered at 1250℃for 2 h to produce WC nanocoatings.The concentration of 0.2 mol/L WO_(3) sol–gel was not enough to cover the surface of the diamond completely,while 0.5 mol/L WO_(3) sol–gel could fully cover it.Moreover,WO_(3) was preferentially deposited on{100}planes of the diamond.WO_(3) converted to WC in-situ nanocoatings after sintering due to the in-situ reaction of WO_(3) and diamond.The diamond-reinforced Al composites with and without WC coating were fabricated by powder metallurgy.The diamond/Al composite without coating has a thermal conductivity of 584.7 W/mK,while the composite with a coating formed by 0.2 mol/L and 0.5 mol/L WO_(3) sol–gel showed thermal conductivities of 626.1 W/mK and 584.2 W/mK,respectively.The moderate thickness of nanocoatings formed by 0.2 mol/L WO_(3) sol–gel could enhance interface bonding,therefore improving thermal conductivity.The nanocoating produced by 0.5 mol/L WO_(3) sol–gel cracked during the fabrication of the composite,leading to Al12W formation and a decrease in thermal conductivity.展开更多
基金supported by Key Projects of Strategic International Scientific and Technological Innovation Cooperation(Grant No.2016YFE0201300)
文摘Zr/WC composite coating was prepared on the surface of Cr12MoV steel by electric spark deposition technology to change its surface properties. The surface and worn surface morphology of the coating were observed using scanning electron microscope. Dry friction and wear tests of the coatings were carried out at room temperature. The results show that the coating is continuous and uniform, and the thickness was about 50-60 μm. The microhardness of the coating surface was highest at 1140 HV_(200g), which was significantly higher than that of the substrate. The ear tests results show that the wear weight loss, wear volume and wear rate follow the following rules: Cr12MoV>WC coating> Zr/WC composite coating.
文摘An experimental study has been carried out to investigate the influence of heat treatment at 300 ℃,450 ℃,550 ℃,650 ℃ and 800 ℃ on the microstructure and sliding wear behavior of Fe Al/WC intermetallic composite coatings produced by high velocity arc spraying (HVAS) and cored wires. The result shows, the main phases in both as sprayed and heat treated Fe Al/WC composite coatings are iron aluminide intermetallics (Fe 3Al+FeAl) and α as well as a little oxide (Al 2O 3) and carbides (WC, W 2C, Fe 2W 2C and Fe 6W 6C). After heat treated at 450-650 ℃, dispersion strengthening of Fe 2W 2C and Fe 6W 6C will lead to a rise in microhardness of the coatings. The microhardness is likely to be the most important factor which influences the sliding wear behavior of the coatings. Increasing the microhardness through heat treatment will improve the sliding wear resistance of the Fe Al/WC composite coatings.
文摘The WC-Co composite coatings bonded tightly to steel substrate have been made by vacuum fusion sinter （VFS）. The concentration distribution of some components were measured by the electron probe, and the microstructure and morphology of VFS coatings were observed and analyzed by SEM, X-ray diffractometer and microhardness tester. Diffusion coefficient of every element was calculated by using the experimental results. The influence of the interracial diffusion on the microstructure, Vickers hardness and interracial bond strength of the VFS coatings was studied in detail. The experimental results show that there is a metallurgical bond area between the VFS WC-Co coatings and the steel substrate. The VFS coatings are characterized by the gradient hardness of the interface and the high bond strength to the steel substate, both of which are beneficial to the improvement of the wear resistance and corrosion resistance.
基金Project(209069)supported by the Key Research Program of Ministry of Education of ChinaProjects(2008GZC00652007GZC0611)supported by the Natural Science Foundation of Jiangxi Province,China
文摘The Fe40Al-xWC(x=0,10,12,15)coatings with dense structure were successfully deposited by high-velocity oxygen fuel (HVOF)spraying of a mixture of Fe,Al and WC powders.The objective of the present work is to provide insight into the oxidation behavior of the as-deposited coatings at 650℃under 0.1 MPa flowing pure O2.The present results show differences in the oxidation behavior of Fe40Al coating and Fe40Al-xWC composite coatings.The irregular Fe2O3 layer is seen on the top surface of the composite coatings.Fe40Al coating and Fe40Al-15WC composite coating both suffer a catastrophic corrosion due to the formation of a porous structure during 24 h of oxidation.However,Fe40Al-10WC and Fe40Al-12WC composite coatings show a good oxidation resistance behavior due to their dense structure.
基金supported by the National Natural Science Foundation of China(No.51931009)the Liaoning Revitalization Talents Program(No.XLYC2007009).
文摘Diamond has poor interface tolerance with Al.To enhance interface bonding,in this study,tungsten carbide(WC)nanocoatings on the surface of diamond particles were prepared using sol–gel and in-situ reaction methods.WO_(3) sol–gel with two concentrations,0.2 mol/L,and 0.5 mol/L,was,respectively,coated on diamond particles,then sintered at 1250℃for 2 h to produce WC nanocoatings.The concentration of 0.2 mol/L WO_(3) sol–gel was not enough to cover the surface of the diamond completely,while 0.5 mol/L WO_(3) sol–gel could fully cover it.Moreover,WO_(3) was preferentially deposited on{100}planes of the diamond.WO_(3) converted to WC in-situ nanocoatings after sintering due to the in-situ reaction of WO_(3) and diamond.The diamond-reinforced Al composites with and without WC coating were fabricated by powder metallurgy.The diamond/Al composite without coating has a thermal conductivity of 584.7 W/mK,while the composite with a coating formed by 0.2 mol/L and 0.5 mol/L WO_(3) sol–gel showed thermal conductivities of 626.1 W/mK and 584.2 W/mK,respectively.The moderate thickness of nanocoatings formed by 0.2 mol/L WO_(3) sol–gel could enhance interface bonding,therefore improving thermal conductivity.The nanocoating produced by 0.5 mol/L WO_(3) sol–gel cracked during the fabrication of the composite,leading to Al12W formation and a decrease in thermal conductivity.