The effects of ultrafine WC(WC_(UF),0.5μm) or W(1μm) and C(0.3μm)(W+C)_(UF) additives on the densification,microstructure and mechanical properties of coarse-grained cemented carbides were compared systematically.O...The effects of ultrafine WC(WC_(UF),0.5μm) or W(1μm) and C(0.3μm)(W+C)_(UF) additives on the densification,microstructure and mechanical properties of coarse-grained cemented carbides were compared systematically.Overall,the cemented carbides with WC_(UF)/(W+C)_(UF) additives are almost fully densification to be higher than 99%,and the average grain size is kept above 2.8μm.The WC_(UF) additive assists grains to(truncated)trigonal prism shape by two dimensional(2D) growth,whereas the(W+C)_(UF) additive assists grains to rounded shape by three dimensional(3D) growth,lowers WC contiguity and increases face-centered-cubic Co.The hardness and bending strength of(75WC_(C)-15WC_(UF))-10Co are 86.6 HRA and 2 272 MPa,respectively,both higher than those of(75WC_(C)-15(W+C)_(UF))-10Co,which could be ascribed to the enhanced densification and unblemished grains.However,the fracture toughness of the(75WC_(C)-15(W+C)_(UF))-10Co is 23.5 MPa·m^(1/2),higher than that of the(75WC_(C)-15WC_(UF))-10Co due to the uniform WC-Co structure and flexible binder phase.展开更多
WC-Co nanocrystalline nitrogen-containing cemented carbides were prepared by vacuum sintering and low pressure sintering.The sintering processes of Cr_(2)(C,N)doped nano WC-Co powders were studied by using thermogravi...WC-Co nanocrystalline nitrogen-containing cemented carbides were prepared by vacuum sintering and low pressure sintering.The sintering processes of Cr_(2)(C,N)doped nano WC-Co powders were studied by using thermogravimetric analysis(TGA)and differential scanning calorimetry(DSC).The effect of sintering temperature on the microstructure and mechanical properties of nanocrystalline cemented carbide was studied by scanning electron microscope(SEM),high resolution transmission electron microscope(HRTEM)and mechanical property test.The results showed that the nano WC grains began to grow in the solid phase sintering stage.A high-performance nano-nitrogen-containing cemented carbide with uniform microstructure and good interfacial bonding can be obtained by increasing the sintering temperature to 1380℃.It has a transverse rupture strength(TRS)of 5057 MPa and a hardness of 1956 HV30.展开更多
The effects of gradient structure on the microstructure and properties of coated cemented carbides were researched with optical microscopy (OM), scanning electron microscopy (SEM), strength measurements, and cutti...The effects of gradient structure on the microstructure and properties of coated cemented carbides were researched with optical microscopy (OM), scanning electron microscopy (SEM), strength measurements, and cutting tests. It shows that vacuum sintering of WC-Ti(C, N)-TaC-Co cemented carbides results in the formation of a surface ductile zone. The ductile zone prevents crack propagation and leads to the increase of transverse rupture strength of the substrate. The impact resistance of coated gradient inserts was obviously improved on the basis of maintaining resistance to abrasion and the forming mechanism of the gradient structure was also analyzed.展开更多
In order to reveal the formation mechanism of cubic carbide free layers (CCFL), graded cemented carbides with CCFL in the surface zone were fabricated by a one-step sintering procedure in vacuum, and the analysis on...In order to reveal the formation mechanism of cubic carbide free layers (CCFL), graded cemented carbides with CCFL in the surface zone were fabricated by a one-step sintering procedure in vacuum, and the analysis on microstructure and element distribution were performed by scanning electron microscopy (SEM) and electron probe micro-analyzer (EPMA), respectively. A new physical model and ki- netic equation were established based on experimental results. Being different f^om previous models, this model suggests that nitrogen diffu- sion outward is only considered as an induction factor, and the diffusion of titanium through liquid phase plays a dominative role. The driving force of diffusion is expressed as the differential value between nitrogen partial pressure and nitrogen equilibrium pressure essentially. Simulation results by the kinetic equation are in good agreement with experimental values, and the effect of process parameters on the growth kinetics of CCFL can also be explained reasonably by the current model.展开更多
This paper deals with the effects of codoped VC/Cr3C2 and sintering temperature on the magnetic and mechanical properties of ultra-fine grained WC-12%Co alloys. Results show that the synergistic action of doped VC/Cr3...This paper deals with the effects of codoped VC/Cr3C2 and sintering temperature on the magnetic and mechanical properties of ultra-fine grained WC-12%Co alloys. Results show that the synergistic action of doped VC/Cr3C2 in optimal proportion enhances both the hardness and transverse rupture strength (TRS) of the alloys, with more homogeneous microstructtLre. When the alloy is sintered at 1430℃ and with 0.5% Cr3C2/0.2% VC, the TRS reaches 3786 MPa, the hardness is 91.7 HRA and the grain size smaller than 0.6 μm. The numerical analyses on grain growth during the sintering process show that both VC precipitating on the WC grain boundary and Cr3C2 dissolving in the Co phase decrease the solid/liquid interfacial energy γ, the process of dissolution and reprecipitation is greatly retarded and the coarsening of WC grains is inhibited.展开更多
The relative density of WC-Co cemented carbides during spark plasma sintering(SPS) was analyzed.Based on the change in displacement of the ram in the SPS system,the relative densities in the sintering process can be...The relative density of WC-Co cemented carbides during spark plasma sintering(SPS) was analyzed.Based on the change in displacement of the ram in the SPS system,the relative densities in the sintering process can be achieved at different temperatures.The results indicated that densification of the samples started at near 900°C,the density rapidly reached its maximum at the increasing temperature stage,in which the temperature was lower than the sintering temperature of 1200°C,and most of the densification took place in the stage.Besides,the theoretical values were consistent with the experimental results.展开更多
The sintering characteristics, microstructure, and mechanical properties of ultrafine WC-12%Co-0.2%VC/0.5%Cr3C2 cemented carbides were investigated. Dilatometric and differential thermal analyses (DTA) indicate that...The sintering characteristics, microstructure, and mechanical properties of ultrafine WC-12%Co-0.2%VC/0.5%Cr3C2 cemented carbides were investigated. Dilatometric and differential thermal analyses (DTA) indicate that the compacts start to shrink at 600°C, the shrinkage rate peak is at 1190°C, and the liquid formation temperature is lower than the W-C-Co eutectic temperature (1330°C). Microstructure analysis results show that the cemented carbides with fine and homogeneous microstructure were obtained when sintered at 1430°C. Continuous and discontinuous grain growth was suppressed due to the synergistic action of VC/Cr3C2. The transverse rupture strength (TRS) of the samples reaches 4286 MPa, with the hardness HRA 92.1. The fine and homogeneous microstructure, alloy strengthening, and different phase constitutions of binder in the cemented carbides result in high hardness and TRS. Continuous and discontinuous grain growth was observed in the cemented carbide sintered at 1450°C, which results in significant decreases of hardness and TRS. It indicates that VC/Cr3C2 additions in the cemented carbides can only suppress the grain growth at a certain temperature.展开更多
Varying the morphology and the structure of γ-phase (Co-base Co-W-C solid solution) by means of altering the cooling rate and the preparing method of liquid sintered WC-Co cemented carbides samples, the mechanism of ...Varying the morphology and the structure of γ-phase (Co-base Co-W-C solid solution) by means of altering the cooling rate and the preparing method of liquid sintered WC-Co cemented carbides samples, the mechanism of fcc→hcp transformation of γ-phase in WC-Co alloy has been explored. The results show that, the cooling rate is an important affecting factor on fcc→hcp transformation of γ-phase and the fcc→hcp transformation is mainly a diffusive type when cooling WC-Co samples above room temperature展开更多
Thermodynamic and kinetic study on TRIP (transformation induced plasticity) steels, cemented carbides and mold steel for plastics were carried out in order to design modern advanced materials. With the sublattice mo...Thermodynamic and kinetic study on TRIP (transformation induced plasticity) steels, cemented carbides and mold steel for plastics were carried out in order to design modern advanced materials. With the sublattice model, equilibrium compositions of ferrite and austenite phases in TRIP steels, as well as volume fraction of austenite at inter-critical temperatures for different time were calculated. Concentration profiles of carbon, manganese, aluminum and silicon in the steels were also estimated in the lattice fixed frame of reference. The effect of Si and Mn on TRIP was discussed according to thermodynamic and kinetic analyses. In order to understand and produce the graded nanophase structure of cemented carbides, miscellaneous phases in the M-Co-C (M= Ti, Ta, Nh) systems and Co-V-C system were modeled. Solution parameters and thermodynamic: properties were listed in detail. The improvement of machining behavior of prehardened mould steel for plastics was obtained by computer-aided composition design. The results showed that the matrix composition of large-section prehardened mould steel for plastic markedly influences the precipitation of non-metallic inclusion and the composition control by the aid of Thermo-Calc software package minimizes the amount of detrimental oxide inclusion. In addition, the modification of calcium was optimized in composition design.展开更多
The nanocrystalline WC-10Co composite powders were produced with the processing method of spray thermal decomposition-continuous reduction&carburization.The grain growth inhibitors of 0.4wt%Cr_(3)C_(2) and 0.4wt%V...The nanocrystalline WC-10Co composite powders were produced with the processing method of spray thermal decomposition-continuous reduction&carburization.The grain growth inhibitors of 0.4wt%Cr_(3)C_(2) and 0.4wt%VC were added into the composite powders to obtain advanced ultrafine hardmetals with minimal porosity,defects and discontinuous.The rod samples were formed by extrusion.They were sintered in cacuum with SIP treatment.The sintered rods were made into PCB microdrill samples after polishing.Mechanical properties(such as density,hardness,transverse rupture strenth(TRS),magnetic saturation induction and magnetic coercivity)of the sintered ultrafine cemented carbides were measured.The microstructures of them were investigated by scanning electron microscopy(SEM)and transmission electron microscopy(TEM).The experimental results show that the transverse rupture strength of the samples sintered in vacuum with sinterhip(SIP)treatment is more excellent.The grain size could be controlled in a range of 200-400 nm with the help of grain growth inhibitors.And the superfine grained materials have superior strength(3900 MPa)and high hardness(HRA=93.3).These features are ideal for PCB microdrills.展开更多
Using the microwave sintering technology, the effects of phosphorus (P) additions on the microstructure and properties of the ultrafine WC-10Co alloys were investigated. The experimental results show that with only ...Using the microwave sintering technology, the effects of phosphorus (P) additions on the microstructure and properties of the ultrafine WC-10Co alloys were investigated. The experimental results show that with only 0.3wt% P additions, full density WC-10Co cermets were obtained at temperature of 1250℃, which is 70 ℃ lower than that of the undoped counterparts. Lower sintering temperature can result in finer WC grain growth; therefore, the P-doped WC-10Co alloys exhibited higher hardness than the undoped ones. But at the same time, P doping could lead to sacrifice of fracture toughness ofWC-10Co cemented carbides.展开更多
The allotropic transformation process of the γ-phase in WC-Co cemented carbides has been explored.Theconcepts of γ-grain and the γ-domain have been proposed forward:The γ-domain is the residual FCC-typeβ-Co grain...The allotropic transformation process of the γ-phase in WC-Co cemented carbides has been explored.Theconcepts of γ-grain and the γ-domain have been proposed forward:The γ-domain is the residual FCC-typeβ-Co grain that failed to transform when cooling alloy sample and γ-base is the HCP-type x-Co transformedmainly by means of diffusion,the outline of the γ-grain is consistent with the newly fromed β-Co grain formedat high temperature.The quantity and distribution of γ-grain domain are related to the cooling rate after sinter-ing and influence the alloys properties.展开更多
Tianjin Institute of Hard Alloy,Tianjin 300222,China ABSTRACT The effects of solutes of wolfram and carbon on specific saturation magnetization(4πσ)of cobalt have been examined on the basis of the measurement of Ana...Tianjin Institute of Hard Alloy,Tianjin 300222,China ABSTRACT The effects of solutes of wolfram and carbon on specific saturation magnetization(4πσ)of cobalt have been examined on the basis of the measurement of Ana for hexagonal typeα-Co and cubic typeβ-Co.The Co-W-C solid solution simulative alloys have been fabricated according to binder composition in WC-Co cemented carbides and the effect of its component and structure on its Ana has been discussed too.It is pointed out that the Co phase structural factor must be considered as measuring the Ana of WC-Co cemented carbides.展开更多
The influence of γ-phase composition in WC-Co cemented carbides on its specific coercive force H_(sc) hasbeen studied by analysing the imitative alloys of γ-phase. The results show that the H_(sc) of γ-phase is low...The influence of γ-phase composition in WC-Co cemented carbides on its specific coercive force H_(sc) hasbeen studied by analysing the imitative alloys of γ-phase. The results show that the H_(sc) of γ-phase is lower thanthat of pure cobalt, because the solute W can raise γ-phase H_(sc) but the carbon exhibits more intense negativeeffect on H_(sc). The effect is enhanced with raising the C solubilities in γ-phase.展开更多
The nanocomposite WC-Co powders were prepared through planetary ball milling method.Effects of grain growth inhibitor addition and the vacuum sintering parameters on the microstructure and properties of ultrafine WC-1...The nanocomposite WC-Co powders were prepared through planetary ball milling method.Effects of grain growth inhibitor addition and the vacuum sintering parameters on the microstructure and properties of ultrafine WC-10Co cemented carbides were investigated using X-ray diffractometer,scanning electron microscope and mechanical property tester.The results show that VC and NbC additions can refine the WC grains,decrease the volume fraction of Co3W3C phase in ultrafine WC-10Co cemented carbides,and increase the hardness and fracture toughness of the base alloys.After sintering for 60 min at 1 400℃,the average grain size and hardness of ultrafine-grained WC-10Co-1VC cemented carbide are 470 nm and HRA 91.5,respectively.The fracture toughness of cemented carbide WC-10Co-1NbC alloy is over 7 MN·m -3/2 .展开更多
Brazing is a suitable technology to join different materials such as cemented carbides and steel. Even though this technology has been investigated for many years, insufficient joints can occur easily, as the brazing ...Brazing is a suitable technology to join different materials such as cemented carbides and steel. Even though this technology has been investigated for many years, insufficient joints can occur easily, as the brazing process is very sensitive concerning the handling parameters. Defects such as voids and cracks are hard to detect by commonly used visual inspection methods. Other nondestructive methods such as radiography or ultrasonic testing are usually not economical for the examination of these joints. Studies proved that the electrical resistance has the potential to serve as an effective alternative for the evaluation of brazed joints. In this study, the authors have compared the electrical resistance and the shear strength. For this, cemented carbides were brazed to steel by means of induction heating at an ambient atmosphere. A silver-based filler metal ( BrazeTec 4900 / Ag 449 ) and a flux ( BrazeTec spezial h / FH12) were selected to enable the brazing process. The brazing time and the temperature were varied in order to produce different joint qualities. After brazing, the resistance was measured on each joint with the 4-point probe method to facilitate a high accuracy. The results underline the possibility to use electrical resistance measurements as an effective tool for a quality control of brazed joints.展开更多
The morphology,structure and distribution of the rare earth compounds in the YG8R.YT5R and YT14R cemented carbides with additions of trace light rare earths were studied with an analytical electron microscope. The par...The morphology,structure and distribution of the rare earth compounds in the YG8R.YT5R and YT14R cemented carbides with additions of trace light rare earths were studied with an analytical electron microscope. The particles of the rare earth compounds in these alloys are all spherical and distribute at interfaces between the Co-cement phase and WC hard phase or(TiW)C solid solution,and in the(TiW)C solid solution.In the YG8R and YTI4R alloys,the rare earth compound is RE_2O_3 with a bcc structure,while in the YT5R alloy. the rare earth compound is RE_2O_2S with a hcp structure.展开更多
A Cemented Carbide material was implanted with dual nitrogen plus tantalum ions at temperatures of 100℃ and 400℃ and a dose of 8× 10^17 ions cm^-2. The thickness of the implanted layers increased by about an or...A Cemented Carbide material was implanted with dual nitrogen plus tantalum ions at temperatures of 100℃ and 400℃ and a dose of 8× 10^17 ions cm^-2. The thickness of the implanted layers increased by about an order of magnitude when the temperature was elevated from 100℃ to 400℃. Higher surface hardness was also obtained in the high temperature implantation. X-ray diffraction showed the presence of nitrides of tantalum and tungsten in the implanted surface.展开更多
A new kind of sintering process, combined sintering process. i.e. vacuum sintering plus hot isolate pressure sintering (HIP), was introduced for producing ultrafine WC-10% Co (mass fraction. so as the follows) cemen...A new kind of sintering process, combined sintering process. i.e. vacuum sintering plus hot isolate pressure sintering (HIP), was introduced for producing ultrafine WC-10% Co (mass fraction. so as the follows) cemented carbides. The effects of some processing parameters on the microstructure and mechanical properties of the obtained cemented carbides were studied. The results show that the rapid shrinkage and the pronounced densification of tile cemented carbides took place during the vacuum sintering stage, which is intinaately correlated with the local liquid sintering occurred during this earl} sintering stage for the high surface activity of ultrafine WC-Co powder. The way of high pressure imposing. isothermal treatment cycle during ac.acuum sintering and HIP sintering stage directly influence the densitication of compacts and the mechanical properties of the produced WC-10%Co cemented carbides.展开更多
基金Funded by the Technology Innovation Leading Program of Shaanxi(No.2022QFY08-02)。
文摘The effects of ultrafine WC(WC_(UF),0.5μm) or W(1μm) and C(0.3μm)(W+C)_(UF) additives on the densification,microstructure and mechanical properties of coarse-grained cemented carbides were compared systematically.Overall,the cemented carbides with WC_(UF)/(W+C)_(UF) additives are almost fully densification to be higher than 99%,and the average grain size is kept above 2.8μm.The WC_(UF) additive assists grains to(truncated)trigonal prism shape by two dimensional(2D) growth,whereas the(W+C)_(UF) additive assists grains to rounded shape by three dimensional(3D) growth,lowers WC contiguity and increases face-centered-cubic Co.The hardness and bending strength of(75WC_(C)-15WC_(UF))-10Co are 86.6 HRA and 2 272 MPa,respectively,both higher than those of(75WC_(C)-15(W+C)_(UF))-10Co,which could be ascribed to the enhanced densification and unblemished grains.However,the fracture toughness of the(75WC_(C)-15(W+C)_(UF))-10Co is 23.5 MPa·m^(1/2),higher than that of the(75WC_(C)-15WC_(UF))-10Co due to the uniform WC-Co structure and flexible binder phase.
基金Funded by the National Key Research and Development Plan of China(No.2017YFB0305900)。
文摘WC-Co nanocrystalline nitrogen-containing cemented carbides were prepared by vacuum sintering and low pressure sintering.The sintering processes of Cr_(2)(C,N)doped nano WC-Co powders were studied by using thermogravimetric analysis(TGA)and differential scanning calorimetry(DSC).The effect of sintering temperature on the microstructure and mechanical properties of nanocrystalline cemented carbide was studied by scanning electron microscope(SEM),high resolution transmission electron microscope(HRTEM)and mechanical property test.The results showed that the nano WC grains began to grow in the solid phase sintering stage.A high-performance nano-nitrogen-containing cemented carbide with uniform microstructure and good interfacial bonding can be obtained by increasing the sintering temperature to 1380℃.It has a transverse rupture strength(TRS)of 5057 MPa and a hardness of 1956 HV30.
文摘The effects of gradient structure on the microstructure and properties of coated cemented carbides were researched with optical microscopy (OM), scanning electron microscopy (SEM), strength measurements, and cutting tests. It shows that vacuum sintering of WC-Ti(C, N)-TaC-Co cemented carbides results in the formation of a surface ductile zone. The ductile zone prevents crack propagation and leads to the increase of transverse rupture strength of the substrate. The impact resistance of coated gradient inserts was obviously improved on the basis of maintaining resistance to abrasion and the forming mechanism of the gradient structure was also analyzed.
基金financially supported by the National Key Technology Support Program (No.2007BAE05B02)
文摘In order to reveal the formation mechanism of cubic carbide free layers (CCFL), graded cemented carbides with CCFL in the surface zone were fabricated by a one-step sintering procedure in vacuum, and the analysis on microstructure and element distribution were performed by scanning electron microscopy (SEM) and electron probe micro-analyzer (EPMA), respectively. A new physical model and ki- netic equation were established based on experimental results. Being different f^om previous models, this model suggests that nitrogen diffu- sion outward is only considered as an induction factor, and the diffusion of titanium through liquid phase plays a dominative role. The driving force of diffusion is expressed as the differential value between nitrogen partial pressure and nitrogen equilibrium pressure essentially. Simulation results by the kinetic equation are in good agreement with experimental values, and the effect of process parameters on the growth kinetics of CCFL can also be explained reasonably by the current model.
基金the National Natural Science Foundation of China (No. 50372043).
文摘This paper deals with the effects of codoped VC/Cr3C2 and sintering temperature on the magnetic and mechanical properties of ultra-fine grained WC-12%Co alloys. Results show that the synergistic action of doped VC/Cr3C2 in optimal proportion enhances both the hardness and transverse rupture strength (TRS) of the alloys, with more homogeneous microstructtLre. When the alloy is sintered at 1430℃ and with 0.5% Cr3C2/0.2% VC, the TRS reaches 3786 MPa, the hardness is 91.7 HRA and the grain size smaller than 0.6 μm. The numerical analyses on grain growth during the sintering process show that both VC precipitating on the WC grain boundary and Cr3C2 dissolving in the Co phase decrease the solid/liquid interfacial energy γ, the process of dissolution and reprecipitation is greatly retarded and the coarsening of WC grains is inhibited.
文摘The relative density of WC-Co cemented carbides during spark plasma sintering(SPS) was analyzed.Based on the change in displacement of the ram in the SPS system,the relative densities in the sintering process can be achieved at different temperatures.The results indicated that densification of the samples started at near 900°C,the density rapidly reached its maximum at the increasing temperature stage,in which the temperature was lower than the sintering temperature of 1200°C,and most of the densification took place in the stage.Besides,the theoretical values were consistent with the experimental results.
基金supported by the Foundation of Scientific and Technologic Development for Universityin Tianjin (No. 20060912)
文摘The sintering characteristics, microstructure, and mechanical properties of ultrafine WC-12%Co-0.2%VC/0.5%Cr3C2 cemented carbides were investigated. Dilatometric and differential thermal analyses (DTA) indicate that the compacts start to shrink at 600°C, the shrinkage rate peak is at 1190°C, and the liquid formation temperature is lower than the W-C-Co eutectic temperature (1330°C). Microstructure analysis results show that the cemented carbides with fine and homogeneous microstructure were obtained when sintered at 1430°C. Continuous and discontinuous grain growth was suppressed due to the synergistic action of VC/Cr3C2. The transverse rupture strength (TRS) of the samples reaches 4286 MPa, with the hardness HRA 92.1. The fine and homogeneous microstructure, alloy strengthening, and different phase constitutions of binder in the cemented carbides result in high hardness and TRS. Continuous and discontinuous grain growth was observed in the cemented carbide sintered at 1450°C, which results in significant decreases of hardness and TRS. It indicates that VC/Cr3C2 additions in the cemented carbides can only suppress the grain growth at a certain temperature.
文摘Varying the morphology and the structure of γ-phase (Co-base Co-W-C solid solution) by means of altering the cooling rate and the preparing method of liquid sintered WC-Co cemented carbides samples, the mechanism of fcc→hcp transformation of γ-phase in WC-Co alloy has been explored. The results show that, the cooling rate is an important affecting factor on fcc→hcp transformation of γ-phase and the fcc→hcp transformation is mainly a diffusive type when cooling WC-Co samples above room temperature
文摘Thermodynamic and kinetic study on TRIP (transformation induced plasticity) steels, cemented carbides and mold steel for plastics were carried out in order to design modern advanced materials. With the sublattice model, equilibrium compositions of ferrite and austenite phases in TRIP steels, as well as volume fraction of austenite at inter-critical temperatures for different time were calculated. Concentration profiles of carbon, manganese, aluminum and silicon in the steels were also estimated in the lattice fixed frame of reference. The effect of Si and Mn on TRIP was discussed according to thermodynamic and kinetic analyses. In order to understand and produce the graded nanophase structure of cemented carbides, miscellaneous phases in the M-Co-C (M= Ti, Ta, Nh) systems and Co-V-C system were modeled. Solution parameters and thermodynamic: properties were listed in detail. The improvement of machining behavior of prehardened mould steel for plastics was obtained by computer-aided composition design. The results showed that the matrix composition of large-section prehardened mould steel for plastic markedly influences the precipitation of non-metallic inclusion and the composition control by the aid of Thermo-Calc software package minimizes the amount of detrimental oxide inclusion. In addition, the modification of calcium was optimized in composition design.
基金Funded by the National Natural Science Foundation of China(No.61704113)the Teaching Quality and Teaching Reform Project of Higher Vocational Education in Guangdong Province(No.GDJG2019394)+2 种基金the Shenzhen Education Science Planning Project(No.zdzz18002)the Shenzhen Philosophy and Social Science Planning Project(No.SZ2020D029)the National Special Support Plan for High-level Talents(Teaching Master Project)。
文摘The nanocrystalline WC-10Co composite powders were produced with the processing method of spray thermal decomposition-continuous reduction&carburization.The grain growth inhibitors of 0.4wt%Cr_(3)C_(2) and 0.4wt%VC were added into the composite powders to obtain advanced ultrafine hardmetals with minimal porosity,defects and discontinuous.The rod samples were formed by extrusion.They were sintered in cacuum with SIP treatment.The sintered rods were made into PCB microdrill samples after polishing.Mechanical properties(such as density,hardness,transverse rupture strenth(TRS),magnetic saturation induction and magnetic coercivity)of the sintered ultrafine cemented carbides were measured.The microstructures of them were investigated by scanning electron microscopy(SEM)and transmission electron microscopy(TEM).The experimental results show that the transverse rupture strength of the samples sintered in vacuum with sinterhip(SIP)treatment is more excellent.The grain size could be controlled in a range of 200-400 nm with the help of grain growth inhibitors.And the superfine grained materials have superior strength(3900 MPa)and high hardness(HRA=93.3).These features are ideal for PCB microdrills.
基金the National Key Technology R&D Program of MOST,China(2003BA328C)the National Natural Science Foundation of China(50472043)Natural Science Foundation of Hubei Province(2006ABA312,2006ABA316)
文摘Using the microwave sintering technology, the effects of phosphorus (P) additions on the microstructure and properties of the ultrafine WC-10Co alloys were investigated. The experimental results show that with only 0.3wt% P additions, full density WC-10Co cermets were obtained at temperature of 1250℃, which is 70 ℃ lower than that of the undoped counterparts. Lower sintering temperature can result in finer WC grain growth; therefore, the P-doped WC-10Co alloys exhibited higher hardness than the undoped ones. But at the same time, P doping could lead to sacrifice of fracture toughness ofWC-10Co cemented carbides.
文摘The allotropic transformation process of the γ-phase in WC-Co cemented carbides has been explored.Theconcepts of γ-grain and the γ-domain have been proposed forward:The γ-domain is the residual FCC-typeβ-Co grain that failed to transform when cooling alloy sample and γ-base is the HCP-type x-Co transformedmainly by means of diffusion,the outline of the γ-grain is consistent with the newly fromed β-Co grain formedat high temperature.The quantity and distribution of γ-grain domain are related to the cooling rate after sinter-ing and influence the alloys properties.
文摘Tianjin Institute of Hard Alloy,Tianjin 300222,China ABSTRACT The effects of solutes of wolfram and carbon on specific saturation magnetization(4πσ)of cobalt have been examined on the basis of the measurement of Ana for hexagonal typeα-Co and cubic typeβ-Co.The Co-W-C solid solution simulative alloys have been fabricated according to binder composition in WC-Co cemented carbides and the effect of its component and structure on its Ana has been discussed too.It is pointed out that the Co phase structural factor must be considered as measuring the Ana of WC-Co cemented carbides.
文摘The influence of γ-phase composition in WC-Co cemented carbides on its specific coercive force H_(sc) hasbeen studied by analysing the imitative alloys of γ-phase. The results show that the H_(sc) of γ-phase is lower thanthat of pure cobalt, because the solute W can raise γ-phase H_(sc) but the carbon exhibits more intense negativeeffect on H_(sc). The effect is enhanced with raising the C solubilities in γ-phase.
基金Project(50823006)supported by the National Natural Science Foundation of ChinaProject(200801348)supported by China Postdoctoral Science FoundationProject(50721003)supported by Innovative Research Groups of the National Natural Science Foundation of China
文摘The nanocomposite WC-Co powders were prepared through planetary ball milling method.Effects of grain growth inhibitor addition and the vacuum sintering parameters on the microstructure and properties of ultrafine WC-10Co cemented carbides were investigated using X-ray diffractometer,scanning electron microscope and mechanical property tester.The results show that VC and NbC additions can refine the WC grains,decrease the volume fraction of Co3W3C phase in ultrafine WC-10Co cemented carbides,and increase the hardness and fracture toughness of the base alloys.After sintering for 60 min at 1 400℃,the average grain size and hardness of ultrafine-grained WC-10Co-1VC cemented carbide are 470 nm and HRA 91.5,respectively.The fracture toughness of cemented carbide WC-10Co-1NbC alloy is over 7 MN·m -3/2 .
文摘Brazing is a suitable technology to join different materials such as cemented carbides and steel. Even though this technology has been investigated for many years, insufficient joints can occur easily, as the brazing process is very sensitive concerning the handling parameters. Defects such as voids and cracks are hard to detect by commonly used visual inspection methods. Other nondestructive methods such as radiography or ultrasonic testing are usually not economical for the examination of these joints. Studies proved that the electrical resistance has the potential to serve as an effective alternative for the evaluation of brazed joints. In this study, the authors have compared the electrical resistance and the shear strength. For this, cemented carbides were brazed to steel by means of induction heating at an ambient atmosphere. A silver-based filler metal ( BrazeTec 4900 / Ag 449 ) and a flux ( BrazeTec spezial h / FH12) were selected to enable the brazing process. The brazing time and the temperature were varied in order to produce different joint qualities. After brazing, the resistance was measured on each joint with the 4-point probe method to facilitate a high accuracy. The results underline the possibility to use electrical resistance measurements as an effective tool for a quality control of brazed joints.
文摘The morphology,structure and distribution of the rare earth compounds in the YG8R.YT5R and YT14R cemented carbides with additions of trace light rare earths were studied with an analytical electron microscope. The particles of the rare earth compounds in these alloys are all spherical and distribute at interfaces between the Co-cement phase and WC hard phase or(TiW)C solid solution,and in the(TiW)C solid solution.In the YG8R and YTI4R alloys,the rare earth compound is RE_2O_3 with a bcc structure,while in the YT5R alloy. the rare earth compound is RE_2O_2S with a hcp structure.
文摘A Cemented Carbide material was implanted with dual nitrogen plus tantalum ions at temperatures of 100℃ and 400℃ and a dose of 8× 10^17 ions cm^-2. The thickness of the implanted layers increased by about an order of magnitude when the temperature was elevated from 100℃ to 400℃. Higher surface hardness was also obtained in the high temperature implantation. X-ray diffraction showed the presence of nitrides of tantalum and tungsten in the implanted surface.
文摘A new kind of sintering process, combined sintering process. i.e. vacuum sintering plus hot isolate pressure sintering (HIP), was introduced for producing ultrafine WC-10% Co (mass fraction. so as the follows) cemented carbides. The effects of some processing parameters on the microstructure and mechanical properties of the obtained cemented carbides were studied. The results show that the rapid shrinkage and the pronounced densification of tile cemented carbides took place during the vacuum sintering stage, which is intinaately correlated with the local liquid sintering occurred during this earl} sintering stage for the high surface activity of ultrafine WC-Co powder. The way of high pressure imposing. isothermal treatment cycle during ac.acuum sintering and HIP sintering stage directly influence the densitication of compacts and the mechanical properties of the produced WC-10%Co cemented carbides.