As one of the most promising photoanode candidates for photoelectrochemical(PEC)water splitting,the photocurrent density of BiVO_(4) still needs to be further improved in order to meet the practical application.In thi...As one of the most promising photoanode candidates for photoelectrochemical(PEC)water splitting,the photocurrent density of BiVO_(4) still needs to be further improved in order to meet the practical application.In this work,a highly‐matched BiVO_(4)/WO_(3) nanobowl(NB)photoanode was constructed to enhance charge separation at the interface of the junction.Upon further modification of the BiVO_(4)/WO_(3)NB surface by NiOOH/FeOOH as an oxygen evolution cocatalyst(OEC)layer,a high photocurrent density of 3.05 mA cm^(−2) at 1.23 V vs.RHE has been achieved,which is about 5‐fold higher than pristine BiVO_(4) in neutral medium under AM 1.5 G illumination.5 times higher IPCE at 450 nm is also achieved compared with the BiVO_(4) photoanode,leading to about 95%faradaic efficiency for both H_(2) and O_(2) gas production.Systematic studies attribute the significantly enhanced PEC performance to the smaller BiVO_(4) particle size(<90 nm)than its hole diffusion length(~100 nm),the improved charge separation of BiVO_(4) by the single layer WO_(3) nanobowl array and the function of OEC layers.Such WO_(3)NB possesses much smaller interface resistance with the substrate FTO glass and larger contact area with BiVO_(4) nanoparticles.This approach provides new insights to design and fabricate BiVO_(4)‐based heterojunction photoanode for higher PEC water splitting performance.展开更多
文摘As one of the most promising photoanode candidates for photoelectrochemical(PEC)water splitting,the photocurrent density of BiVO_(4) still needs to be further improved in order to meet the practical application.In this work,a highly‐matched BiVO_(4)/WO_(3) nanobowl(NB)photoanode was constructed to enhance charge separation at the interface of the junction.Upon further modification of the BiVO_(4)/WO_(3)NB surface by NiOOH/FeOOH as an oxygen evolution cocatalyst(OEC)layer,a high photocurrent density of 3.05 mA cm^(−2) at 1.23 V vs.RHE has been achieved,which is about 5‐fold higher than pristine BiVO_(4) in neutral medium under AM 1.5 G illumination.5 times higher IPCE at 450 nm is also achieved compared with the BiVO_(4) photoanode,leading to about 95%faradaic efficiency for both H_(2) and O_(2) gas production.Systematic studies attribute the significantly enhanced PEC performance to the smaller BiVO_(4) particle size(<90 nm)than its hole diffusion length(~100 nm),the improved charge separation of BiVO_(4) by the single layer WO_(3) nanobowl array and the function of OEC layers.Such WO_(3)NB possesses much smaller interface resistance with the substrate FTO glass and larger contact area with BiVO_(4) nanoparticles.This approach provides new insights to design and fabricate BiVO_(4)‐based heterojunction photoanode for higher PEC water splitting performance.