INFLUENCING FACTORS FOR OBTAINING ULTRAFINE AUSTENITE GRAINS WITH INITIAL MICROSTRUCTURE OF WARM-ROLLED FERRITE/PEARLITE 被引量:2
1
作者 S.J. Yao L.X. Du X.H. Liu G.D. Wang 《Acta Metallurgica Sinica(English Letters)》 SCIE EI CAS CSCD 2008年第6期391-398,共8页
Three warm-rolled ferrite/pearlite microstructures were prepared by rolling at 500℃, and the austenitizing characteristics were discussed in conjunction with deformation during the heating stage. The results indicate... Three warm-rolled ferrite/pearlite microstructures were prepared by rolling at 500℃, and the austenitizing characteristics were discussed in conjunction with deformation during the heating stage. The results indicated that the final austenite grain size was sensitive to the deformation direction of the initial warm-rolled microstructure. The transient microstructure at a given temperature was the most important influencing factor on the austenitizing characteristic combined with deformation. Moreover, the hot-rolled mierostructure also had to be prepared in an optimal state because of its direct effect on the warm-rolled microstructure. 展开更多
关键词 warm-rolled ferrite/pearlite AUSTENITE Deformation RECRYSTALLIZATION
下载PDF
The Influence of Abnormal Segregation Band on Mechanical Properties of Hot Rolled Ferrite/Pearlite Steel Plate 被引量:1
2
作者 Rui Feng Benkui Gong +2 位作者 Hongwei Cui Yaokun Pan Jiahui Bao 《Materials Sciences and Applications》 2018年第1期81-91,共11页
In order to further reveal the influence of abnormal segregation band on mechanical properties of hot rolled ferrite/pearlite steel plate, especially on laminated tensile fracture, the experimental method of delaminat... In order to further reveal the influence of abnormal segregation band on mechanical properties of hot rolled ferrite/pearlite steel plate, especially on laminated tensile fracture, the experimental method of delamination tension was adopted. In this paper, the thin tensile samples with 3 mm thickness from the surface, 1/4 positions and center along the thickness orientation of test plate were measured, also the relationship between microstructure and mechanical properties was probed. The results show that the center region of hot rolled ferrite/pearlite steel plate exists granular bainite and ferrite mixed grains, which leads to lower plasticity and toughness of this region. During the tensile process, microcracks are generated and extended at the center of steel plate due to the inconsistency of deformation and fracture on the adjacent structures, finally leading to laminated fracture of steel plate. 展开更多
关键词 ferrite/pearlite Steel Plate SEGREGATION Microstructure LAMINATED FRACTURE
下载PDF
Predication of Plastic Flow Characteristics in Ferrite/Pearlite Steel Using a Fern Unit Cell Method
3
作者 Hong Li Jingtao Han Jing Liu Lv Zhang 《上海交通大学学报》 EI CAS CSCD 北大核心 2004年第z2期61-66,共6页
The flow stress of ferrite/pearlite steel under uni-axial tension was simulated with finite element method (FEM) by applying commercial software MARC/MENTAT. Flow stress curves of ferrite/pearlite steels were calculat... The flow stress of ferrite/pearlite steel under uni-axial tension was simulated with finite element method (FEM) by applying commercial software MARC/MENTAT. Flow stress curves of ferrite/pearlite steels were calculated based on unit cell model. The effects of volume fraction, distribution and the aspect ratio of pearlite on tensile properties have been investigated. 展开更多
关键词 ferrite/pearlite STEEL unit cell flow CURVE FINITE element METHOD simulation
下载PDF
Influence of boron on ferrite formation in copper-added spheroidal graphite cast iron 被引量:1
4
作者 Ying Zou Hideo Nakae 《China Foundry》 SCIE CAS 2014年第4期375-381,共7页
This paper reviews the original work of the authors published recently,describing the influence of B on the matrix of the Cuadded spheroidal graphite cast iron.The effect of Cu has been corrected as a ferrite formatio... This paper reviews the original work of the authors published recently,describing the influence of B on the matrix of the Cuadded spheroidal graphite cast iron.The effect of Cu has been corrected as a ferrite formation promoter in the matrix of the grey cast iron by the usage of high-purity material.Also,this paper focuses on the ferrite formation and the observation of the Cu distribution in the B-added and B-free Cu-containing spheroidal graphite cast iron.The Cu film on the spheroidal graphite can be successfully observed in the B-free sample using a special etching method.However,in the B-added sample,no Cu film could be found,while the secondary graphite was formed on the surface of the spheroidal graphite.The interaction between B and Cu is stressed as a peculiar phenomenon by the employment of a contrast experiment of B and Mn.The heat treatment could make Cu precipitate more significantly in the eutectic cells and in the matrix in the form of large Cu particles because of the limited solubility of Cu. 展开更多
关键词 spheroidal graphite cast iron CU B pearlite formation ferrite formation Cu distribution
下载PDF
Sb微合金化QT600-10铸件的生产技术
5
作者 焦凯 陈振江 +5 位作者 付岳楼 刘海 赵利飞 高伟龙 韩艳妮 马雪峰 《铸造设备与工艺》 2024年第5期49-52,共4页
研究了一种低成本Sb微合金化QT600-10铸件生产技术,并分析了Sb含量对铸件显微组织和力学性能的影响。结果表明,通过控制铁液化学成分,并添加适量Sb,采用合理的球化和孕育工艺,可以获得符合QT600-10标准的铸件,其珠光体含量可达55%.Sb的... 研究了一种低成本Sb微合金化QT600-10铸件生产技术,并分析了Sb含量对铸件显微组织和力学性能的影响。结果表明,通过控制铁液化学成分,并添加适量Sb,采用合理的球化和孕育工艺,可以获得符合QT600-10标准的铸件,其珠光体含量可达55%.Sb的添加促进了石墨的圆整化,并随着Sb含量的增加,珠光体含量也增加,从而显著提高了铸件的抗拉强度、屈服强度和硬度。然而,当Sb含量超过0.008 wt.%时,铸件的延伸率将无法满足QT600-10标准的要求。本研究为低成本生产高性能QT600-10铸件提供了一种新的技术途径。 展开更多
关键词 低成本 QT600-10 SB 珠光体-铁素体基体 力学性能
下载PDF
Hydrogen-assisted fracture features of a high strength ferrite-pearlite steel 被引量:4
6
作者 Yuefengjiang Bo Zhang +4 位作者 Dongying Wang Yu Zhou Jianqiu Wang En-Hou Han Wei Ke 《Journal of Materials Science & Technology》 SCIE EI CAS CSCD 2019年第6期1081-1087,共7页
Up to now, the exact reason of hydrogen-induced fracture for ferrite-pearlite(FP) steel is still not fully understood. This study presents detail observations of the feature beneath the fracture surface with the aim t... Up to now, the exact reason of hydrogen-induced fracture for ferrite-pearlite(FP) steel is still not fully understood. This study presents detail observations of the feature beneath the fracture surface with the aim to reveal the hydrogen-induced cracking initiation and propagation processes. Slow strain rate tensile(SSRT) testing shows that the FP steel is sensitive to hydrogen embrittlement(HE). Focused ion beam(FIB)was used to prepare samples for TEM observations after HE fracture. The corresponding fractographic morphologies of hydrogen charged specimen exhibit intergranular(IG) and quasi-cleavage(QC) fracture feature. Pearlite colony, ferrite/pearlite(F/P) boundary and the adjacent ferrite matrix are found to be responsible for the initial HE fracture and the subsequent propagation. With increasing of the stress intensity factor, fracture mode is found to change from mixed IG and QC to entire QC feature which only occurs at the ferrite matrix. No crack is observed at the ferrite/cementite(F/C) interface. This may be mainly due to the limited pearlite lamella size and relatively low interface energy. 展开更多
关键词 ferrite-pearlite STEEL TEM FRACTURE HYDROGEN EMBRITTLEMENT
原文传递
Characteristic of Near-surface Microstructure and Its Effects on the Torsion Performance of Cold Drawn Pearlitic Steel Wires for Bridge Cables
7
作者 ZHANG Fan MAO Xinping +6 位作者 BAO Siqian ZHAO Gang ZHAO Sixin DENG Zhaojun HE Meng HUANG Fangyu QU Xi 《Journal of Wuhan University of Technology(Materials Science)》 SCIE EI CAS 2022年第5期992-999,共8页
The characteristic of near-surface microstructure and its effects on the torsion performance of cold-drawn pearlitic steel wires for bridge cables were investigated by focused ion beam-scanning electron microscope,tra... The characteristic of near-surface microstructure and its effects on the torsion performance of cold-drawn pearlitic steel wires for bridge cables were investigated by focused ion beam-scanning electron microscope,transmission electron microscopy and differential scanning calorimetry.The samples with similar tensile strength before and after hot-dip galvanizing process are,respectively,characterized as delaminated and non-delaminated in torsion test which indicates that the tensile strength is independent of the toughness value(i e,reduction area and torsion ability).It is interesting to find that there exists submicron granular ferrite on near-surface of the wires,which can be attributed to dislocation rearrangement and sub-grains rotation during cold drawing and hot-dip galvanizing process.And their distribution can suggest homogeneousness of deformation degree to a certain extent:the closer to the surface of their distribution,the more homogeneous deformation of the wires.There is a close relationship between the thermal stability of the cementite layer and distribution of granular ferrite:differential scanning calorimetry(DSC)analysis shows that the sample is accompanied by submicron granular ferrite which is located closer to the surface has higher thermal stability under galvanizing temperature(450°C).A new mechanism of the torsion delamination of pearlitic steel wires is discussed in terms of the thermal stability of the cementite layer and distribution of granular ferrite. 展开更多
关键词 cold-drawn pearlite steel wires torsion performance near-surface microstructure submicron granular ferrite
下载PDF
Prediction of mechanical behavior of ferrite-pearlite steel
8
作者 Lei Wang Di Tang Yong Song 《Journal of Iron and Steel Research International》 SCIE EI CAS CSCD 2017年第3期321-327,共7页
A new approach describing the flow stress of ferrite-pearlite steel has been proposed,which divided the deformation process into three stages based on whether ferrite or pearlite yielded. Iso-work increment assumption... A new approach describing the flow stress of ferrite-pearlite steel has been proposed,which divided the deformation process into three stages based on whether ferrite or pearlite yielded. Iso-work increment assumption was applied to describe the transfer of load between the components. The physically based model to describe ferrite was approximated with Swift's equation in order to obtain the analytic solution.The tensile strength of ferrite-pearlite had a linear relation with pearlite volume fraction,square root reciprocal of ferrite grain size and reciprocal of pearlite interlamellar spacing. Moreover,a model to calculate the tensile strength of ferrite-pearlite steel was proposed. The predicted values of tensile strength were in good agreement with experimental results when the pearlite volume fraction was less than 20%.Considering the plastic relaxation mechanisms,the internal stress was modified with pearlite volume fraction,total strain,yield stress of ferrite and pearlite when the pearlite volume fraction was more than 20%. 展开更多
关键词 MODELING ferrite-pearlite steel Flow stress Tensile strength Internal stress
原文传递
某中碳钢的组织与拉伸性能的关系 被引量:1
9
作者 朱飞 林俊 +2 位作者 李仕超 谢有 邓向阳 《材料热处理学报》 CAS CSCD 北大核心 2023年第2期118-126,共9页
首先对某中碳钢进行不同工艺的热处理,获得了不同的原奥氏体晶粒尺寸。利用光学显微镜、扫描电镜及拉伸性能测试等研究了原奥氏体晶粒尺寸及冷速对试验钢铁素体-珠光体组织及拉伸性能的影响,并研究了试验钢的组织与性能之间的关系。结... 首先对某中碳钢进行不同工艺的热处理,获得了不同的原奥氏体晶粒尺寸。利用光学显微镜、扫描电镜及拉伸性能测试等研究了原奥氏体晶粒尺寸及冷速对试验钢铁素体-珠光体组织及拉伸性能的影响,并研究了试验钢的组织与性能之间的关系。结果表明:冷速对试验钢铁素体-珠光体组织的影响远大于原奥氏体晶粒尺寸。随冷却速率增加,先共析铁素体形貌由等轴状向不闭合网状过渡,先共析铁素体含量和尺寸分别由16.3 vol%、16.4μm降低至1.0 vol%、4.1μm,珠光体含量由83.7 vol%逐渐增加至99.0 vol%,珠光体平均片层间距由419 nm逐渐降低至174 nm。不同铁素体-珠光体组织试验钢的拉伸强度与布氏硬度满足线性拟合关系。试验钢抗拉强度测试值与考虑到退化珠光体存在的某数学模型符合较好。因先共析铁素体含量(形貌)、组织细化、珠光体含量及片层间距等因素的共同影响,试验钢断后伸长率与断面收缩率的变化随冷速的变化并不一致。 展开更多
关键词 中碳钢 铁素体-珠光体 片层间距 组织定量 冷却速率
下载PDF
变形温度对45#精冲钢组织演变的影响
10
作者 张晓磊 张明博 +4 位作者 窦双江 张志新 齐敏 吴红艳 杜林秀 《河北冶金》 2023年第1期29-34,共6页
利用热模拟单道次压缩实验研究了45#钢在不同温度变形过程中微观组织的演变规律。通过对变形过程中组织形貌的观察和应力-应变曲线的分析,讨论了变形过程中的相变行为和软化过程。结果显示,实验钢在热变形过程发生铁素体(DIF)和珠光体(D... 利用热模拟单道次压缩实验研究了45#钢在不同温度变形过程中微观组织的演变规律。通过对变形过程中组织形貌的观察和应力-应变曲线的分析,讨论了变形过程中的相变行为和软化过程。结果显示,实验钢在热变形过程发生铁素体(DIF)和珠光体(DIP)两种形变诱导相变,Ar3温度以上变形时,主要发生形变诱导铁素体相变,伴随少量珠光体生成,并且随着变形温度的降低铁素体增加,珠光体略微降低;Ar3温度以下变形时,形变诱导珠光体逐渐取代铁素体,且随温度的变化趋势相反。低温变形时,形变诱导相变是软化的主要原因,高温变形时主要发生动态再结晶,导致软化,并且动态再结晶的软化作用要比形变诱导相变的好。 展开更多
关键词 45#钢 亚共析钢 热模拟 形变诱导相变 奥氏体 珠光体 铁素体
下载PDF
铁素体/珠光体组织对管线钢中氢扩散行为的影响
11
作者 王晓霖 程光 +1 位作者 李世瀚 杨静 《力学与实践》 北大核心 2023年第2期305-313,共9页
长距离管道输送是氢气输送的重要发展方向之一。氢在管线钢的扩散和局部聚集导致材料力学性能下降,在外界作用下引发脆性失效。因此,氢在管线钢材中的扩散和富集是评价管线钢相容性与判断管道升级可行性的重要参考依据。以三种不同等级... 长距离管道输送是氢气输送的重要发展方向之一。氢在管线钢的扩散和局部聚集导致材料力学性能下降,在外界作用下引发脆性失效。因此,氢在管线钢材中的扩散和富集是评价管线钢相容性与判断管道升级可行性的重要参考依据。以三种不同等级的管线钢(X52,X65,X70)共22种材料为研究对象,结合图像处理技术与基于材料内铁素体/珠光体组织结构的连续介质数值计算,推算长期服役后结构内部氢的扩散和富集。考虑到铁素体和珠光体组织中的氢扩散速率与晶界的扩散阻碍作用,通过对比量化不同铁素体/珠光体的结构分布和组织取向下氢质量浓度和扩散通量的差异,分析铁素体/珠光体组织对管线钢中氢的扩散和富集作用,为长距离输氢管道材料选用提供技术参考。 展开更多
关键词 管线钢 微观结构 铁素体/珠光体 氢扩散 有限元模拟
下载PDF
超高强抗震钢筋弯曲断裂原因
12
作者 田伟 李博 +2 位作者 李娜 李强刚 林生秀 《理化检验(物理分册)》 CAS 2023年第5期30-33,36,共5页
超高强抗震钢筋在进行弯曲试验时发生断裂。采用宏观观察、化学成分分析、扫描电镜分析、金相检验、中心偏析检验等方法,对弯曲试样断裂的原因进行分析。结果表明:热轧前加热温度较高,变形后奥氏体晶粒长大,使得珠光体团尺寸增大、珠光... 超高强抗震钢筋在进行弯曲试验时发生断裂。采用宏观观察、化学成分分析、扫描电镜分析、金相检验、中心偏析检验等方法,对弯曲试样断裂的原因进行分析。结果表明:热轧前加热温度较高,变形后奥氏体晶粒长大,使得珠光体团尺寸增大、珠光体含量增多;冷却缓慢导致网状铁素体沿奥氏体晶界析出,使材料的塑性和韧性下降,最终导致试样在弯曲试验时发生断裂。 展开更多
关键词 超高强抗震钢筋 弯曲断裂 珠光体团 网状铁素体
下载PDF
薄板坯连铸连轧65Mn钢的热轧组织与力学性能 被引量:15
13
作者 黄刚 焦国华 +4 位作者 温德智 周春泉 陈建新 周明伟 吴开明 《材料工程》 EI CAS CSCD 北大核心 2010年第8期72-77,共6页
利用光学显微镜,扫描电子显微镜(SEM),透射电子显微镜(TEM)和拉伸试验机,硬度仪分析薄板坯连铸连轧工艺CSP生产的高碳高强度钢65Mn的热轧板微观组织与力学性能。该钢主要由珠光体和少量多边形铁素体组成,珠光体片层间距在0.2-0.5μ... 利用光学显微镜,扫描电子显微镜(SEM),透射电子显微镜(TEM)和拉伸试验机,硬度仪分析薄板坯连铸连轧工艺CSP生产的高碳高强度钢65Mn的热轧板微观组织与力学性能。该钢主要由珠光体和少量多边形铁素体组成,珠光体片层间距在0.2-0.5μm之间。该钢的平均屈服强度为489MPa,硬度为HRC22.3,伸长率达到18%;没有明显的C和Mn元素偏析,力学性能分布均匀。通过与传统连铸工艺生产的65Mn钢热轧组织与力学性能对比,CSP工艺生产的65Mn钢的组织更加细小,性能更加优良和均匀。 展开更多
关键词 CSP 珠光体 铁素体 高强度钢
下载PDF
形变参数对中碳钢组织演变的影响 被引量:18
14
作者 田鹏 惠卫军 +3 位作者 刘荣佩 张步海 于同仁 苏世怀 《材料热处理学报》 EI CAS CSCD 北大核心 2005年第4期69-73,共5页
通过热模拟实验研究了不同形变温度及在700℃下不同形变量时中碳钢35K的组织演变过程。结果表明,中碳钢通过形变可获得形变诱导铁素体(DIF);形变提高奥氏体向铁素体转变温度,随着形变温度的降低,DIF含量呈反“S”形增加,即先缓慢增加,... 通过热模拟实验研究了不同形变温度及在700℃下不同形变量时中碳钢35K的组织演变过程。结果表明,中碳钢通过形变可获得形变诱导铁素体(DIF);形变提高奥氏体向铁素体转变温度,随着形变温度的降低,DIF含量呈反“S”形增加,即先缓慢增加,随后快速增加,当DIF量超过平衡态铁素体量时,其增加趋势趋缓。随700℃形变量的增加,DIF含量呈“S”形增加,在形变量为0.7时可获得良好的球化组织。在中碳钢形变后的控冷过程中,根据形变量和形变温度所影响的未转变的奥氏体尺寸、形变储能、富碳程度和能量与成分起伏等,未转变的奥氏体将发生不同于传统未变形奥氏体的转变。因此,控制轧制和控制冷却后可获得离异珠光体、球粒状或短棒状渗碳体的微观组织。 展开更多
关键词 中碳钢 热模拟 组织演变 形变诱导铁素体
下载PDF
低碳低合金钢的连续冷却相变组织特征及其形成机制 被引量:22
15
作者 王立军 蔡庆伍 +2 位作者 余伟 武会宾 雷爱娣 《材料工程》 EI CAS CSCD 北大核心 2010年第8期29-33,共5页
利用Formastor-Digital全自动相变仪测定低碳Mn,Ni,Mo,Cr,V,Ti等低合金化钢的静态CCT曲线,结合光学显微镜、透射电镜、显微硬度法分析冷却速率对相变组织演变规律的影响。结果表明:当冷速为0.03℃/s时,相变组织为多边形铁素体(PF)+珠光... 利用Formastor-Digital全自动相变仪测定低碳Mn,Ni,Mo,Cr,V,Ti等低合金化钢的静态CCT曲线,结合光学显微镜、透射电镜、显微硬度法分析冷却速率对相变组织演变规律的影响。结果表明:当冷速为0.03℃/s时,相变组织为多边形铁素体(PF)+珠光体(P);冷速为0.06℃/s时,出现退化珠光体(PD);冷速为0.29℃/s时,出现针状铁素体(AF);冷速为1.7℃/s时,组织为粒状贝氏体(GB)+板条贝氏体(LB);冷速为42℃/s时,出现马氏体(M)。提出极低冷速下低碳钢中出现退化珠光体是由于多元低合金元素的耦合交互作用,引起碳活度的变化所致。针状铁素体在晶内形核并长大,对后续相变组织起到分割作用,利于细化组织。低碳钢中局部孪生马氏体的形成归因于淬透性元素聚集对钢局域相变切应力过大所致。 展开更多
关键词 连续冷却相变 低碳 退化珠光体 针状铁素体 组织
下载PDF
管线钢的研究进展 被引量:19
16
作者 高惠临 张骁勇 +3 位作者 冯耀荣 霍春勇 吉玲康 李为卫 《机械工程材料》 CAS CSCD 北大核心 2009年第10期1-4,16,共5页
根据材料的显微组织将管线钢分为四种类型,即铁素体-珠光体管线钢、针状铁素体管线钢、贝氏体-马氏体管线钢和回火索氏体管线钢;并以此为线索介绍了该四类管线钢的化学成分、显微组织和性能,综述了管线钢的发展历程。
关键词 管线钢 铁素体-珠光体 针状铁素体 贝氏体-马氏体 回火索氏体
下载PDF
超细晶粒钢的显微组织 被引量:12
17
作者 宋立秋 侯豁然 +4 位作者 左军 王义成 刘清友 张开坚 董瀚 《钢铁钒钛》 CAS 北大核心 2003年第3期32-36,共5页
分析了以普碳钢成分生产的超细晶粒钢的显微组织。结果表明:工业生产的超细晶粒钢的显微组织由铁素体和珠光体组成,铁素体的晶粒尺寸为4~5μm,组织中珠光体所占体积分数较低。珠光体中渗碳体以短棒状或颗粒状存在,细小的铁素体晶粒使... 分析了以普碳钢成分生产的超细晶粒钢的显微组织。结果表明:工业生产的超细晶粒钢的显微组织由铁素体和珠光体组成,铁素体的晶粒尺寸为4~5μm,组织中珠光体所占体积分数较低。珠光体中渗碳体以短棒状或颗粒状存在,细小的铁素体晶粒使晶粒内的位错塞积密度减少,有利于提高钢的强度和韧性。 展开更多
关键词 超细晶粒钢 铁素体 珠光体
下载PDF
普通C-Mn钢超细晶中厚板的带状组织 被引量:29
18
作者 范建文 谢瑞萍 +3 位作者 张维旭 代晓莉 金永春 王祖滨 《钢铁》 CAS CSCD 北大核心 2004年第8期100-104,共5页
采用Gleeble2000热模拟试验机研究了普通C-Mn钢的再结晶规律,在实验室轧机上进行了C-Mn钢超细晶中板的轧制,并且在首钢中厚板厂工业轧机上进行了超细晶中厚板的工业试制,研究了工艺条件对中厚板带状组织的影响,分析了带状组织产生的机理... 采用Gleeble2000热模拟试验机研究了普通C-Mn钢的再结晶规律,在实验室轧机上进行了C-Mn钢超细晶中板的轧制,并且在首钢中厚板厂工业轧机上进行了超细晶中厚板的工业试制,研究了工艺条件对中厚板带状组织的影响,分析了带状组织产生的机理.研究结果表明,在靠近静态相变温度Ara附近的未再结晶区进行大变形量轧制(形变诱导相变),不仅可以使板材的铁素体晶粒细化甚至获得超细晶组织,而且普通C-Mn钢中厚板中的带状组织减轻1~2级;降低精轧开轧温度有利于减轻板材的带状组织;在未再结晶区控轧有利于减轻板材的带状组织;随着未再结晶区形变量增加,板材的带状组织减弱. 展开更多
关键词 超细晶 带状组织 普通碳锰钢 中厚板轧制
下载PDF
Si对过共析锰钢力学性能及晶界组织的影响 被引量:6
19
作者 朱晓东 李承基 +2 位作者 章守华 邹明 苏世怀 《金属学报》 SCIE EI CAS CSCD 北大核心 1996年第11期1130-1138,共9页
本文用SEM,TEM研究了Si对过共析锰钢经950℃(>Acm)奥氏体化和560℃等温处理后的组织及力学性能的影响结果表明,Si提高冲击韧性和延伸率,抑制先共析渗碳体在奥氏体晶界呈连续网状析出,并促进在过共析钢中晶界... 本文用SEM,TEM研究了Si对过共析锰钢经950℃(>Acm)奥氏体化和560℃等温处理后的组织及力学性能的影响结果表明,Si提高冲击韧性和延伸率,抑制先共析渗碳体在奥氏体晶界呈连续网状析出,并促进在过共析钢中晶界铁素体的形成.本文重点讨论了含Si过共析钢中晶界铁素体的形成机理及其对韧性的影响. 展开更多
关键词 过共析钢 晶界 铁素体 珠光体
下载PDF
控轧控冷参数对含铌微合金钢组织的影响 被引量:10
20
作者 贾志鑫 衣海龙 +3 位作者 刘嵩韬 杜林秀 王国栋 刘相华 《机械工程材料》 CAS CSCD 北大核心 2006年第9期7-9,共3页
利用Gleeble-1500型热模拟试验机研究了含铌微合金钢在不同控轧控冷参数下组织的变化规律。结果表明:低温变形由于引发了形变诱导铁素体相变,对珠光体转变的促进作用更加明显;珠光体片层间距随变形温度的升高而减小,并且随冷却速率增... 利用Gleeble-1500型热模拟试验机研究了含铌微合金钢在不同控轧控冷参数下组织的变化规律。结果表明:低温变形由于引发了形变诱导铁素体相变,对珠光体转变的促进作用更加明显;珠光体片层间距随变形温度的升高而减小,并且随冷却速率增加明显减小;高温变形扩大了贝氏体相变的冷速区间,低温变形由于引发形变诱导铁素体相变,对贝氏体相变起到了抑制作用。 展开更多
关键词 形变诱导相变 含铌微合金钢 珠光体 贝氏体