Corrosion Resistance of Graphene-Reinforced Waterborne Epoxy Coatings

Graphene （G） was dispersed uniformly in water and used as an inhibitor in waterborne epoxy coatings. The effect of dispersed G on anticorrosion performance of epoxy coatings was evaluated. The composite coatings displayed outstanding barrier properties against H20 molecule compared to the neat epoxy coating. Open circuit potential （OCP）, Tafel and electrochemical impedance spectroscopy （EIS） analysis confirmed that the corrosion rate exhibited by composite coatings with 0.5 wt% G was an order of magnitude lower than that of neat epoxy coating. Salt spray test results revealed superior corrosion resistance offered by the composite coating.

多壁碳纳米管改性环氧涂层的防腐蚀性能

研究了多壁碳纳米管(multiwalled carbon nanotubes,MWCNTS)在环氧涂层中的分散性对涂层耐蚀性能的影响。采用电化学阻抗谱对未添加任何填料的环氧涂层、添加原始MWCNTS的环氧涂层和添加改性MWCNTS的环氧涂层等三种涂层体系进行了耐蚀性评价。结果表明,随着在电解质溶液中浸泡时间的延长,三种涂层体系的阻抗值都降低,对比涂层阻抗谱变化以及失效时间,添加改性MWCNTS的环氧涂层体系耐蚀性最佳。

环氧铝粉涂层和氟碳涂层耐蚀性能的比较

采用电化学阻抗谱技术(EIS)研究了环氧铝粉涂层和FEVE氟碳涂层/碳钢体系在天然海水介质中的电化学腐蚀行为,通过对两涂层的涂层电容分析及腐蚀后表面形貌的观察,评价了两种有机涂层的防腐蚀性能。结果表明,随着浸泡时间的延长,两种有机涂层体系的保护作用都有所降低。环氧铝粉涂层在浸泡初期呈现单容抗弧特征,浸泡57天时出现了双容抗弧。氟碳涂层在浸泡周期内EIS曲线均呈现单容抗弧特征,浸泡110天时低频阻抗模值仍高于108Ω.cm2。在整个浸泡周期内,氟碳涂层的涂层电容基本维持在1.6×10-10～1.8×10-10 F.cm-2,约为环氧铝粉涂层电容的1/20,表现出低渗水性。

环氧基水性带锈防腐涂料的制备及性能研究

针对输变电钢结构腐蚀问题提供了一种基于水性环氧树脂的带锈防腐涂料。研究防锈颜料、填料、共溶剂对涂料附着力和耐盐雾性能的影响。采用傅里叶变换红外光谱与扫描电子显微镜对漆膜的成分及形貌进行表征。通过电化学交流阻抗测试了漆膜的耐腐蚀性能,分析漆膜的防腐机理。试验结果表明,涂料在带锈钢板上的附着力达到8 MPa,耐中性盐雾达到500 h。三聚磷酸铝可以有效建立防腐保护膜,而锌粉可以在保护膜形成的过程中起到有效的阴极保护作用,提升漆膜的耐腐蚀性能。