The modified petroleum resin emulsion prepared from the C9petroleum resin was modified with maleic anhydride.The effects of maleic rosin and maleic anhydride addition level,the modification time and the alkali liquor ...The modified petroleum resin emulsion prepared from the C9petroleum resin was modified with maleic anhydride.The effects of maleic rosin and maleic anhydride addition level,the modification time and the alkali liquor on the properties of the emulsion were discussed.The results showed that the optimum process conditions covered:a maleic anhydride mass fraction of 1.5%,a maleic rosin mass fraction of 10%,a KOH mass fraction of 1%,a petroleum resin modification temperature of 200℃,a petroleum resin modification duration of 3 h,and a modified petroleum resin emulsion/wax emulsion mixing ratio of 1:1.The particle size of modified petroleum resin emulsion prepared under these conditions was equal to 104.166μm.展开更多
Early water damage of asphalt pavement is one of the major types of destruction,so taking maintenance on asphalt pavement at the proper time is necessary. Many new maintenance materials and methods are in use nowadays...Early water damage of asphalt pavement is one of the major types of destruction,so taking maintenance on asphalt pavement at the proper time is necessary. Many new maintenance materials and methods are in use nowadays to prevent pavement from water damage and skidding. This paper aims to study the effects of the silicone maintenance materials on thermal aging resistance of asphalt mixture. After thermal aging,the asphalt mixture using silicone materials and the control mixture are evaluated through their engineering properties,including indirect tensile modulus,low-temperature performance and fatigue resistance. The results indicate that the silicone materials used as repairing material can improve low-temperature performance and fatigue resistance of asphalt mixture,and decrease the indirect tensile modulus ratio before and after thermal aging. Consequently,the silicone maintenance material has the ability to protect asphalt mixture from thermal aging.展开更多
文摘The modified petroleum resin emulsion prepared from the C9petroleum resin was modified with maleic anhydride.The effects of maleic rosin and maleic anhydride addition level,the modification time and the alkali liquor on the properties of the emulsion were discussed.The results showed that the optimum process conditions covered:a maleic anhydride mass fraction of 1.5%,a maleic rosin mass fraction of 10%,a KOH mass fraction of 1%,a petroleum resin modification temperature of 200℃,a petroleum resin modification duration of 3 h,and a modified petroleum resin emulsion/wax emulsion mixing ratio of 1:1.The particle size of modified petroleum resin emulsion prepared under these conditions was equal to 104.166μm.
基金Key Laboratory of Silicate Materials Science and Engineering for its financial support of this project.
文摘Early water damage of asphalt pavement is one of the major types of destruction,so taking maintenance on asphalt pavement at the proper time is necessary. Many new maintenance materials and methods are in use nowadays to prevent pavement from water damage and skidding. This paper aims to study the effects of the silicone maintenance materials on thermal aging resistance of asphalt mixture. After thermal aging,the asphalt mixture using silicone materials and the control mixture are evaluated through their engineering properties,including indirect tensile modulus,low-temperature performance and fatigue resistance. The results indicate that the silicone materials used as repairing material can improve low-temperature performance and fatigue resistance of asphalt mixture,and decrease the indirect tensile modulus ratio before and after thermal aging. Consequently,the silicone maintenance material has the ability to protect asphalt mixture from thermal aging.