Effect of deep cryogenic treatment on mechanical behavior of a Cu-Cr-Zr alloy for electrodes of spot welding

The effects of deep cryogenic treatment on mechanical behavior of a Cu-Cr-Zr alloy for electrodes of spot welding were investigated employing Brinell-hardness testing unit, abrasion examination machine, electronic almighty testing machine and X-ray stress analyzer. Tensile fracture surfaces of the alloy were characterized by scanning electronic microscope （SEM） with energy dispersive X-ray spectroscopy （EDS）. The results showed that, after deep cryogenic treatment, σb and σ0.2 increased 23 MPa and 21 MPa respectively, the wear rate of the alloy exhibited the trend of decrease with the decreasing temperature and increasing time of deep cryogenic treatment, and the surface residual stress of the alloy was partially eliminated by deep cryogenic treatment.

Modeling, Simulation and Control of Pulsed DE-GMA Welding Process for Joining of Aluminum to Steel

Joining of aluminum to steel has attracted significant attention from the welding research community,automotive and rail transportation industries.Many current welding methods have been developed and applied,however,they can not precisely control the heat input to work-piece,they are high costs,low efficiency and consist lots of complex welding devices,and the generated intermetallic compound layer in weld bead interface is thicker.A novel pulsed double electrode gas metal arc welding（Pulsed DE-GMAW）method is developed.To achieve a stable welding process for joining of aluminum to steel,a mathematical model of coupled arc is established,and a new control scheme that uses the average feedback arc voltage of main loop to adjust the wire feed speed to control coupled arc length is proposed and developed.Then,the impulse control simulation of coupled arc length,wire feed speed and wire extension is conducted to demonstrate the mathematical model and predict the stability of welding process by changing the distance of contact tip to work-piece（CTWD）.To prove the proposed PSO based PID control scheme’s feasibility,the rapid prototyping experimental system is setup and the bead-on-plate control experiments are conducted to join aluminum to steel.The impulse control simulation shows that the established model can accurately represent the variation of coupled arc length,wire feed speed and the average main arc voltage when the welding process is disturbed,and the developed controller has a faster response and adjustment,only runs about 0.1 s.The captured electric signals show the main arc voltage gradually closes to the supposed arc voltage by adjusting the wire feed speed in 0.8 s.The obtained typical current waveform demonstrates that the main current can be reduced by controlling the bypass current under maintaining a relative large total current.The control experiment proves the accuracy of proposed model and feasibility of new control scheme further.The beautiful and smooth weld beads are also obtained by this method.Pulsed DE-GMAW can thus be considered as an alternative method for low cost,high efficiency joining of aluminum to steel.

Self-Adaptive Control System for Additive Manufacturing Using Double Electrode Micro Plasma Arc Welding

Wire arc additive manufacturing(WAAM)has been investigated to deposit large-scale metal parts due to its high deposition efficiency and low material cost.However,in the process of automatically manufacturing the high-quality metal parts by WAAM,several problems about the heat build-up,the deposit-path optimization,and the stability of the process parameters need to be well addressed.To overcome these issues,a new WAAM method based on the double electrode micro plasma arc welding(DE-MPAW)was designed.The circuit principles of different metal-transfer models in the DE-MPAW deposition process were analyzed theoretically.The effects between the parameters,wire feed rate and torch stand-off distance,in the process of WAAM were investigated experimentally.In addition,a real-time DE-MPAW control system was developed to optimize and stabilize the deposition process by self-adaptively changing the wire feed rate and torch stand-off distance.Finally,a series of tests were performed to evaluate the control system’s performance.The results show that the capability against interferences in the process of WAAM has been enhanced by this self-adaptive adjustment system.Further,the deposition paths about the metal part’s layer heights in WAAM are simplified.Finally,the appearance of the WAAM-deposited metal layers is also improved with the use of the control system.

Arc Stability Characterization of Double Coated Electrodes for Hardfacing

The aim of this work is to establish the influence of the relative position of the alloy charge C-Cr-Mn in the structure of the coating of rutile electrodes for hardfacing,on the operational behavior(arc stability).For this,three variants of electrodes with similar chemical composition are elaborated in the metallic core and the coating,differentiating only in the relative position that occupies the alloy charge(C-Cr-Mn)in the structure of the coating:internal,external and homogeneous.For the development of the research,a completely random design is used.The operative characterization of the electrodes is performed in terms of the arc stability.In conclusion,it can be seen that the position of the alloy load influences the operation behavior(stability of the arc).The variant of internal alloy charge in the coating presents the better arc stability performance.

Development of RM-1 type coated electrode for reducing retorts in magnesium refining

According to the working condition of high temperature oxidation and sulphidation corrosion of the ZG35Cr24Ni7SiN heat resisting stainless steel used for reducing retort in magnesium refining, and the practical situation which the weld metal between the body and cover of reducing retort must possess resisting high temperature oxidation and corrosion, a kind of RM 1 type coated electrode for reducing retorts in magnesium refining with special alloying system and excellent usability has been developed. The RM 1 coated electrode is made of H0Cr21Ni10 wire core and is alloyed chromium and nickel simultaneously through coating material and wire core and some rare earth oxides are added in coating material. The electrode has been verified to be satisfied the operation requirements of practical production.