Polyether polyurethane was synthesized from modified wheat straw oxygen-alkaline lignin, polyethylene glycol and two different diisocyanates (diphenylemethane-4, 4’-diisocyanate, tolulene diisocyanate) by solution ca...Polyether polyurethane was synthesized from modified wheat straw oxygen-alkaline lignin, polyethylene glycol and two different diisocyanates (diphenylemethane-4, 4’-diisocyanate, tolulene diisocyanate) by solution casting method, its properties were investigated. The results show that modified wheat straw oxygen-alkaline lignin can substitute part of polyethylene glycol to react with diisocyanate to synthesize polyurethane. The molar ratio of NCO to OH and modified wheat straw oxygen-alkaline lignin content affect the properties of lignin-based polyether polyurethane respectively. The addition of plasticizer in the polyurethane synthesis process improves the properties of synthesized polyurethane, especially the elasticity of polyurethane. The synthesized polyurethane from modified wheat straw oxygen-alkali lignin can be used as both engineering plastic and hard foam plastic in future.展开更多
The aromatic nature of lignin makes it a potential renewable source of chemicals and other valuable products.Isolation of lignin from lignocellulosic biomass using organic solvents enables the production of high-purit...The aromatic nature of lignin makes it a potential renewable source of chemicals and other valuable products.Isolation of lignin from lignocellulosic biomass using organic solvents enables the production of high-purity lignin.The use of formic acid in the organosolv pulping and fractionation process has been widely studied.Characterization of lignin is necessary to achieve valueadded applications of lignin.To simplify the isolation of formic acid-treated lignin,herein,milled wheat straw lignin(MWSL) was employed as an archetype for characterization of the structural changes of lignin during formic acid treatment.The results showed that the MWSL was GSH-type(comprising p-hydroxyphenyl(H),guaiacyl(G),and syringyl(S) monolignols) and underwent structural changes during formic acid treatment.Lignin was esterified during the formic acid treatment.The content of alkyl hydroxyl groups in lignin decreased upon formic acid treatment,corresponding to an increase of the number of double bond equivalents(DBE).Lignin units with active reaction sites were liable to slight condensation,which resulted in a moderate increase of the molecular weight.The molecular weight distribution of formic acid-treated MWSL(FMWSL) was wider than that of the MWSL,although the molecular weight of both species did not differ significantly.The β-O-4 linkage in lignin was partially cleaved during formic acid treatment,resulting in the production of new phenolic structures.This improved the solubility of lignin in the cooking liquor and its reactivity for downstream applications.展开更多
In this paper, a new type of retention system of PEO/cofactor retention system is introduced, the cofactors used are phenol-formaldehyde resin, wheat straw alkaline lignin and its derivatives such as hydroxymethylated...In this paper, a new type of retention system of PEO/cofactor retention system is introduced, the cofactors used are phenol-formaldehyde resin, wheat straw alkaline lignin and its derivatives such as hydroxymethylated lignin, sulfited lignin and lignin-based phenol-formaldehyde resin. The first pass retention of newsprint slurry and the properties of handsheet are improved by using the system. The results indicate that a new application field for lignin has been exploited.展开更多
Characteristics of uncondensed lignin reactions in soda cooking of wheat straw were studied. Mild and intense cooking conditions were used to get the pulp sample in which lignin was dissolved physically and the pulp s...Characteristics of uncondensed lignin reactions in soda cooking of wheat straw were studied. Mild and intense cooking conditions were used to get the pulp sample in which lignin was dissolved physically and the pulp sample in which lignin was dissolved chemically respectively. The pulp samples were analyzed by phenolic group determination, alkaline nitrobenzene oxidation and ozonation method. The results indicated that around 90% of lignin in wheat straw is alkali-soluble at the mild conditions, is basically dissolved physically without chemical change. The phenolic group content was not changed greatly, the nitrobenzene oxidation yield only changed slightly during the mild cooking. The phenolic group content was increased obviously and uncondensed lignin content was decreased very much when the intense cooking conditions were applied and the delignification was over 90%. The lignin structure was changed greatly during this period.展开更多
文摘Polyether polyurethane was synthesized from modified wheat straw oxygen-alkaline lignin, polyethylene glycol and two different diisocyanates (diphenylemethane-4, 4’-diisocyanate, tolulene diisocyanate) by solution casting method, its properties were investigated. The results show that modified wheat straw oxygen-alkaline lignin can substitute part of polyethylene glycol to react with diisocyanate to synthesize polyurethane. The molar ratio of NCO to OH and modified wheat straw oxygen-alkaline lignin content affect the properties of lignin-based polyether polyurethane respectively. The addition of plasticizer in the polyurethane synthesis process improves the properties of synthesized polyurethane, especially the elasticity of polyurethane. The synthesized polyurethane from modified wheat straw oxygen-alkali lignin can be used as both engineering plastic and hard foam plastic in future.
文摘The aromatic nature of lignin makes it a potential renewable source of chemicals and other valuable products.Isolation of lignin from lignocellulosic biomass using organic solvents enables the production of high-purity lignin.The use of formic acid in the organosolv pulping and fractionation process has been widely studied.Characterization of lignin is necessary to achieve valueadded applications of lignin.To simplify the isolation of formic acid-treated lignin,herein,milled wheat straw lignin(MWSL) was employed as an archetype for characterization of the structural changes of lignin during formic acid treatment.The results showed that the MWSL was GSH-type(comprising p-hydroxyphenyl(H),guaiacyl(G),and syringyl(S) monolignols) and underwent structural changes during formic acid treatment.Lignin was esterified during the formic acid treatment.The content of alkyl hydroxyl groups in lignin decreased upon formic acid treatment,corresponding to an increase of the number of double bond equivalents(DBE).Lignin units with active reaction sites were liable to slight condensation,which resulted in a moderate increase of the molecular weight.The molecular weight distribution of formic acid-treated MWSL(FMWSL) was wider than that of the MWSL,although the molecular weight of both species did not differ significantly.The β-O-4 linkage in lignin was partially cleaved during formic acid treatment,resulting in the production of new phenolic structures.This improved the solubility of lignin in the cooking liquor and its reactivity for downstream applications.
文摘In this paper, a new type of retention system of PEO/cofactor retention system is introduced, the cofactors used are phenol-formaldehyde resin, wheat straw alkaline lignin and its derivatives such as hydroxymethylated lignin, sulfited lignin and lignin-based phenol-formaldehyde resin. The first pass retention of newsprint slurry and the properties of handsheet are improved by using the system. The results indicate that a new application field for lignin has been exploited.
文摘Characteristics of uncondensed lignin reactions in soda cooking of wheat straw were studied. Mild and intense cooking conditions were used to get the pulp sample in which lignin was dissolved physically and the pulp sample in which lignin was dissolved chemically respectively. The pulp samples were analyzed by phenolic group determination, alkaline nitrobenzene oxidation and ozonation method. The results indicated that around 90% of lignin in wheat straw is alkali-soluble at the mild conditions, is basically dissolved physically without chemical change. The phenolic group content was not changed greatly, the nitrobenzene oxidation yield only changed slightly during the mild cooking. The phenolic group content was increased obviously and uncondensed lignin content was decreased very much when the intense cooking conditions were applied and the delignification was over 90%. The lignin structure was changed greatly during this period.