Powder metallurgic Ti2 AlNb alloys with W addition are sintered at 900, 1000, 1070 °C,and 1150 °C(i.e., in the O + B2, a_2+ B2 + O, a_2+ B2, and single B2 phase regions, respectively)for 12 h, followed by wa...Powder metallurgic Ti2 AlNb alloys with W addition are sintered at 900, 1000, 1070 °C,and 1150 °C(i.e., in the O + B2, a_2+ B2 + O, a_2+ B2, and single B2 phase regions, respectively)for 12 h, followed by water quenching and furnace cooling. Comparisons of phase and microstructure between quenched and furnace-cooled W-modified alloys are carried out to illustrate the phase transformation and microstructure evolution during the cooling process. Furthermore, a comparison is also made between W-modified and W-free alloys, to reveal the function of the W alloying.W addition accelerates the solutions of a_2 and O phases during the high-temperature holding, and a Widmannsta¨tten B2 + O structure, which contributes to the properties, is induced by furnace cooling from all the phase regions. The Widmannsta¨tten structure includes a B2 matrix, primary O, and secondary O precipitates. However, W alloying refines the Widmannsta¨tten structure only when the alloys are solution-treated and then cooled from the single B2 phase. Although the hardness of the W-modified alloys is lower than that of the W-free alloys sintered in the same phase region, an enhancement of hardness, 489 ± 18 HV, is obtained in the alloy solution-treated in the single B2 phase region for only 0.5 h.展开更多
基金the National Natural Science Foundation of China(Grant Nos.51474156 and U1660201)the National High Technology Research and Development Program(‘‘863" Program)of China(Grant No.2015AA042504)for financial support
文摘Powder metallurgic Ti2 AlNb alloys with W addition are sintered at 900, 1000, 1070 °C,and 1150 °C(i.e., in the O + B2, a_2+ B2 + O, a_2+ B2, and single B2 phase regions, respectively)for 12 h, followed by water quenching and furnace cooling. Comparisons of phase and microstructure between quenched and furnace-cooled W-modified alloys are carried out to illustrate the phase transformation and microstructure evolution during the cooling process. Furthermore, a comparison is also made between W-modified and W-free alloys, to reveal the function of the W alloying.W addition accelerates the solutions of a_2 and O phases during the high-temperature holding, and a Widmannsta¨tten B2 + O structure, which contributes to the properties, is induced by furnace cooling from all the phase regions. The Widmannsta¨tten structure includes a B2 matrix, primary O, and secondary O precipitates. However, W alloying refines the Widmannsta¨tten structure only when the alloys are solution-treated and then cooled from the single B2 phase. Although the hardness of the W-modified alloys is lower than that of the W-free alloys sintered in the same phase region, an enhancement of hardness, 489 ± 18 HV, is obtained in the alloy solution-treated in the single B2 phase region for only 0.5 h.