Reinforcing effects of modified Kevlar~ fiber on the mechanical properties of wood-flour/polypropylene composites

Kevlar fiber （KF） is a synthesized product with strong mechanical properties. We used KF as a reinforcement to improve the mechanical properties of wood-flour/polypropylene （WF/PP） composites. KF was pretreated with NaOH to improve its compatibility with the thermoplastic matrix. Maleated polypropylene （MAPP） was used as a coupling agent to improve the interfacial adhesion between KF, WF, and PP. Incorporation of KF improved the mechanical properties of WF/PP composites. Treatment of KF with NaOH resulted in further improvement in mechanical strength. Addition of 3% MAPP and 2% hydrolyzed KF （HKF） led to an increment of 93.8% in unnotched impact strength, 17.7% in notched impact strength, 86.8% in flexure strength, 50.8% in flexure modulus, and 94.1% in tensile strength compared to traditional WF/PP composites. Scanning electron microscopy of the cryo-fractured section of WF/PP showed that the HKF surface was rougher than the virgin KF, and the KF was randomly distributed in the composites, which might cause a mechanical interlocking between KF and polypropylene molecules in the composites.

Preliminary study of viscoelastic properties of MAPP-modified wood flour/polypropylene composites

Viscoelastic properties of maleated polypropylene （MAPP）-modified wood flour/polypropylene composites （WPC） were investigated by both a compression stress relaxation method and dynamic mechanical analyses （DMA）. Three wood to polymer ratios （40：60, 60：40, and 80：20） and five MAPP loading levels （0, 1, 2, 4 and 8%） were used to study their effects on the viscoelastic prop- erties of MAPP-WPC. The results show that： 1） higher wood to polymer ratio corresponds to higher stress relaxation levels for unmodified WPC. The modification with MAPP has an obvious effect on the stress relaxation of MAPP-WPC at higher wood to polymer ratios （60：40 and 80：20）, but almost no effect at the 40：60 wood to polymer ratio. The optimal MAPP loading level for the wood to polymer ratio of 60：40 appears at 1%; 2） the storage modulus reaches its maximum at a MAPP loading level of 1% for wood to polymer ratios of 40：60 and 60：40, while for the 80：20 wood to polymer ratio, a higher storage modulus is observed at higher MAPP loading levels, which is quite consistent with the stress relaxation results. The results suggested that a suitable loading level of MAPP has a positive effect on the viscoelastic properties of WPC at higher wood to polymer ratios. Excessive MAPP loading would have resulted in adverse effects.

Effect of maleic anhydride grafted styrene-ethylene-butylene-styrene （MA-SEBS） on impact fracture behavior of polypropylene / wood fiber composites

MA-SEBS as compatibilizer and impact modifier was incorporated into Polypropylene/Wood Fiber （PP/WF） to enhance interface adhesion and impact strength of the composite. The effect of MA-SEBS content on the impact fracture behavior of PP/WF composites was studied. The impact properties of composites with 8% MA-SEBS reached the maximum value. And further increasing of MA-SEBS content to 10% did not improve the fracture toughness, but improved the stiffness of composites by DMA analysis. This was attributed to the improved PP/WF adhesion. As the MA-SEBS content is more than 8%, the molecule interaction of PP and WF was expected to much stronger than lower MA-SEBS. Scanning electron microscopy （SEM） was performed to analyze the impact fracture surface and showed a stronger affinity for the wood surfaces.

Dielectric properties of Simon poplar wood flour/polypropylene composite at oven-dry state

Interfacial compatibility is a crucial factor to the performance of wood-plastic composites （WPCs）. Yet, so far, the coupling mechanisms of WPC have not been completely understood. In order to further clarify the interfacial coupling mechanism, the dielectric constant and dielectric loss factor of Simon poplar wood flour/polypropylene composites without additives at different wood contents were measured at oven-dry state, and parameters and thermodynamic quantities of the relaxation process were also analyzed and calculated. Consequently, an obvious relaxation process based on the reorientation of methanol groups in amorphous region of wood cell wall was observed exactly that its dielectric loss factor peak decreased with the decreasing wood content within the measured range of 50%-100%. With the trend of dielectric relaxation strength, the two changing trends both revealed that the existence of polypropylene could hinder reorientation of methanol groups. Following the decreasing wood contents, the effect of the hindrance on the dielectric properties turned obvious gradually. It elucidated that introduction of polypropylene caused the quantities of hydrogen bonds formed between each methanol group and the groups around it change. The same conclusion could be drawn from the analysis of thermodynamic quantities during the dielectric relaxation progress.

Effect of Wood Variables on the Properties of Wood Fiber-Polypropylene Composites

The effect of wood species (Chinese fir and Poplar), wood fiber content (10%, 25%, 40%) and wood fiber sizes (16 to 32 mesh, 32-65 mesh, above 65 mesh) on the properties of the wood fiber-Polypropylene composites were studied in this paper. The results indicate that the effect of wood fiber content and size in composite were more important than that of chosen wood species. Compared with polypropylene without wood fiber, the flexural strength of the composites increased when adding wood fiber into polypr...

Dynamic Mechanical Properties of Wood Powder /Polypropylene Composites

The dynamic mechanical properties of wood powder/polypropylene composites with different wood content treated and untreated with the compatibilizer have been studied. It has been found that addition of wood powders and the compatibilizer can both improve the viscoelasticity of composites. Glass transition temperature (Tg) of appropriate wood powder-filled composites decreased. The value for the storage modulus (G') increased gradually with increasing wood powder content. The addition of the compatibiliz...