Growth and morphology of neodymium or ytterbium doped calcium gadolinium yttrium oxoborate (Re∶Ca 4Gd x Y 1- x O(BO 3) 3(Re∶GdYCOB)Re =Nd,Yb; x =0-1)were systematically studied. Polycrystalline materials used for Re...Growth and morphology of neodymium or ytterbium doped calcium gadolinium yttrium oxoborate (Re∶Ca 4Gd x Y 1- x O(BO 3) 3(Re∶GdYCOB)Re =Nd,Yb; x =0-1)were systematically studied. Polycrystalline materials used for Re∶GdYCOB single crystals growth were synthesized by multistage solid phase reaction method.Re∶GdYCOB single crystals were grown by Czochralski technique.The pulling rates are 0.5-2mm/h and the rotation rates are 10-30r/min.Usually 65-75% polycrystalline materials can be transformed into good quality single crystals under our growth conditions. The structures of some as grown Re∶GdYCOB single crystals were measured by using a four circle diffractometer.The results measured show that the space group of the crystals is C 3 s Cm.The determined lattice constants of 8 at% Nd doped Ca 4YO(BO 3) 3 single crystal are a =0.8076nm, b =1.6020nm, c =0.3527nm , β =101.23°.展开更多
The magnetic properties of （Cox Fe1-x）A （Zn1-x Fe1＋x）B O4 are studied using mean-field theory and the probability distribution law to obtain the saturation magnetization, the coercive field, the critical temperat...The magnetic properties of （Cox Fe1-x）A （Zn1-x Fe1＋x）B O4 are studied using mean-field theory and the probability distribution law to obtain the saturation magnetization, the coercive field, the critical temperature, and the exchange interactions with different values of D （nm） and x. High-temperature series expansions （HTSEs） combined with the Pade approximant are used to calculate the critical temperature of （CoxFe1-x）A（Znl-xFe1＋x）BO4, and the critical exponent associated with magnetic susceptibility is obtained.展开更多
文摘Growth and morphology of neodymium or ytterbium doped calcium gadolinium yttrium oxoborate (Re∶Ca 4Gd x Y 1- x O(BO 3) 3(Re∶GdYCOB)Re =Nd,Yb; x =0-1)were systematically studied. Polycrystalline materials used for Re∶GdYCOB single crystals growth were synthesized by multistage solid phase reaction method.Re∶GdYCOB single crystals were grown by Czochralski technique.The pulling rates are 0.5-2mm/h and the rotation rates are 10-30r/min.Usually 65-75% polycrystalline materials can be transformed into good quality single crystals under our growth conditions. The structures of some as grown Re∶GdYCOB single crystals were measured by using a four circle diffractometer.The results measured show that the space group of the crystals is C 3 s Cm.The determined lattice constants of 8 at% Nd doped Ca 4YO(BO 3) 3 single crystal are a =0.8076nm, b =1.6020nm, c =0.3527nm , β =101.23°.
文摘The magnetic properties of （Cox Fe1-x）A （Zn1-x Fe1＋x）B O4 are studied using mean-field theory and the probability distribution law to obtain the saturation magnetization, the coercive field, the critical temperature, and the exchange interactions with different values of D （nm） and x. High-temperature series expansions （HTSEs） combined with the Pade approximant are used to calculate the critical temperature of （CoxFe1-x）A（Znl-xFe1＋x）BO4, and the critical exponent associated with magnetic susceptibility is obtained.