Cu films of30nm and 15 nm thick were deposited on MgO(001) substrates at 185℃ by dc plasma-sputtering at 1.9kv and 8 mA in pure Ar gas. A dc bias voltage Vs, of 0 V or -80 V was applied to the substrate during depos...Cu films of30nm and 15 nm thick were deposited on MgO(001) substrates at 185℃ by dc plasma-sputtering at 1.9kv and 8 mA in pure Ar gas. A dc bias voltage Vs, of 0 V or -80 V was applied to the substrate during deposition. Structural and electrical proper-ties have been investigated by cross-sectional transmission electron microscopy (XTEM), high resolution XTEM (XHRTEM) and by measuring temperature coefficient of electrical resistance (TCR;η) in the temperature interval of-135℃ to 0 ℃. The Cu film is pol- ycrystalline at Vs= 0 V while it epitaxially grows with Cu(00 )|| MgO(00 1) and Cu[0 10] || MgO[010] at Vs,=-80 V. However, the latter has a very rough surface. The change of η with film thickness and Vs is interpreted in terms of the structure change. Misfit dislocations and lattice expansion are induced along the MgO surface to relax the strain energy due to the lattice mismatch between Cu and MgO.展开更多
文摘Cu films of30nm and 15 nm thick were deposited on MgO(001) substrates at 185℃ by dc plasma-sputtering at 1.9kv and 8 mA in pure Ar gas. A dc bias voltage Vs, of 0 V or -80 V was applied to the substrate during deposition. Structural and electrical proper-ties have been investigated by cross-sectional transmission electron microscopy (XTEM), high resolution XTEM (XHRTEM) and by measuring temperature coefficient of electrical resistance (TCR;η) in the temperature interval of-135℃ to 0 ℃. The Cu film is pol- ycrystalline at Vs= 0 V while it epitaxially grows with Cu(00 )|| MgO(00 1) and Cu[0 10] || MgO[010] at Vs,=-80 V. However, the latter has a very rough surface. The change of η with film thickness and Vs is interpreted in terms of the structure change. Misfit dislocations and lattice expansion are induced along the MgO surface to relax the strain energy due to the lattice mismatch between Cu and MgO.