利用共沉淀法制备二氧化碳加氢合成低碳醇的 Cu- Co基催化剂 ,采用 XRD和 TPR等方法对 Cu- Co基催化剂进行物理表征 ,考察制备催化剂时不同加料顺序对其物性的影响 ;同时 ,在反应压力 2 .5 MPa～ 3.0 MPa,反应温度 5 73K及空速 5 0 0 0 h-1～ 1 0 0 0 0 -1的条件下 ,利用固定床微型反应器对 Cu- Co基催化剂进行活性评价 .结果表明 ,催化剂制备时不同加料顺序影响催化剂的物相组成及几何结构 ;Cu- Co合金是合成低碳醇的活性物相 .

Optimization of the preparation process of nano TiO2 with sol-gel method at low temperature

In this paper, preparation process of nano TiO2 with sol-gel method at low temperature was optimized by response surface method. The nano TiO2 was analysised by DRS and XRD. Result show that： 20mL tetrabutyl titanate, 10mL acetic acid, 6mL ethanol dosage, aging time was 29h, aging temperature was 36℃, Nano TiO2 was prepared under the condition. Particle size of nano particles was 37.3nm, Photodegradation rate was 90.2%. It had good photocatalytic ability.