ZSM-5/MCM-41 composite molecular sieve was prepared by the nano-assembling method.The ZSM-5 molecular sieve,the MCM-41 molecular sieve,the ZSM-5/MCM-41 mechanical mixture and the ZSM-5/MCM-41 composite molecular sieve...ZSM-5/MCM-41 composite molecular sieve was prepared by the nano-assembling method.The ZSM-5 molecular sieve,the MCM-41 molecular sieve,the ZSM-5/MCM-41 mechanical mixture and the ZSM-5/MCM-41 composite molecular sieve were characterized by X-ray powder diffractometry,N_2 adsorption isotherms,temperature programmed desorption of ammonia and scanning electron microscopy and their properties were analyzed.Using FCC gasoline as the feed,activities of different molecular sieves for reducing olefin content were investigated in a continuous high-pressure micro-reactor unit under the following conditions:a reaction temperature of 400℃,a reaction time of 2 h,a weight hourly space velocity of 3h^(-1),and a reaction pressure of 2.0 MPa.The results showed that the HMCM-41 molecular sieve had low reaction performance,and the HZSM-5 molecular sieve demonstrated high aromatization activity,while the ZSM-5/MCM- 41 composite molecular sieve exhibited a best olefin-reducing performance because of its high isomerization activity and moderate aromatization activity.With a largest olefin-reducmg capability and a reasonable distribution of products,the composite molecular sieve was more suitable for FCC gasoline upgrading compared to other three catalysts.展开更多
Mesoporous molecular sieve MCM-41 has been synthesized in the extremely dense system (with H2O/Si<10) and characterized by XRD, N-2 adsorption isotherm as well as probe reactions of cracking of cumene and isomeriza...Mesoporous molecular sieve MCM-41 has been synthesized in the extremely dense system (with H2O/Si<10) and characterized by XRD, N-2 adsorption isotherm as well as probe reactions of cracking of cumene and isomerization of o-xylene.展开更多
The new crystalline V-Ti-silicalite with mesoporous MCM-41 type molecular sieve structure is synthesized hydrothermally; The framework IR spectra associated with ESR, Si-29 MAS NMR, DRS and XPS data shows that V and T...The new crystalline V-Ti-silicalite with mesoporous MCM-41 type molecular sieve structure is synthesized hydrothermally; The framework IR spectra associated with ESR, Si-29 MAS NMR, DRS and XPS data shows that V and Ti are simultaneously incorporated into V-TiMCM-41 framework.展开更多
采用后合成法制备复合分子筛Y/MCM-41,并以其为载体,用活性组分硝酸镍对其改性,制备Ni-Y/MCM-41催化剂,并利用XRD、BET、N2吸附-脱附对其进行表征。结果表明,复合分子筛同时具有微孔分子筛Y沸石和介孔材料MCM-41分子筛的特征。以硫质量...采用后合成法制备复合分子筛Y/MCM-41,并以其为载体,用活性组分硝酸镍对其改性,制备Ni-Y/MCM-41催化剂,并利用XRD、BET、N2吸附-脱附对其进行表征。结果表明,复合分子筛同时具有微孔分子筛Y沸石和介孔材料MCM-41分子筛的特征。以硫质量分数为300μg/g的模拟油进行催化氧化脱硫实验,考察了Ni离子的负载量、反应温度、反应时间、催化剂用量、氧化剂用量等工艺条件对脱硫率的影响。结果表明:硝酸镍的负载量为10%,模拟油用量为20 m L,反应温度为70℃,反应时间为80 min,剂油比(催化剂与模拟油的质量比)为1∶70,V(H2O2)/V(油)=0.03时,脱硫率可达86.53%。展开更多
An MCM-41/mordenite composite with two- fold porous structure and stepwise-distributed acidity was prepared for the first time by using zeolite mordenite as the silica-alumina source. The composite molecular sieve has...An MCM-41/mordenite composite with two- fold porous structure and stepwise-distributed acidity was prepared for the first time by using zeolite mordenite as the silica-alumina source. The composite molecular sieve has been investigated and compared with a mechanical mixture of mordenite and MCM-41 for their structure, acidity and catalytic activity by means of XRD, N2 adsorption and desorption, HRTEM, DTG, NH3-TPD and catalytic reaction. The characterization results show that the structure and property of the composite molecular sieve are quite different from those of the mechanical mixture, which might be ascribed to the incorporation of secondary building units characteristic of zeolite mordenite into the mesoporous walls of the composite which gives rise to the thicker mesoporous walls, the higher hydrothermal stability and more strong acid sites. Furthermore, the new strategy could be used as a new general method for the preparation of catalysts for the reaction system with multifold large molecules, and the results were well confirmed by the dealkylation of C10+ aromatic hydrocarbon.展开更多
The mesoporous molecular sieves MCM-41 were prepared using room tempera-ture ionic liquid （RTIL） synthesized in laboratory and cethytrimethylammonium bromide （CTAB） as compound templates for the first time. They w...The mesoporous molecular sieves MCM-41 were prepared using room tempera-ture ionic liquid （RTIL） synthesized in laboratory and cethytrimethylammonium bromide （CTAB） as compound templates for the first time. They were prepared under low aging temperature and short aging time. Via characterizing by XRD and nitrogen adsorption instrument, MCM-41 synthesized by this new method exhibited good crystal structure and narrow pore distribution. The following pre-paratory conditions was optimal： the molar ratio of RTIL to CTAB was 1.0∶1.0, aging at 80 ℃, for 40 h and calcined at 540 ℃. It is found that the acidified MCM-41 improves its activity as catalyst over the unmodified ones.展开更多
Following hydrothermal synthesis process, MCM-41 was synthesized by using cetyltriethylammonium bromide as templating agent. The experimental results showed that MCM-41 with pore diameter in the range of 4-7 nm can be...Following hydrothermal synthesis process, MCM-41 was synthesized by using cetyltriethylammonium bromide as templating agent. The experimental results showed that MCM-41 with pore diameter in the range of 4-7 nm can be obtained by adjusting nsurf/nsi. It was proved that cetyltriethylammonium bromide is an effective templating agent for increasing pore diameter of molecular sieve MCM-41.展开更多
文摘ZSM-5/MCM-41 composite molecular sieve was prepared by the nano-assembling method.The ZSM-5 molecular sieve,the MCM-41 molecular sieve,the ZSM-5/MCM-41 mechanical mixture and the ZSM-5/MCM-41 composite molecular sieve were characterized by X-ray powder diffractometry,N_2 adsorption isotherms,temperature programmed desorption of ammonia and scanning electron microscopy and their properties were analyzed.Using FCC gasoline as the feed,activities of different molecular sieves for reducing olefin content were investigated in a continuous high-pressure micro-reactor unit under the following conditions:a reaction temperature of 400℃,a reaction time of 2 h,a weight hourly space velocity of 3h^(-1),and a reaction pressure of 2.0 MPa.The results showed that the HMCM-41 molecular sieve had low reaction performance,and the HZSM-5 molecular sieve demonstrated high aromatization activity,while the ZSM-5/MCM- 41 composite molecular sieve exhibited a best olefin-reducing performance because of its high isomerization activity and moderate aromatization activity.With a largest olefin-reducmg capability and a reasonable distribution of products,the composite molecular sieve was more suitable for FCC gasoline upgrading compared to other three catalysts.
文摘Mesoporous molecular sieve MCM-41 has been synthesized in the extremely dense system (with H2O/Si<10) and characterized by XRD, N-2 adsorption isotherm as well as probe reactions of cracking of cumene and isomerization of o-xylene.
文摘The new crystalline V-Ti-silicalite with mesoporous MCM-41 type molecular sieve structure is synthesized hydrothermally; The framework IR spectra associated with ESR, Si-29 MAS NMR, DRS and XPS data shows that V and Ti are simultaneously incorporated into V-TiMCM-41 framework.
文摘采用后合成法制备复合分子筛Y/MCM-41,并以其为载体,用活性组分硝酸镍对其改性,制备Ni-Y/MCM-41催化剂,并利用XRD、BET、N2吸附-脱附对其进行表征。结果表明,复合分子筛同时具有微孔分子筛Y沸石和介孔材料MCM-41分子筛的特征。以硫质量分数为300μg/g的模拟油进行催化氧化脱硫实验,考察了Ni离子的负载量、反应温度、反应时间、催化剂用量、氧化剂用量等工艺条件对脱硫率的影响。结果表明:硝酸镍的负载量为10%,模拟油用量为20 m L,反应温度为70℃,反应时间为80 min,剂油比(催化剂与模拟油的质量比)为1∶70,V(H2O2)/V(油)=0.03时,脱硫率可达86.53%。
基金supported by the National Natural Science Foundation of China(Grant Nos.20173039 and 20476060)the National Basic Research Program of China(Grant No.2004CB2 17806)the Petrochina Chemical Company Limiled.
文摘An MCM-41/mordenite composite with two- fold porous structure and stepwise-distributed acidity was prepared for the first time by using zeolite mordenite as the silica-alumina source. The composite molecular sieve has been investigated and compared with a mechanical mixture of mordenite and MCM-41 for their structure, acidity and catalytic activity by means of XRD, N2 adsorption and desorption, HRTEM, DTG, NH3-TPD and catalytic reaction. The characterization results show that the structure and property of the composite molecular sieve are quite different from those of the mechanical mixture, which might be ascribed to the incorporation of secondary building units characteristic of zeolite mordenite into the mesoporous walls of the composite which gives rise to the thicker mesoporous walls, the higher hydrothermal stability and more strong acid sites. Furthermore, the new strategy could be used as a new general method for the preparation of catalysts for the reaction system with multifold large molecules, and the results were well confirmed by the dealkylation of C10+ aromatic hydrocarbon.
基金Funded by Zhengzhou Natural Science Foundation (No. 064SJZJ23115)Key Laboratory Catalysis and Materials Science of Southcentral Universityfor Nationalities Foundation
文摘The mesoporous molecular sieves MCM-41 were prepared using room tempera-ture ionic liquid （RTIL） synthesized in laboratory and cethytrimethylammonium bromide （CTAB） as compound templates for the first time. They were prepared under low aging temperature and short aging time. Via characterizing by XRD and nitrogen adsorption instrument, MCM-41 synthesized by this new method exhibited good crystal structure and narrow pore distribution. The following pre-paratory conditions was optimal： the molar ratio of RTIL to CTAB was 1.0∶1.0, aging at 80 ℃, for 40 h and calcined at 540 ℃. It is found that the acidified MCM-41 improves its activity as catalyst over the unmodified ones.
文摘Following hydrothermal synthesis process, MCM-41 was synthesized by using cetyltriethylammonium bromide as templating agent. The experimental results showed that MCM-41 with pore diameter in the range of 4-7 nm can be obtained by adjusting nsurf/nsi. It was proved that cetyltriethylammonium bromide is an effective templating agent for increasing pore diameter of molecular sieve MCM-41.